Evaluation of some of the properties of plasma treated wool fabric

Low temperature plasma (LTP) treatment was applied to wool fabric with the use of a nonpolymerizing gas, namely oxygen. Properties of the LTP‐treated samples including low stress mechanical behavior, air permeability, and thermal characteristics were evaluated in this study. Kawabata evaluation system fabric (KES‐F) was employed to determine the tensile, shearing, bending, and compression strength properties and surface roughness of the specimens. The changes in these properties are believed to be closely related to the interfiber and interyarn frictional force induced by the LTP. The decrease in the air permeability of the LTP‐treated wool fabric was found to be probably because of the plasma action effect on increasing the fabric thickness and a change in fabric surface morphology, which was confirmed by scanning electron microscopy micrographs. The change in the thermal properties of the LTP‐treated wool fabric was in good agreement with the earlier findings and can be attributed to the amount of air trapped between the yarns and fibers. This study suggested that the LTP treatment can influence the final properties of the wool fabric, and also provide information for developing LTP‐treated wool fabric for industrial use. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 5958–5964, 2006     

碳纤维经氧等离子/KH550处理后的表面形态和结构

碳纤维(CF)表面经氧等离子、KH550和 LiAlH_4处理后,其物理和化学性能得以改善.由于提高了 CF 和树脂间的联结,使 CF 复合材料的层间剪切强度提高50%以上,在湿热下的强度保留率达94%以上.使用纤维接触角测定仪,SEM 和 XPS 等对 CF 表面的浸润性、形态和化学组成进行了研究.实验指出:CF 经等离子和 KH550处理后,其临界表面能有了提高;CF 本身仅受氧离子刻蚀,故其拉伸强度的损失小于其他处理方法.     

Oxygen plasma modification of poly(3‐hydroxybutyrate‐co‐3‐hydroxyvalerate) film surfaces for tissue engineering purposes

Plasma glow‐discharge application is known as a technique to coat or modify the surfaces of various materials. In this study, the influence of oxygen rf‐plasma treatment on surface and bulk properties of a biological polyester, poly(3‐hydroxybutyrate‐co‐3‐hydroxyvalerate), were studied by determining water content and water contact angle, and by using X‐ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM). The plasma‐treated films absorbed more water than the untreated film, and the absorbance increased with the total power applied. The water contact angles decreased and O/C atomic ratio increased on treatment, indicating that the material became more hydrophilic due to increases in the oxygen‐containing functional groups on the surface of the polymer. A direct relation could be observed when the O/C ratio was plotted against the total power applied (treatment duration × treatment power). SEM revealed a visual record of surface modification, the extent of which increased with increased total power. It was thus possible to alter the surface chemistry and relevant properties of the polymer film using oxygen plasma as a tool. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 87: 1285–1289, 2003     

提高等离子体裂解煤制乙炔收率的方案研究

将反应体系的温度升高到升华点以上 ,是提高等离子体裂解煤制乙炔收率的必由之路 .采用最小自由能方法研究了煤的 C- H- O热力学平衡体系 ,在此基础上提出了一种以煤层气甲烷为冷却剂的等离子体裂解煤制乙炔方案 ,初始反应体系的温度在 40 0 0 K以上 .理论的计算和分析结果表明 ,这种方案可获得较高的乙炔收率 ,而单位质量乙炔的比能耗很低 ,具有很好的经济效益和环境效益 .     

Plasma desorption mass spectrometry, an analytical tool in protein engineering: characterization of modified insulins

Californium-252 plasma desorption mass spectrometry (PDMS) hasbeen employed for the characterization of a series of humaninsulin derivatives in order to evaluate the performance ofthis technique as an analytical tool in protein engineering.Several of the characterized modifications result in a 1 a.m.u.mass change. The precision in mass determination obtainableby PDMS analysis is not sufficient for unambiguous verificationof such modifications based on the molecular weight alone. Itis, however, possible to carry out in situ enzymatic digestionof the sample. Subsequent PDMS analysis will in most cases revealif the modification has been introduced as intended.     

