Physico-chemical characterization of hybrid polymers obtained by 2-hydroxyethyl(methacrylate) and alkoxides of zirconium

Hybrid monolithic materials were prepared through polymerisation of 2-hydroxyethyl methacrylate (HEMA) mixed with zirconium alkoxides (Zr(OBuⁿ)₄, Zr(OPrⁿ)₄ and Zr(OEt)₄), modified by acetylacetonate groups. The molar ratio HEMA/Zr varied between 1 and 4. Thermo-Gravimetry coupled with Mass Spectroscopy (TG-MS) analyses, ¹³C MAS NMR and Dynamical Mechanical Thermal Analysys (DMTA) indicated the polymeric chains were interconnected by the inorganic component.The presence of zirconium alkoxides modified substantially the poly-HEMA properties. Glass transition temperature of hybrid materials derived from butoxy and propoxy was found in the range 50-80 °C, depending on the composition. The typical swelling of p-HEMA in the water, was suppressed by the presence of zirconium compounds. After immersion in distilled water, hybrid polymers showed an initial slight weight increase, followed by a small mass loss, which increases proportionally to the length of alkoxyl group (ethoxide(propoxide(butoxide) and reaches a constant value after about 40 days. The hybrids remained always rigid and transparent. Flexural modulus and strength of about 400-900 and 4-8 MPa were measured.     

SCB火工品的研究与发展

文章评述了半导体桥火工品问世以来的研究成果与发展趋势。主要内容有半导体桥作用机理、半导体桥的结构与封装、半导体桥火工品的特点、半导体桥火工品的应用、半导体桥火工品的研究和发展趋势。     

医用激光治疗机的触摸屏控制系统设计

介绍了医用红宝石激光器触摸屏控制系统的基本结构，分析了医用红宝石激光器中主要电磁干扰（EMI）的产生机制，提出了具体的电磁兼容（EMC）技术措施并得到实验验证。     

The effect of segment length on some properties of thermoplastic poly(ester–siloxane)s

A series of novel thermoplastic elastomers, based on poly(dimethylsiloxane) (PDMS) as the soft segment and poly(butylene terephthalate) (PBT) as the hard segment, were synthesized by catalyzed two‐step, melt transesterification reactions of dimethyl terephthalate and methyl esters of carboxypropyl‐terminated poly(dimethylsiloxane)s (M?_n = 550–2170 g mol^?1) with 1,4‐butanediol. The lengths of both the hard and soft segments were varied while the weight ratio of the hard to soft segments in the reaction mixture was maintained constant (57/43). The molecular structure, composition and molecular weights of the poly(ester–siloxane)s were examined by ¹H NMR spectroscopy. The effectiveness of the incorporation of the methyl‐ester‐terminated poly(dimethylsiloxane)s into the copolymer chains was verified by chloroform extraction. The effect of the segment length on the transition temperatures (T_m and T_g) and the thermal and thermo‐oxidative degradation stability, as well as the degree of crystallinity and hardness properties of the synthesized TPESs, were studied. Copyright © 2003 Society of Chemical Industry     

镍层耐硝酸腐蚀性测试——一种简单的预先探测ENIG镍层“黑盘”现象的测试方法

随着更加精细的SMT、BGA等表面贴装技术的运用,化学沉镍金(ENIG)作为线路板最终表面处理得到了越来越广泛的应用,同时可怕的“黑盘”现象也随之更广泛地“流行”起来,直接导致贴装后元器件焊接点不规则接触不良。为了贯彻执行最好的流程控制和采取有效的预防措施,了解这种焊接失败的产生机理是非常重要的,及早的观测到可能发生“黑盘”现象的迹象变得同样关键。本文介绍了一种简单的预先探测ENIG镍层“黑盘”现象的测试方法-镍层耐硝酸腐蚀性测试,这种测试可以用于作为一种常规的测试方法监测一般化学沉镍溶液在有效使用寿命范围内新鲜沉积的镍层的质量。利用Weibull概率统计分析在不同的金属置换周期(MTO)下镍层的可靠性能表现。结合试验结果得出了一个镍层耐硝酸腐蚀性的判定标准。     

在二(2-乙基己基)磷酸钠的微乳液中金属萃合物对水增溶的影响

测算了由二（2－乙基己基）磷酸钠，金属盐（CoSO4,NiSO4,ZnSO4,MgCl2或Cr(NO3)3)水溶液，正辛醇和正辛烷组成的微乳液中正辛醇从连续油相到界面的ΔGo→i^o和水的极限增容量φ'H2O。用金属萃取络合物反胶束的形成及其亲油性解释了金属离子对φ'H2O和ΔGo→i^o的影响。     

丙烯腈－苯乙烯共聚物水解磺化产物对泥浆的稳定作用

在实验室条件下对用丙烯腈－苯乙烯共聚物在硫酸存在下的水解磺化产物（ＨＳＡＳ）处理的泥浆性能进行了评定。ＨＳＡＳ处理的泥浆有较小的滤失性，较好的耐盐和抗高温性。     

T8钢－聚有机硅氧烷仿生减粘降阻复合涂层的特性

研究了Ｔ８钢－聚有机硅氧烷仿生减粘降阻复合涂层的表面润湿性、磨料磨损特性及对土壤的减粘降阻性能与金属材料相比，仿生复合涂层的表面憎水性显著提高，水在其表面上的接触角达９２°；与４５钢相比，其磨料磨损的体积相对耐磨系数为６３％，降阻率达１５．２２％～２２．２７％     

δ－Al_2O_3纤维／Al－12Si复合材料室温拉伸强度分析

对δ－Ａｌ２Ｏ３纤维／Ａｌ－１２Ｓｉ复合材料室温拉伸强度的分析表明，在实验条件下该复合材料存在δ－Ａｌ２Ｏ３纤维的最小体积分数Ｖｍｉｎ和临界体积分数Ｖｃｒｉｔ，并求出其基体强度σ＇ｍ和室温强度σｃ－δ－Ａｌ２Ｏ３纤维体积分数Ｖｆ直线方程及纤维的临界长度ｌｃ和复合材料的剪切应力τｉ．确定复合材料的ＲＯＭ预测曲线，应首先判断σ＇ｍ是否等于未增强合金的强度σｕｍ才能得出正确的结论     

烧结工艺对液相合成（SrPb）TiO3基陶瓷热敏特性影响的研究

本文在液相合成（ＳｒＰｂ）ＴｉＯ３粉的基础上，研究了升温速率、保温时间、烧结温度及降温方式对（ＳｒＰｂ）ＴｉＯ３基陶瓷的Ｖ型ＰＴＣ热敏特性的影响。实验表明：升温速率对其热敏特性影响不大，保温时间和烧结温度的作用是一致的，具有一最佳范围。而降浊方式对材料的热敏特性影响较大。综合各因素的影响，本配方中，样品的烧结制度定为：以２００℃／ｈ的速率升温，在１２５０℃保温１ｈ，炉冷至９５０℃，保温０．５ｈ，再