Effect of hydrometallurgical process parameters on the Mn2O3 nano catalysts derived from spent batteries used in the plasma catalytic oxidation of BTX

Manganese oxide catalysts have been synthesized from the used batteries via hydrometallurgical method and effect of hydrometallurgical parameters such as the effect of acid type (H₂SO₄, HNO₃, HCl), acid concentration (0.5, 1, 1.5, 2 %v/v) and powder to acid ratio (1/50, 1/60, 1/70, 1/80) were in detail investigated. The physico-chemical properties of as-prepared catalysts were characterized by FT-IR, XRD, FESEM, EDX, BET, TEM, and TPR-H₂ analysis. The activity of as-prepared catalysts were investigated towards the oxidation of benzene, toluene, and xylene (BTX) in a plasma-catalytic process. The results show that benzene and toluene conversion were almost constant in the range of 97–98% in case of various acid types, acid concentrations and solid to liquid ratios. However, the xylene conversion were varied in case of different hydrometallurgical factors. The highest xylene conversion was obtained in the presence of MnS0.5–60, which was prepared using H₂SO₄ with concentration of 0.5%v/v and solid to liquid ratio of 1/60. The effect of the input voltage and BTX flow rate on the BTX conversion was also investigated using MnS0.5–60 catalyst in detail.     

Research on phase shift characteristics of electromagnetic wave in plasma

The phase shift characteristics reflect the state change of electromagnetic wave in plasma sheath and can be used to reveal deeply the action mechanism between electromagnetic wave and plasma sheath. In this paper, the phase shift characteristics of electromagnetic wave propagation in plasma were investigated. Firstly, the impact factors of phase shift including electron density,collision frequency and incident frequency were discussed. Then, the plasma with different electron density distribution profiles were employed to investigate the influence on the phase shift characteristics. In a real case, the plasma sheath around the hypersonic vehicle will affect and even break down the communication. Based on the hypersonic vehicle model, we studied the electromagnetic wave phase shift under different flight altitude, speed, and attack angle. The results indicate that the phase shift is inversely proportional to the flight altitude and positively proportional to the flight speed and attack angle. Our work provides a theoretical guidance for the further research of phase shift characteristics and parameters inversion in plasma.     

水提法提取—电感耦合等离子体质谱法测定婴幼儿配方奶粉中的碘

用水提取婴幼儿奶粉中的碘,亚铁氰化钾和乙酸锌盐析法沉淀蛋白,过滤后可以得到澄清处理液。用电感耦合等离子体质谱对提取样液进行测定,130Te作为内标物进行定量分析。该方法简便快捷,检出限为0.10 mg/kg加标回收率为90.8%~109%,相关系数0.999,精密度试验RSD2%。     

New anti-ablation candidate for carbon/carbon composites: Preparation,composition and ablation behavior of Y2Hf2O7 coating under an oxyacetylene torch

Y₂Hf₂O₇ possesses low thermal conductivity and high melting point, which make it promising for a new anti-ablation material. For evaluating the thermal stability and the potential applications of Y₂Hf₂O₇ on anti-ablation protection of C/C composites, Y₂Hf₂O₇ ceramic powder was synthesized by solution combustion method and Y₂Hf₂O₇ coating was prepared on the surface of SiC coated C/C composites using SAPS. Results shown that the coating exhibits good ablation resistance under the heat flux of 2.4?MW/m² with the linear and mass ablation rates are 0.16?μm?s^?1 and ?0.028?mg?s^?1, respectively, after ablation for 40?s. With the prolonging of the ablation time, the increasing thermal stress causes the increase of cracks. Moreover, the chemical erosion from SiO₂ and the physical volatilization of low temperature molten products aggravate failure of the Y₂Hf₂O₇ coating.     

快速灵敏的LC-MS/MS法测定人血浆中阿莫西林并应用于两种制剂的一致性评价

目的: 建立快速灵敏的LC-MS/MS法测定人血浆中阿莫西林浓度，并用于两种阿莫西林胶囊的一致性评价。方法: 采用岛津公司LCMS-8060型LC-MS/MS仪，以MRM模式测定阿莫西林（m/z 366.00/114.00）的浓度，d4-阿莫西林作内标（m/z 370.10/114.05），离子源为ESI源。色谱柱选用Waters ACQUITY BEH C18（2.1×50 mm，1.7 μm），梯度洗脱。血浆样本加入内标，经甲醇沉淀蛋白后取上清液进样检测。结果: 所建方法经验证，其线性、准确度、精密度、最低定量限、提取回收率、特异性、基质效应、稳定性等各项指标均符合CFDA的指导原则及最新核查标准要求，并较文献报道中的方法有处理简单、灵敏度高、色谱峰形好的优点。结论: 所建方法快速、灵敏，适用于人血浆中阿莫西林浓度的检测。用于一致性评价的样本实测，两种制剂生物等效。     

Preparation of nanocrystalline nickel oxide from nickel hydroxide using spark plasma sintering and inverse Hall-Petch related densification

Nanocrystalline nickel oxide (NiO) was prepared from nickel hydroxide by Spark plasma sintering (SPS) and the mechanisms involved in the densification of NiO were studied. Reverse precipitated nickel hydroxide powders were SPS processed at 400, 600 and 700?°C with 70?MPa pressure. Pure NiO with 12?nm crystallite size formed after 400?°C sintering process. However NiO grains had grown to 18 and 38?nm after 600 and 700?°C sintering respectively. NiO pellets prepared using 600 and 700?°C SPS sintering schedules had relative densities of 83% and 94% respectively. Two displacement rate regimes were observed during densification of NiO in both 600 and 700?°C sintering processes. Decomposition of nickel hydroxide and particle sliding of NiO led to first displacement rate maximum while inverse Hall-Petch based plastic deformation facilitated densification during the constant second displacement rate regime. No densification occurred during sintering holding times indicating the limited role that diffusion played during densification.     

BaTiO3基Au纳米颗粒复合薄膜的制备及其光学性质研究

采用溶胶-凝胶（sol-gel）方法，成功的将高体积面分比的Au纳米颗粒复合到BaTiO3的非晶薄膜中，并对其光学性质进行了研究。用XRD、TEM、椭偏仪、吸收光谱、光克尔效应OKE（Optical Kerr Effcet）方法对薄膜进行了表征和测试。从吸收光谱观察到表面等离子体共振SPR（Surface Plasma Resonance)峰随热处理温度升高而红移的现象。光学非线性测试表明薄膜具有高的三阶非线性极化率Χ^(3)和超快的响应时间。     