T-ZnO晶须增强环氧树脂复合材料的力学行为

研究了以四脚状氧化锌（T-ZnO）晶须为增强剂，环氧树脂复合材料的力学行为。结果表明，由具有三维空间结构的T-ZnO晶须为增强剂所制备的环氧树脂复合材料具有各向同性的力学性能，T-ZnO晶须填加质量分数为6%时，就可使材料的力学性能改善；拉伸强度提高到169%，拉伸功几乎提高了100%，冲击强度提高到300%，抗弯的断裂功提高到158%，而压缩强度略有下降。     

行政行为的概念及构成要素

行政法学的研究应该尽量放宽视角,适应将来法治建设的需要。我们必须把行政行为的概念放到整个法治体系中甚至整个社会的发展中去研究。     

Does life satisfaction moderate the effects of stressful life events on psychopathological behavior during adolescence?

Psychologists within a positive psychology framework have proposed the existence of a set of psychological strengths that buffer against the development of psychopathology. To date, most research efforts in positive psychology have focused on adults. This longitudinal study tested the prediction that adolescents' judgments of life satisfaction moderate the influence of stressful life events on the subsequent development of psychopathological behavior. Using a sample of 816 middle and high school students, the study demonstrated support for the moderational model for externalizing behavior outcomes, but not internalizing behavior problems. Specifically, adolescents with positive life satisfaction (vs. those who were dissatisfied with their lives) were less likely to develop later externalizing behaviors in the face of stressful life events. The study also revealed that adolescent life satisfaction reports show moderate stability across a one-year time frame and independently predict subsequent externalizing behavior even while controlling for prior levels of externalizing behavior... (PsycINFO Database Record (c) 2011 APA, all rights reserved)     

外源乙烯对黄瓜幼苗根系生长及内源多胺含量的影响

精确控制营养液溶氧浓度和外源乙烯浓度,研究了黄瓜幼苗根系在低氧水培时的生长情况以及PAs含量的变化。结果表明,外源乙烯对根际低氧逆境下黄瓜幼苗根系的生长有抑制作用,虽然根径增粗,含水量增加,但根系的总根数、总表面积、总体积、干重和鲜重都有所减少,随着乙烯浓度的增加,抑制作用增强;外源乙烯对根际低氧逆境下黄瓜幼苗根系PAs含量有着明显的拮抗作用,外源乙烯使根际低氧逆境下黄瓜幼苗根系的伤害症状加重。     

微桥法镍膜的弹性模量和残余应力测量

利用MEMS技术制作了不同尺寸的镍(Ni)膜微桥结构样品。采用纳米压痕仪XP系统测量了微桥载荷与位移的关系,并结合微桥力学理论模型得到了两种不同尺寸的Ni膜的弹性模量和残余应力。结果表明,两种不同尺寸的Ni膜的弹性模量结果一致,为190 GPa左右,但是残余应力变化较大。与采用纳米压痕仪直接测得的带有硅(Si)基底的Ni膜弹性模量186.8 7.5 GPa相比较,两者符合较好。     

The Person Reference Process in Spontaneous Trait Inferences.

Five studies examined whether spontaneous trait inferences uniquely reference the person who performed a trait-implying behavior. On each study trial in 5 studies, participants saw 2 faces and a behavioral sentence referring to one of them. Later, participants saw face-trait pairs and indicated whether they had seen the trait word in the sentence presented with the face. Participants falsely recognized implied traits more when these traits were paired with actors' faces than with control faces. This effect was replicated for a large set effaces (120), after a week delay between study and recognition test, when equal attention was paid to each face, and when the orientation of the face at recognition was different from the orientation at encoding. (PsycINFO Database Record (c) 2010 APA, all rights reserved)     

魏氏组织对20#碳钢H2S应力腐蚀开裂性能的影响

文章对H₂S-CO₂-H₂O腐蚀环境下发生H₂S应力腐蚀的20^＃碳钢弯管（无缝钢管）进行了成分、组织、拉伸、硬度和应力腐蚀开裂等性能的试验研究，并与同材质、同时投产、腐蚀环境基本相似而未发生应力腐蚀开裂的在役弯管及未使用的新弯管作对比，结果表明魏氏组织是引起20^＃钢发生应力腐蚀开裂的主要原因；正火能消除魏氏组织，降低钢的应力腐蚀开裂敏感性。     

烟气轮机叶片应力分析与寿命评估方法评述

烟气轮机是炼油厂催化裂化装置的关键设备,合理预测叶片疲劳寿命是保障烟机安全运行的有效手段。从力学建模和边界条件两个方面简要阐述了叶片的应力分析方法,并系统分析了影响烟机叶片疲劳寿命的主要因素,提出了利用改进的局部应力应变法进行叶片寿命预测的合理性和叶片疲劳寿命的评估方法。     

晶须取向对SiCw/6061Al复合材料热压缩变形行为的影响

采用SEM 和 Magiscan-2A 图像分析系统研究了晶须取向对SiCw/6061Al复合材料在300℃压缩变形行为的影响.结果表明:晶须取向影响着晶须折断程度和转动角度; 随着晶须取向角的增加,晶须转动和折断行为所导致的软化效果下降.同时晶须取向也影响复合材料的热压缩应力-应变曲线的形状.在热压缩变形过程中,晶须取向角为0°和30°的复合材料表现出明显应变软化现象, 晶须取向角为45°的复合材料无明显软化现象.晶须取向角为90℃的复合材料表现出应变硬化现象.     

双转向垂向控缝技术实验研究及现场应用

针对压裂过程中缝高较难控制的问题，研制开发出新型的油溶性垂向双转向剂，并开展了室内实验研究。首次验证了转向剂对裂缝延伸的控制机理，确定了转向剂的适用浓度及控缝能力。实验表明，转向剂可以增加隔层应力3～4MPa左右。在此基础上研究了控制裂缝高度施工方案的设计方法，并利用全三维软件结合垂向应力剖面对控缝技术进行了优化。现场推广应用30井次，取得了较好的控缝效果。