我国的锑深加工产品

介绍了目前我国锑深加工产品的种类、用途、主要生产厂家 ,以及某些产品的生产工艺和质量状况。并针对国内锑品现状 ,提出了几点建议     

合成2,4-二叔丁基苯酚工业试验

以离子交换树脂为催化剂，苯酚和甲基叔丁基醚为原料合成2，4-二叔丁基苯酚(简称2，4酚)，合成产物经过滤再经间歇真空精馏精制提纯，得到高纯度的2，4酚成品。成品精馏后釜中残液在酸性白土催化剂的作用下通过歧化反应生成对叔丁基苯酚，再经精馏提纯得到成品对叔丁基苯酚。通过工艺优化，使2，4酚、对叔丁基苯酚形成联产生产工艺，降低了生产原料消耗和成本。     

新标准新突破--MP4NET引领安防行业发展

介绍了视频压缩技术从MPEG1、MPEG2到目前主流技术MPEG4,分析了数字视频存储、检索、传输上优于模拟技术的特点,从而使视频网络应用,数据库支撑的应用、安防行业的数字化应用的迅速发展。     

Microstructural Investigation on Failure of Internal Drive Shaft

17-4 PH stainless steel is used as internal drive shaft material in liquid engine pumps. One of the drive shafts failed during operation. The shaft pieces were in contact for short duration after failure, which has resulted in abrasion of fractured surfaces. Samples from the location of failure were taken, and investigation of the failure was carried out using optical and scanning electron microscopy. The microstructural analysis of the material and fractographic analysis of the fractured surface show that the failure was caused by excessive torsion.     

兼容IPv4及IPv6的网络程序设计

介绍了在Window系统中设计兼容IPv4及IPv6的网络程序的方法,并给出了用WinsockAPI编程的具体步骤。     

Influence of Ni Interlayers on the Mechanical Properties of Ti6Al4V/(WC-Co) Friction Welds

Ni interlayers were introduced prior to dissimilar friction welding of Ti6Al4V base material to three cemented carbide substrates. The fracture strength of Ti6Al4V/(WC-6 wt% Co) welds were poor and were markedly improved when 20-µm thick Ni interlayers were introduced prior to dissimilar friction welding. These results were only produced when the (WC-6 wt% Co) cermet was electroplated prior to friction welding. When the Ti6Al4V alloy was electroplated prior to friction welding, fractured WC particles and cracking were observed in the (WC-Co) carbide substrate. The fracture strengths of Ti6Al4V/(WC-11 wt% Co) and Ti6Al4V/(WC-24 wt% Co) welds were not improved when 20-µm thick Ni interlayers were introduced prior to friction welding. During mechanical testing, the Ni layer retained at the dissimilar joint interface created a region of weakness.     

Synthesis of chemically and structurally modified dicalcium silicate

This paper describes the synthesis of cements, chemically and structurally related to Ca₂SiO₄. Silica was obtained from rice hull after heating at 600 °C. Calcium oxide and small amounts of barium chloride were mixed in order to obtain a final (Ca/Si) or (Ca+Ba)/Si ratio equal to 1.95, 1.90, and 1.80, which is lower than in the conventional cement. The solids were mixed and ultrasonically treated for 1 h with a water/solid ratio of about 20. After drying and grinding, the mixtures were heated up to 1100 °C. It was possible, in some cases, to obtain a cementitious material. These cements are structurally related to β-Ca₂SiO₄ and the lower (Ca+Ba)/Si ratio obtained was 1.95. The initial chemical compositions of these cements are: (Ca_1.83+Ba_0.12)SiO₄ and (Ca_1.79+Ba_0.16)SiO₄. A further lowering in the (Ca+Ba)/Si ratio changes the nature of the silicates.     

用环氧厚浆涂料防混凝土碳化

介绍了针对早期建筑的混凝土桥梁碳化情况采用H52-S4环氧厚浆涂料进行封闭保护、防腐处理的施工方法及施工工艺，并提出施工中应注意的有关事项，对温度影响、表面气泡处理进行了讨论，提出合理化建议。     

MPEG-4流媒体技术及其实现方法

详细地介绍了一种基于MPEG-4压缩的嵌入式网络流媒体采集、传输和控制应用系统的设计与实现技术。该嵌入式平台采用203 MHz的ARM920T内核处理器S3C2410B,嵌入式操作系统采用Linux操作系统,用户可在这个系统平台上进行自主软件开发。视频采集模块采用TI公司的TVP5145,视频压缩芯片采用硬压缩W IS GO7007B进行处理,将Y:Cb:Cr格式的视频流转换为MPEG-4编码。     

环氧基的PCB对无铅组装的兼容性

综述了环氧树脂基的PCB与无铅化组装的兼容性问题。经过大量试验表明,常规的FR-4基材和双氰胺固化的高Tg基材是不能满足无铅化组装要求的,而采用酚醛固化的中等-Tg的环氧树脂基材是可能成为无铅化组装用基材的。同时,PCB制造过程也起着重要的作用。PCB设计和再(回)流焊的加热梯度也影响着无铅化的性能。