应用音平化渣图象分析和指导转炉造渣操作

利用音平化渣图象可以清晰地看出在转炉造渣过程中何时发生喷溅，何时发生炉渣返干和何时化渣正常。应用音平化渣图象和炉渣三元相图，可以正确地分析发生喷溅和返干的原因，从而找到避免突发性喷溅和严重返干的方法。正确的枪位和炉渣碱度控制是实现平稳吹炼的保证，而音平化渣图象能帮助操作工实现这一目标。     

Study on combustion characteristics of blended coals

Power plants in China have to burn blended coal instead of one specific coal for a variety of reasons. So it is of great necessity to investigate the combustion of blended coals. Using a test rig with a capacity of 640 MJ/h with an absolute milling system and flue gas online analysis system, characteristics such as burnout, slag, and pollution of some blended coals were investigated. The ratio of coke and slag as a method of distinguishing coal slagging characteristic was introduced. The results show that the blending of coal has some effect on NO _x but there is no obvious rule. SO _x emission can be reduced by blending low sulfur coal. Translated from Proceedings of the CSEE, 2005, 25(18): 97–103 [译自: 中国电机工程学报]     

高炉炉渣流动性的实验研究

以宝钢高炉渣中的四大组元(CaO,SiO2,Al2O3,MgO)为基础,实验研究MgO,Al2O3含量及碱度对炉渣的熔化性温度和流动性的影响.结果表明,炉渣中Al2O3含量控制在16%,配制适量的MgO(9%～10%),在1 500℃以上的高温区域,炉渣仍能保持正常的流动性,适合炉缸温度充沛的高炉使用;MgO含量由6%增加到10%时,较明显地降低了炉渣粘度,粘度的递减值约为0.07～0.15 Pa.s.     

钒钛渣对刚玉莫来石耐火材料的侵蚀研究

通过不同温度下钒钛渣对刚玉莫来石耐火材料的侵蚀实验，分析了炉渣、温度对材料的影响，认为致密结构、低气孔率是提高炉衬寿命的关键，板条状莫来石的存在利于减缓渣的侵蚀过程。     

电炉钢外来夹杂控制的研究

介绍了夹杂物的来源,包括内生夹杂和外来夹杂,着重于二次氧化产物、卷渣、内衬侵蚀.同时介绍了鄂钢电炉厂在冶炼和连铸过程中控制夹杂物的操作实践.     

溅渣护炉工艺探讨

从炉渣对炉衬和溅渣层的侵蚀机理入手,提出了兼顾冶金和溅渣双重效果的直接造渣工艺,探讨了终渣碱度、MgO、FeO含量等的调整范围,分析了溅渣操作中枪位、时间等的控制和炉底上涨的原因,以期更好地运用溅渣护炉技术。     

从水淬渣中回收镓的试验研究

对鼓风炉（ISP法）或烟化炉水淬渣中回收镓的工艺进行了研究。结果表明，利用浓硫酸恒温熟化的独特浸出工艺，克服硅对液固分离的影响；以伯胺N9123作为萃取剂在硫酸介质中萃取镓；获得了含镓品位为2.82%的富集物。     

广钢3#高炉大修炉渣处理工艺探讨与分析

本文对处理高炉炉渣的图拉法工艺设计进行了总结，并对广钢3#高炉使用中出现的问题做了分析，生产实践表明，该工艺安全可靠，水渣质量好，而且有利于环境保护。     

真空钙热还原炉渣的综合利用研究

研究了从真空钙热还原炉渣中回收稀土的工艺条件；采用本工艺得到的合格稀土溶液，其回收率达65．41％；副产品氟化钙用作炼硅铁合金的助熔剂，使钙热还原炉渣得到综合利用。     

电弧炉采用石灰石单渣冶炼工艺的研究

采用优质石灰石取代质量差的白灰 ,进行了单渣电弧炉熔炼。结果表明 ,钢水成本降低 ,钢水质量提高 ,取得了良好的效果。