Alloying behavior and novel properties of CoCrFeNiMn high-entropy alloy fabricated by mechanical alloying and spark plasma sintering

An equiatomic CoCrFeNiMn high-entropy alloy was synthesized by mechanical alloying (MA) and spark plasma sintering (SPS). During MA, a solid solution with refined microstructure of 10 nm which consists of a FCC phase and a BCC phase was formed. After SPS consolidation, only one FCC phase can be detected in the HEA bulks. The as-sintered bulks exhibit high compressive strength of 1987 MPa. An interesting magnetic transition associated with the structure coarsening and phase transformation was observed during SPS process.     

Electromagnetic shielding properties of iron oxide impregnated kenaf bast fiberboard

The electromagnetic shielding effectiveness of kenaf fiber based composites with different iron oxide impregnation levels was investigated. The kenaf fibers were retted for removing the lignin and extractives from the fibers and magnetized. Using the unsaturated polyester and the magnetized fibers, kenaf fiber based composites were manufactured by the compression molding process. The transmission energies of the composites were characterized when the composite samples were exposed under the irradiation of electromagnetic (EM) wave with a variable frequency from 9 GHz to 11 GHz. Using the Scanning Electron Microscope (SEM), the iron oxide nanoparticles were observed on the surfaces and inside the micropore structures of single fibers. As the Fe content increased from 0% to 6.8%, 15.9% and 18.0%, the total surface free energy of kenaf fibers with the magnetizing treatments increased from 44.8 mJ/m² to 46.1 mJ/m², 48.8 mJ/m² and 53.0 mJ/m², respectively, while the modulus of elasticity reduced from 2875 MPa to 2729 MPa, 2487 MPa and 2007 MPa, respectively. Meanwhile, the shielding effectiveness was increased from 30–50% to 60–70%, 65–75% and 70–80%, respectively.     

Synthesis and characterization of nanostructured magnetoresistive Ni doped ZnO films

We report a method to produce magnetic nanostructured semiconductor films based in ZnO doped with Nickel to control their magnetic properties. The method is based on a combined diffusion–oxidation process within a controlled atmosphere chamber to produce a uniform distribution of Ni ions in the ZnO films (ZnO:Ni). The synthesis of ZnO:Ni films is reported as well as the magnetoresistive characteristics, the used method yields films with reproducible and homogeneous properties. The films were also characterized structurally by X-Ray Diffraction (XRD) and Raman spectroscopy, and by Hall–van der Pauw measurements. The XRD measurements confirm the nanocrystalline films character. The films resulted of n-type conductivity with electron concentrations of ~10²⁰ cm⁻³ in average and carrier mobilities of 5 cm²/V s. The Magnetoresistance (MR) behavior of the films at 300 K shows negative changes of ΔR~0.5% in accordance with the usual literature reports on samples produced by other methods.     

Effect of Sr doped the YFeO3 rare earth ortho-ferrite on structure,magnetic properties,and microwave absorption performance

Given the remarkable performances of rare earth multiferroic ortho-ferrites with magnetic optical and dielectric properties, the Y_1-xSr_xFeO₃ (x = 0, 0.05, 0.1, 0.15) perovskite structure microwave absorbing ferrite materials was successfully synthesized by Sr²⁺ ions A-site doping based on sol-gel technology in this paper. The XRD of all samples was refined with FullProf software, which confirmed the formation of the orthogonal perovskite structure (SG: Pnma). The SEM and TEM results display the average particles size of the samples is distributed between 110 and 160 nm. The increase of Sr doping concentration leads to the increase of particles size, which may be related to the growth of preferred orientation and incomplete substitution. The XPS analysis shows that Fe³⁺ was accompanied by the presence of Fe²⁺ with the doping of Sr²⁺ ions and oxygen vacancies increased significantly. The samples change from weak ferromagnetic state to paramagnetic state with the increase of Sr content. The minimum reflection loss (RL) of the Y_0.95Sr_0.05FeO₃ samples at 12.2 GHz reached −30.87 dB with thickness of 2.2 mm, where its effective absorption bandwidth (EAB, RL ≤ −10 dB) reached 2.4 GHz (11.3–13.7 GHz). Moreover, the EAB of the Y_0.85Sr_0.15FeO₃ samples reached 2.64 GHz, and the corresponding range is 9.0–11.6 GHz (X-band).     

