一种制做三维牙——颌骨光弹性模型的新方法

本文提出一种用“整体浇注法”制做三维牙——颌骨光弹性模型的新方法,即用价格便宜的石膏做阴模,先制出与真实牙几何相似的牙光弹性模型和模拟牙周膜的乳胶套,将它们粘接好,然后将其放入颌骨石膏阴模的适当位置,浇入环氧树脂混合液,用“二次固化法”进行固化,即可制成三维牙——颌骨整体光弹性模型。此法能保证模型与实物的严格几何相似和牙周的边界条件相似,使实验精度大大提高且工艺简单、成本低。     

Mold-filling characteristics of AZ91 magnesium alloy in the low-pressure expendable pattern casting process

The magnesium (Mg) alloy low-pressure expendable pattern casting (EPC) process is a newly developed casting technique combining the advantages of both EPC and low-pressure casting. In this article, metal filling and the effect of the flow quantity of inert gas on the filling rate in the low-pressure EPC process are investigated. The results showed that the molten Mg alloy filled the mold cavity with a convex front laminar flow and the metal-filling rate increased significantly with increasing flow quantity when flow quantity was below a critical value. However, once the flow quantity exceeded a critical value, the filling rate increased slightly. The influence of the flow quantity of inert gas on melt-filling rate reveals that the mold fill is controlled by flow quantity for a lower filling rate, and, subsequently, controlled by the evaporation of polystyrene and the evaporation products for higher metal velocity. Meanwhile, the experimental results showed that the melt-filling rate significantly affected the flow profile, and the filling procedure for the Mg alloy in the low-pressure EPC process. A slower melt-filling rate could lead to misrun defects, whereas a higher filling rate results in folds, blisters, and porosity. The optimized filling rate with Mg alloy casting is 140 to 170 mm/s in low-pressure EPC.     

大型薄壁铝铸件表面沟槽缺陷的产生及消除

针对大型薄壁铝铸件内腔表面出现的沟槽缺陷,从差压铸造、树脂砂、铸件结构等工艺条件方面探讨了产生的机理,并通过试验和对比研究,确定排气不畅是该缺陷的首要引发因素,找到了消除该缺陷的工艺方法,提出了相关预防措施,避免了因此产生的废品损失.     

离心铸造汽缸套白斑产生机理

针对离心铸造汽缸套的白斑特征，以模拟试验手段探寻原因。用金属凝固理论解释白斑形成机理。经过装车试用，验证了白斑对摩擦性能的影响。     

Strengthening technology and mechanism for semi-solid die casting of aluminum alloy

Combined with theoretical evaluation,an optimized strengthening process for the semi-solid die castings of A356 aluminum alloy was obtained by studying the mechanical properties of castings solution treated and aged under different conditions in detail,then,the semi-solid die castings and liquid die castings were heat treated with the optimized process.The results show that the mechanical properties of semi-solid die castings of aluminum alloy are superior to those of the liquid die castings,especially the strengthening degree of heat treated semi-solid die castingsis much greater than that of liquid die castings with the tensile strength more than 330 MPa and the elongation more than 10％,and this is mainly contributed to the non-dendritic and more compact microstructure of semi-solid die castings.The strengthening mechanism of heat treatment for the semi-solid die castings of A356 aluminum alloy is due to the dispersive precipitation of the second phase(Mg2 Si) and formation of GP Zone.     

Analysis of Intermetallic Phases Formed on Surface Vapor Oxidized H13 Hot Work Steels in Molten Aluminum

In this paper, the author dipped surface vapor oxidized H13 steel specimens into 700℃ molten aluminum liquid for a certain period of time. Analyze the intermetallic phases formed on the H13 samples surface with optical microscope and X-ray diffraction method. The observation of immersion test sample's cross-section shows that Fe3O4 film will protect die substrate from molten aluminum erosion. The identification of the intermetallic phases reveals that they consist of 2parts, which is named as the composite layer and the compact layer. Further investigations are made in order to know the phase constituents of the 2 layers, they are Al8Fe2Si (outer composite layer), (AlCuMg) and Al5Fe2 (compact layer),respectively. The experimental results show that on the same specimen, a convex surface with bigger radius of curvature is more likely to be molten and the melting loss speed is also faster than a flat and smooth surface. The thickness of compact layer on a smooth surface is much bigger than that of the convex surface. Therefore, the author supposes the compact layer is favorable in stabilizing the die surface material from further melting loss, as their formation on the die surface, the melting loss speed will decrease.     

粉煤灰填充尼龙6浇铸制品的研究

将粉煤灰用硅烷偶联剂处理后填充到尼龙6浇铸制品(MC尼龙)中,可以改善制品的吸水性、收缩率及热稳定性等,还可以降低成本。该项研究结果有很大的实用价值。     

Influence of volatile matter and deposited carbon on coke yield from coals

The relations between coke yields and the volatile matter content of 30 individual and 30 blended coals were investigated. Coke yields and deposited carbon related to volatile matter content can be expressed in the following equations: CY (%) = 97.89?0.86 VMch+VMc; and DC (%)= ?2.24+0.16 VMch; where: CY=real coke yield; VMch = volatile matter content of charging coal; VMc=volatile matter content of coke, and in the case of <2%; DC = deposited carbon. The test results show excellent correlation with practice.     

FC-26高中油型加氢裂化催化剂的工艺研究

抚顺石油化工研究院研制开发的新一代FC -2 6高中油型加氢裂化催化剂 ,以W -Ni为加氢组分 ,以无定型硅铝为主载体 ,并添加改性分子筛。工艺研究及工业应用结果表明 ,FC -2 6催化剂活性及中油选择性高 ,稳定性好 ,原料适应性强 ,具有广阔的应用前景。