In-situ composite Cu-Cr contact cables with high strength and high conductivity

In order to develop a new type of contact cable with high strength and high electrical conductivity, Cu-Cr alloy series were selected as materials and Cu-Cr alloy castings were produced by means of directional solidification continuous casting (DSCC) process. The results show that the fibrillar strengthening phase, 13-Cr, orderly arranges among the copper matrix phase along the wire direction; and a microstructure of in-situ composite forms, which retains the basic property of good conductivity of the copper matrix and meanwhile obtains the strengthening effect of [3-Cr phase. The production technology as well as the mechanical property, electrical property, and synthetic property of the in-situ composite contact cables was discussed.     

Yield Stress and Microstructure of Set Yogurt Made from High Hydrostatic Pressure-Treated Full Fat Milk

ABSTRACT: Set yogurts were prepared from fortified milk subjected to the following processes: (a) Thermal process (85C,°C,35 min), (b) High hydrostatic pressure process (193 or 676 MPa for 5 or 30 min), and (c) Nonprocessed milk (control). Yogurts from milk treated with 676 MPa for 30 min exhibited similar yield stress and water-holding capacity (WHC) to yogurts from heated milk. Transmission Electron Microscopy (TEM) micrographs exhibited small round casein micelle aggregates without appendages in yogurts from heated milk. Yogurts from milk treated with 193 MPa and untreated milk exhibited low yield stress, low WHC, and large clusters of coalesced micelles. Mechanisms for gel formation are discussed.     

薄板坯连铸连轧流程Ti微合金化高强钢开发与应用

在薄板坯连铸连轧流程上，经过对Ti微合金化技术研究，有效解决了Ti微合金化强度性能波动大的问题，开发出屈服强度450～700MPa高强钢。对试制钢组织性能和工业应用分析研究，表明该产品通板性能良好，通板强度差30MPa左右；成形性能良好，d=0时冷弯测试全部合格；同时还具有良好焊接性能，焊接后，强度波动较小，均在母材部位断开；试制钢显微组织为珠光体和铁素体，晶粒均匀细小，平均尺寸为4～8／μm；实物质量满足集装箱和汽车制造行业要求，具有广阔市场前景。     

Investigation of Centreline Segregation and Centreline Porosity in CC ‐ Slabs

Improvements of solidification processing in conventional or near net shape casting depend on sophisticated methods of macroscopic examination of central unsoundness and inhomogeneity of the cast material. As long as remarkable deviations referring to the quality features exist between the slab centre and the bulk material such methods should be looked after. Two semi‐macroscopic methods of segregation analysis are discussed in this paper: firstly, the potential of the emission spectral analysis combined with sectioning of a sample and secondly, the computer aided micro‐probe analysis. Both methods are restricted to small local areas. The proneness of elements and steel grades with respect to micro‐ and macrosegregation as well as distribution‐ and segregation coefficients are determined. The effect of a diffusion anneal on homogenisation of segregation is studied. Last not least the precipitation of sulphides, phosphides or carbonitrides is estimated. Ultrasonic detection of the central unsoundness of conventional slabs or thin slabs is a new approach towards a quantitative macroscopic examination. The sample size is 400 mm x 300 mm x 30 mm. To achieve a low ultrasonic noise using a 5 MHz‐transducer the samples are heat treated for grain refinement. “Dog bone porosity”, macroscopic topographical misfit between the upper and lower solidifying shells, periodical corner cracks or systematic transverse centre cracks are detected. Obviously, segregations do not reflect the ultrasonic beam. However, it can be presumed that an interrelation exists between porosity and segregation, although these might be locally apart from each other. This new ultrasonic test of the central unsoundness of continuous cast (c.c.) slabs gives valuable arguments to machine builders and maintenance people to decide on the right concepts for strand guidance, support rollers and secondary cooling. Soft reduction can be optimized and variations in casting speed counteracted by dynamic means. R&D service of this kind can help steelmakers when decisions are impending to build new casting machines or revamp old ones.     

现代电弧炉流程钢液氮控制的试验研究

通过生产试验研究了电弧炉冶炼过程、LF精炼过程及连铸过程钢液氮的控制。研究表明，电弧炉冶炼过程主要是电弧区增氮，LF过程及连铸过程钢液增氮主要是钢液与大气接触，LF供电制度也对钢液吸氮有影响。     

合金钢连铸机生产工艺分析及实践

对新钢特殊钢有限责任公司整个合金钢连铸机的生产工艺进行了分析，提出了提高钢水质量和优化连铸工艺参数的有效措施，使铸坯的质量得到了有效控制和改善。     

技术攻关提高成材率

介绍了广钢集团高速线材生产线的生产和工艺概况，分析了成材率的影响因素，阐述了技术攻关提高成材率所采取的措施和取得的良好效果及经济效益。     

薄板坯连铸生产SS400钢工艺技术研究

对唐钢薄板坯连铸机生产的SS400钢的生产工艺进行了分析,认为薄板坯连铸机生产的SS400钢,在采取了精炼站在线定氧,将钢水全氧控制在25×10~(-6)左右,同时连铸采取保护浇注和轻压下等技术后,能够确保薄板坯连铸SS400钢的顺利浇注,轧制的板带材表面质量良好,机械性能符合要求。     

高合金钢铸造用涂料的试制与开发

介绍了炉爪用合金钢1Cr25Ni20Si2Re,导板用合金钢2Cr32Ni5采用串箱铸造过程中，有关镁砂粉涂料和石英粉涂料的试制。结果表明：镁砂粉涂料为不透气涂料，不太适用，而合理配方的石英粉涂料使用性能良好。