对比研究了B和C含量的变化对铸造TiAl基合金宏观和显微组织的影响。结果表明 ，B或C含量的增加均能细化TiAl基合金的晶粒，但二者的作用特点不同。B含量对宏观组织和晶粒尺寸的影响是渐进的，而C对其影响存在一个临界含量。显微观察表明，微量的B就能使合金析出TiB2，随着合金中B含量的增加，硼化物颗粒呈不同的形貌。对于含C合金，当C含量低于临界含量时，在光学尺度上观察不到碳化物相，而当C含量高于临界含量时，合金中生成大量的Ti2AlC碳化物颗粒。讨论了B和C细化TiAl基合金的机制。     

碳化钨对常压烧结氮化硅陶瓷致密化的影响

研究碳化钨对常压烧结Si3N4-MgO－CeO2陶瓷致密化和性能的影响，通过球磨引入适量的碳化钨对烧结氮化硅陶瓷的致密化和性能是有利的，通过控制球磨时间和球料比可控制磨入的碳化钨的含量，当碳化钨含量为3．9wt％时，效果最好，烧结氮化硅陶瓷的相对密度为98．5％，室温抗弯强度为948MPa。     

Ca15(CBN)6(C2)2O- a new cubic structure type containing CBN-anions together with acetylide and oxo anions

Ca₁₅(CBN)₆(C₂)₂O contains CBN⁴⁻ anions as well as C₂⁻ units and isolated O²⁻ anions. The compound is obtained by heating a stoichiometric mixture of CaO, C and BN with an excess of Ca in sealed niobium ampoules to 1270 K. It crystallizes in the space group Ia d with a = 1656.84(9) pm. Preparation, crystal structure, NMR and IR-spectroscopic properties are discussed.     

Hydrogen effects on the passive film formation and pitting susceptibility of nitrogen containing type 316L stainless steels

The effects of hydrogen on the passivity and pitting susceptibility of type 316L stainless steels have been investigated with alloys containing different nitrogen contents (0.015, 0.198 and 0.556 wt.% N). The study revealed that electrochemically pre-charged hydrogen significantly reduced the pitting resistance of alloys conatining 0.015 and 0.198 wt.% nitrogen contents. In alloy with highest nitrogen content (0.556 wt.% N), an increase in the passive film current density with hydrogen was observed without affecting breakdown potential. Auger electron spectroscopy (AES) analysis of the passive film indicated the presence of nitrogen in the passive film. On other hand, for hydrogen charged samples, nitrogen was found to be significantly less in the passive film. In Electrochemical impedance spectroscopy (EIS) measurement, the decrease in semi-circle radius of Nyquist plot, and the polarization resistance, R_P associated with the resistance of the passive film was observed with hydrogen, indicating that hydrogen decreased the stability of the passive film. The present investigation indicated that precharged hydrogen deteriorated the passive film stability and pitting corrosion resistance in these alloys, and the increase in nitrogen content of the alloy offsets the deleterious effect of precharged hydrogen.     

铝合金化对LaNi5-xAlx电子结构的影响

在全电子水平上,基于广义梯度近似密度泛函和全势能线性缀加平面波方法,计算了不同Al含量LaNi5-xAlx(x＝0,0.5,1.0)的晶体结构、能带结构、状态密度等特征.对LaNi5的计算表明:GGA Perdew96的计算结果可信,自旋极化对优化结构和能量的影响不明显;对LaNi4Al的研究表明Al原子最可能取代3g位的Ni原子;对LaNi4 5Al0.5的优化结构与实验结果一致.随着Al含量的升高,晶胞能量、费米面能量升高,如从LaNi5,LaN45Al05到LaNi4Al,费米面能量从-10.591、-10.134 eV升高到-9.441 eV,而Ef上的态密度和材料对应的低温比热容则急剧下降,态密度从11.81、8.86急剧降低到1.61 eV/f.u..并计算给出了LaNi4.5Al0.5的能带结构、状态密度图.     

Visual C++对Solid Works二次开发技术及应用

介绍了三维CAD系统Solid Works的特点及其API函数,讨论了对Solid Works进行二次开发的关键技术及系统设计,并通过实例阐述了利用Visual C 工具开发Solid Works动态连接库DLL的步骤和编程方法,这有利于对Solid Works进行本地化和专业化的二次开发工作,使其在我国企业中更有效地发挥作用.     

Al4C3的形成及对Gr-Al-Si复合材料的作用

Al4C3的生成会影响Gr-Al-Si复合材料的界面反应，然而研究证明在原料中少量的Al4C3存在，有利于提高石墨分布的均匀性，又不影响该材料的高温抗拉强度等综合性能。Al4C3的形成温度以550～600℃为宜，Al4C3的含量可用X射线定量分析来确定。     

离子束增强沉积氮化硅膜及TiAl抗高温氧化性能的改善

用离子束增强沉积（ＩＢＥＤ）方法在金属间化合物ＴｉＡｌ上合成厚度为０．５，１，和２μｍ的氮化硅薄膜。所形成的薄膜为非晶态，膜与基底间存在混合的过渡区，膜与基底结合紧密用ＡＥＳ，ＸＲＤ和ＸＰＳ研究薄膜的组成和结构，高温循环氧化结果表明，经沉积膜的ＴｉＡｌ试样的抗氧化性能显著提高其中沉积０．５μｍ薄膜的试样表现出极好的抗循环氧化性能由ＳＥＭ及ＥＤＳ分析得出，良好的高温稳定性能、高的膜／基底结合力和形成富Ａｌ２Ｏ３和硅化物的保护层是提高ＴｉＡｌ抗高温氧化性能的主要因素．     

空气-乙炔碳氮氧离子多元共渗工艺研究

用空气-乙炔混合气体作为气源,对40Cr钢进行了离子碳氮氧多元共渗;用光学金相显微镜、X射线衍射仪和显微硬度计,对渗层形貌、物相和显微硬度进行了分析检测。结果表明:乙炔浓度是影响性能的关键因素,它对硬度、物相起着决定性的作用。与常规离子渗氮相比,以空气-乙炔混合气体作为气源的碳氮氧离子多元共渗工艺操作简便,成本低廉。     

ICP-OES法测定氮化硅粉中微量元素Fe、Al、Ca的含量

本文提出了电感耦合等离子体发射光谱法直接测定Si3N4粉中微量元素Fe、Al、Ca含量的分析方法。进行了样品分解试验,考察了基体对测定元素的影响以及各元素间的相互干扰情况,优化了分析条件,各元素的相对标准偏差均在5%以下,回收率为94%～102%。