Investigation on external stimuli engendered magnetic ordering in polycrystalline CaCu3Ti4O12 quadruple perovskite

The consequences of high energy mechanical milling, microwave-assisted heating and rapid thermal cooling on magnetic ordering in polycrystalline CaCu₃Ti₄O₁₂ cubic perovskite have been investigated by means of X-ray powder diffractometry (300?K), dc magnetization in field – cooled and zero – field cooled modes (H = 100?Oe and 1000?Oe, T?=?5–300?K) (M – T curves) and M – H loop characteristics (T?=?5?K and 300?K, H_max = 70?kOe). The M – T curves of unmilled and 16?h milled samples show pure antiferromagnetic and weak ferromagnetic ordering, respectively, 1?h and 6?h milled samples demonstrate the coexistence of both the phases while microwave-assisted and quenched samples exhibit classic antiferromagnetic transition and a low temperature paramagnetic–like contribution with different weights, well supported by the M – H loop characteristics. The observed transformations in the magnetic ordering are attributed to the ball-milling induced stress which curtails hybridization of empty Ti-3d orbitals with Cu-3d and O-2p orbitals and secondary phase formation. Oxygen vacancies associated with bound magnetic polarons originate ferromagnetism in the milled samples while unpaired electrons inhabited at the empty sites are the cause of paramagnetic centers. The low-temperature Curie – tail in M – T curve for quenched and microwave assisted samples is attributed to Ti³⁺ cations.     

Influence of Bridgman solidification on microstructures and magnetic behaviors of a non-equiatomic FeCoNiAlSi high-entropy alloy

The non-equiatomic FeCoNiAlSi alloy is prepared by the Bridgman solidification (BS) technique at different withdrawal velocities (V = 30, 100, and 200 μm/s). Various characterization techniques have been used to study the microstructure and crystal orientation. The morphological evolutions accompanying the crystal growth of the alloy prepared at different withdrawal velocities are nearly the same, from equiaxed grains to columnar crystals. The transition of coercivity is closely related to the local microstructure, while the saturation magnetization changes little at different sites. The coercivity can be significantly reduced from the equiaxed grain area to the columnar crystal area when the applied magnetic field direction is parallel to the crystal growth direction, no matter what is the withdrawal velocity. In addition, the alloy possesses magnetic anisotropy when the applied magnetic field is in different directions.     

Stability and cytotoxicity study of NiFe2O4 nanocomposites synthesized by co-precipitation and subsequent thermal annealing

In this article, NiFe₂O₄ nanoparticles (NPs) were prepared by co-precipitation method with subsequent thermal annealing leading to obtainment NPs with average sizes of 78 nm. Structure and magnetic analysis were performed by X-ray diffraction, transmission electron microscopy, Mössbauer spectroscopy and vibrating sample magnetometry techniques. Stability of NiFe₂O₄ NPs was evaluated in PBS solution during 20 days. The toxicity of prepared NPs was evaluated in vitro using different cancer cell lines: HeLa (cervical cancer cell), PC-3 (prostate cancer cell). Fibroblasts like cells of L929 obtained from subcutaneous adipose tissue of mouse were used as normal cells. Results indicate successful synthesis of NiFe₂O₄ NPs that exhibit low cytotoxicity in concentration range from 1 to 100 μg/ml. Presented physical and biological results indicate the possibility of application investigated magnetic nanoparticles in hyperthermia, targeted drug delivery, magnetic resonance imaging or cell separation.     

Influences of magnetic fields on current–voltage characteristics of gold-DNA-gold structure with variable gaps

Achieving highly sensitive magnetic sensors by means of Metal-DNA-Metal (MDM) structure is a key issue. DNA, being a genetic information carrier in living cells reveals tunable semiconducting response in the presence of external electric and magnetic fields, which is promising for molecular electronics. The influence of magnetic fields up to 1200 mT on the current–voltage (I–V) behavior of Gold-DNA-Gold (GDG) structure having variable gap sizes from 20–50 μm are reported in this work. These structures were fabricated using UV lithography, DC magnetron sputtering and thermal evaporation techniques. DNA strands were extracted from Boesenbergia rotunda plant via standard protocol. The acquired I–V characteristics display the semiconducting diode nature of DNA in GDG structures. The potential barrier for all the structures exhibit an increasing trend with the increase of externally imposed magnetic field irrespective of variable gap sizes. Furthermore, the potential barrier in GDG junction at higher magnetic field strengths (>1000 mT) is found to be considerably enhanced. This enhancement in the junction barrier height at elevated magnetic fields is attributed to the reduction of carrier mobility and augmentation of resistance. The achieved admirable features of magnetic sensitivity suggest the viability of using these GDG sandwiches as a prospective magnetic sensor.