Solid-liquid phase equilibria of the benzene + 2-methyl-2-propanol system have been investigated at temperatures from 278 to 323 K and pressures up to 300 MPa using a high-pressure optical vessel. The uncertainties of the measurements of temperature, pressure and composition are within ±0.1 K, ±0.5 MPa, and ±0.001 mole fraction, respectively. The freezing pressure at a constant composition increases monotonously with pressure. The eutectic point shifts to a higher temperature and benzene-rich composition with increasing pressure. In order to describe the pressure-temperature-composition relation of high-pressure solid-liquid phase equilibria, a new simple equation has been proposed as follows:

用LG55冷轧管机轧制小直径不锈钢管孔型改进

介绍了ＬＧ５５冷轧管机使用Φ７～３２ｍｍ、Φ５０～３２ｍｍ孔型轧制小直径不锈钢管的工艺特点。试验表明，两种孔型可行，且Φ５７～３２ｍｍ孔型的综合使用效果更好。     

提高Cr12MoV钢冷作模具寿命的措施

从原材料改锻、预备热处理、淬火及回火、深冷处理、表面强化处理等方面分析介绍了提高Cr12MoV钢冷作模具寿命的一些方法和措施 ,并通过实例表明 ,采用这些方法和措施可较大幅度地提高模具寿命     

The generation of surface roughness during slurry erosion-corrosion and its effect on the pitting potential

Results of experiments performed to isolate the effect of surface roughness generated during slurry erosion-corrosion of 304L stainless steel are presented. Surfaces prepared by grinding to different finishes show that increasing the roughness lowers the pitting potential in chloride solution. Subsequent erosion by an aqueous sand slurry then alters this pitting potential (E_p), as measured in the solution phase alone, in a manner dependent on the initial surface roughness. Surfaces which were initially rougher show a pronounced rise in _p after erosion, while those with an initially smoother finish show a fall in E_p after erosion. Measurement of E_p during erosion-corrosion does not fit either process, with values of _Ep lower than those predicted from the surface roughness alone.     

Characterization of blasted austenitic stainless steel and its corrosion resistance

It is known that the corrosion resistance of stainless steel is deteriorated by blasting, but the reason for this deterioration is not clear. A blasted austenitic stainless steel plate (JIS-SUS304) has been characterized with comparison to the scraped and non-blasted specimens. The surface roughness of the blasted specimen is larger than that of materials finished with #180 paper. A martensite phase is formed in the surface layer of both blasted and scraped specimens. Compressive residual stress is generated in the blasted specimen and the maximum residual stress is formed at 50–100 μm from the surface. The corrosion potentials of the blasted specimen and subsequently solution treated specimen are lower than that of the non-blasted specimen. The passivation current densities of the blasted specimens are higher those of the non-blasted specimen. The blasted specimen and the subsequently solution treated specimen exhibit rust in 5% sodium chloride (NaCl) solution, while the non-blasted specimen and ground specimen do not rust in the solution. It is concluded that the deterioration of corrosion resistance of austenitic stainless steel through blasting is caused by the roughed morphology of the surface.     

Use of electron microscopy on microstructure characterization of high chromium cast irons

The physical metallurgy underlying the development of cast microstructures in abrasion resistant high chromium cast irons, and their structural modification by thermal treatments is relatively complex. Structural characterisation via electron microscopy therefore has a key role to play in furthering our understanding of the phase transformations that control the microstructures and hence the service performances of these irons as wear parts. This paper shows how both scanning and especially transmission electron microscopy can provide valuable information on the nature of eutectic and secondary carbides and on the matrix structures in these irons. Particular attention is given to current characterisation research on conventionally cast 30%Cr irons that are used for applications involving corrosive wear e.g. slurry pumps and on a semi-solid cast 27%Cr iron that has a potential for applications in industry.     

Enabling factors toward production of nanostructured steel on an industrial scale

Utilizing the existing properties of steel, a modern technological society has been constructed. While there are over 25,000 worldwide equivalent steels based on manipulating the eutectoid transformation, there exist only a handful of commercial nanostructured steel alloys based on manipulating the more complex glass devitrification transformation. Thus, research on nanostructured steels is in its infancy, and many further developments are expected with the demonstrated promise of developing new combinations of superior properties. In this article, seven enabling metallurgical factors are presented that ultimately allow a variety of nanostructured steel products to be produced in an ever-increasing array of industrial processing techniques. Additionally, a case example of the formation of nanostructured steel are given showing how these factors can be harnessed on an industrial scale.     

DD—921钢铁常温发黑剂的研制和应用

研究了钢铁常温发黑过程的成膜机理,各组分之间的作用以及相互之间的影响,着重分析了常温发黑的优缺点,工艺控制参数以及经济性。