Effect of low‐temperature plasma and chitosan treatment on wool dyeing with Acid Red 27

This study examines in detail the influence of low‐temperature plasma and biopolymer chitosan treatments on wool dyeability. Wool knitted fabrics were treated and characterized by whiteness and shrink‐resistance measurements. Surface modification was assessed by contact‐angle measurements of human hair fibers, which were used as a model to study the wetting properties of the treated wool knitted fabrics. The dyeing behavior was assessed from the diffusion mechanism point of view. The dyeing kinetics were measured at two different pHs (4.2 and 6.5) and three different temperatures (60, 85, and 100°C) to gain information about the contribution of the surface modification treatment to the dyeing mechanism. The exhaustion and reflectance data were compared, and the apparent diffusion coefficients were calculated. On the basis of the obtained results, a model for the dyeing mechanism of the chitosan treated wool was proposed. When treated with chitosan, the polymer sheath spread on the surface of the fibers acted as a predominant dyeing site in very short dyeing times, thus interacting with the dye and in later stages imparting the dye to the wool fiber. © 2005 Wiley Periodicals, Inc. J Appl Polym Sci 97: 2204–2214, 2005     

半透明氮化硅陶瓷的放电等离子烧结制备及性能

用放电等离子烧结(spark plasma sintering,SPS)技术,以质量分数(下同)为9%氮化铝(A1N),3%氧化镁(MgO)为烧结助剂,在1850℃烧结5min,成功制备了半透明氮化硅(Si3N4)陶瓷.半透明Si3N4陶瓷在中红外波段表现出良好的透过率,最大透过率为66.4%.SPS的快速致密化过程保证了烧结体具有良好的晶体结构,有利于提高透过率.SPS快速的烧结过程和A1N和MgO的加入能够有效抑制烧结过程中Si3N4陶瓷由α相向β相的转变,是制备光学性能良好的Si3N4陶瓷的关键.报道了半透明Si3N4陶瓷的其他性能.光学性能与其他性能的结合,势必大大拓宽Si3N4陶瓷的应用领域.     

Wetting properties of polystyrene ionomers treated with plasma source ion implantation

The wetting properties of polystyrene‐based ionomers treated with plasma source ion implantation (PSII) were investigated by the measurement of water contact angles. When sulfonated ionomers were aged for a few days, the hydrophobic recovery for the ionomers became much slower than that for the nonionic polymers. However, when the samples were aged over 20 days, the water contact angle of the ionomers converged with that of the nonionic polymer. Thus, it was concluded that the ionic interaction between the ionic groups and the presence of ionic groups together resulted in the slow hydrophobic recovery and that the aging effect was significant for the ionomers. For the methacrylate ionomer of low ion content, on the other hand, it was found that the PSII treatment produced only a small change in hydrophobic recovery behavior. Thus, it was suggested that the low ionic content coupled with the small size of the ionic unit might cause changes only of a very insignificant degree in hydrophobic recovery behavior. © 2002 Wiley Periodicals, Inc. J Appl Polym Sci 83: 2500–2504, 2002     

单晶金刚石膜与多晶金刚石膜的制备工艺及性能

本文主要介绍了用微波等离子体化学气相沉积法(以下简称MP CVD法)以甲醇-氢气混合气和丙酮-氢气混合气为源气体,分别以单晶硅的(111)面和人造金刚石的(100)面为衬底材料,制备出了面积为20mm×20mm厚为10μm的多晶金刚石膜和面积为1.0mm×1.0mm厚为5μm的单晶金刚石膜。通过试验发现,源气体配比和衬底温度对薄膜质量起决定性作用。另外,衬底在反应腔中的位置对薄膜的生成也有很大影响。单晶金刚石膜制备过程中衬底金刚石的晶体取向与金刚石薄膜的生长及质量有密切的关系。在金刚石的(100),(110)和(111)面上分别获得了单晶金刚石膜和金刚石多晶粒子。选用扫描电镜、显微激光拉曼、反射电子衍射对多晶金刚石膜及单晶金刚石膜的性能进行了测试。