Effect of Chromium Powder on Sintering Property of Chrome Oxide Materials

The specimens were prepared using Cr2O3 micropowder, TiO2 micropowder and chromium powder as starting materials, PVA as binder, after spraying granulation and cold isostatic pressing, firing at 1 450 ℃ for 3 h in standard nitrogen and oxygen control atmosphere (oxygen partial pressure was 1 010 Pa and 10.1 Pa, respectively). Effects of chromium powder (mass percent were 0, 0.5%, 1.0%, 1.5% and 2.0%, respectively) on sintering behaviors of Cr2O3 materials were researched. The results show that: adding 0.5% c...     

金属铬粉对致密氧化铬材料烧结性能的影响

以Cr2O3微粉、TiO2微粉、金属铬粉为原料,聚乙烯醇(PVA)为结合剂,经喷雾造粒、冷等静压成型后,采用标准氮气和氧气的混合气体控制气氛,其氧分压分别控制在1 010、10.1 Pa,1 450 ℃保温3 h烧成,研究了金属铬粉加入量(其质量分数分别为0、0.5%、1.0%、1.5%和2.0%)对致密氧化铬材料烧结性能的影响.结果表明:添加0.5%的金属铬粉可明显降低试样内部氧分压,且由于此时氧化反应引起的膨胀小,致密氧化铬材料在1 010和10.1 Pa的较高氧分压下即可实现致密化烧结;致密氧化铬材料中引入的金属铬粉不宜过多,否则金属铬粉氧化发生的膨胀反应会导致材料的性能下降.     

镓、铟与酸性铬深蓝络合物吸附波的研究

在醋酸盐缓冲溶液中,用单扫示波极谱法得到了镓（Ⅲ）、铟（Ⅲ）与酸性铬深蓝两个良好的导数极谱波。两个波的峰电位分别为－０．５１Ⅴ和－０．６３Ⅴ（ｖｓ．ＳＣＥ）。线性范围镓（Ⅲ）为７．２０×１０－７～７．４６×１０－６ｍｏｌ／Ｌ;铟（Ⅲ）为１．７４×１０－７～４．８８×１０－６ｍｏｌ／Ｌ。用多种电化学方法研究了两个极谱波的性质及其电极反应机理,试验表明这两个谱波属络合物吸附波。     

电镀铝车轮的镀层性能测试

前言 对电镀铝车轮镀层质量的评定有两类方法,其一是让电镀后的铝车轮在使用条件下进行实效考核,这类方法虽然结果最准确,但测定周期很长,因而,一般广泛采用第二类方法,     

高纯镁砂与西藏铬矿间固相反应的研究

为了考察镁砂与铬矿间的反应过程及其特征,以高纯镁砂颗粒和西藏铬矿细粉为原料,在200 MPa下制成50 mm×20 mm的试样,然后在高温隧道窑中于1 750℃烧成,并对烧成后的试样进行BSE和EDS分析。结果表明:随着距离镁砂-铬矿边界距离的增加,镁砂颗粒内部Cr、Fe、Al的质量分数均减少,镁砂颗粒边缘富含Fe,颗粒内部Cr含量较高。镁砂-铬矿边界呈直接结合,镁砂内的尖晶石相分布较均匀。     

影响活塞环复合镀铬层网纹特性的因素研究

本文简要介绍了活塞环复合镀铬技术及其主要性能指标和网纹特性定义,重点分析了影响活塞环复合镀铬层网纹特性的因素,试验表明镀铬槽液成份特别是添加剂的种类和含量、镀液温度和特殊处理方法工艺等是影响网纹特性的最主要因素。     

烷醇酰胺琥珀酸单酯磺酸二钠盐的助鞣性能研究

在传统铬鞣工序中应用加脂剂不仅有助鞣作用，而且能赋予蓝坯革一定的加脂效果。我们在实验中合成了两种烷醇酰胺琥珀酸单酯磺酸二钠盐──Ｎ—２—羟乙基烷基酰胺琥珀酸单酯磺酸二钠［简称ＨＥＡＡＳＳ］和Ｎ，Ｎ—二（２—羟乙基）烷基酰胺二（琥珀酸单酯磺酸二钠）［简称ＤＨＥＡＡＤＳＳ］，将其试用于浸酸铬鞣，发现二者均有良好的助鞣效果，但ＤＨＥＡＡＤＳＳ的助鞣性能要优于ＨＥＡＡＳＳ。     

禁用含金属染料的新情况及新染料的开发

本文阐述了欧盟发出的禁用和限制含金属染料的新情况，介绍了取代禁用和限制含金属染料的新型染料。     

铬鞣--一种可持续发展的工艺

从铬（Ⅲ）盐鞣革的优越性、铬（Ⅲ）对人类健康和环境的影响,以及与其它鞣法相比,铬鞣具有更为成熟的回收利用方法这几方面出发,论述了铬鞣是一种可持续的工艺,不可能被其它鞣法完全取代。