Study of the solid-liquid equilibria in the LiPO3-Y(PO3)3 binary system

The LiPO₃-Y(PO₃)₃ system has been studied for the first time. Microdifferential thermal analysis (μ-DTA), infrared spectroscopy (IR) and X-ray diffraction were used to investigate the liquidus and solidus relations. The only new compound observed within this system is LiY(PO₃)₄, melting incongruently at 1104 K. An eutectic appears at 4±1 mol% Y(PO₃)₃ at 933 K. LiY(PO₃)₄ crystallizes in the monoclinic system C_2/c with a unit cell: a=16.201(4) Å, b=7.013(2) Å, c=9.573(2) Å, β=125.589(9)°, Z=4 and V=884.5 Å³, which is isostructural to LiNd(PO₃)₄. The infrared absorption spectrum indicates that this salt is a chain polyphosphate.     

疏水缔合型聚丙烯酰胺的合成与性能评价

为了提高高相对分子质量的聚丙烯酰胺的抗温抗盐性能,利用自制的两亲表面活性单体与丙烯酰胺共聚合成了疏水缔合型聚丙烯酰胺并进行室内评价。结果表明,在高温、高盐、高钙条件下,合成的疏水缔合型聚丙烯酰胺具有良好的增粘性和较强的热稳定性;克服了疏水缔合型聚合物在盐水中溶解性差的问题,可用各种矿化度的盐水和油田产出污水配制;具有良好的无机盐增粘性能和抗温性能。     

N,N′-二(β-十八酰氧基)乙基乙二胺二乙酸钠的合成及性能研究

用 N,N′-二羟乙基乙二胺、氯乙酸钠合成了 N,N′-二羟乙基乙二胺二乙酸钠(中间体),中间体再与硬脂酰氯反应制备了一种新型 Gemini 两性表面活性剂 N,N′-二(β-十八酰氧基)乙基乙二胺二乙酸钠。对产物合成条件进行了考察,优化的反应条件为:n(硬脂酰氯):n(中间体)=2.5,溶剂 V(水):V(氯仿)=1:2,pH=9.0～10.0,反应温度15～20℃,反应时间5 h。通过红外光谱和质谱分析确定了产物结构,并测试了产物的表面性能。结果表明,在25℃时,该产物的临界胶束浓度为0.24 mmol/L,临界胶束浓度下的表面张力为35.7 mN/m;即时泡沫高度为250 mm,5 min 后泡沫高度为220 mm;乳化时间为22.48 min(甲苯-水物系)和4.65 min(正己烷-水物系),亲水-亲油平衡值为5.4,等电点为 pH 3.3～6.5。     

4-氨基-3-肼基-5-巯基-1,2,4-三唑的合成及其对醛的检验

以硫脲和水合肼合成了可用于检验醛的试剂——4-氨基-3-肼基-5-巯基-1，2，4-三唑(别名：紫醛)，其结构通过红外光谱、核磁进行了确定。试验表明，紫醛对醛的检验敏感、专一、快速、操作简单。     

Synthesis and properties of novel amphiphilic sulfated ionomers by the ring‐opening reaction of an epoxidized styrene–butadiene–styrene triblock copolymer

A method for the synthesis of novel sulfated ionomer of styrene–butadiene–styrene triblock copolymer (SBS) was developed. SBS was first epoxidized by performic acid in the presence of a phase‐transfer catalyst; this was followed by a ring‐opening reaction with an aqueous solution of alkali salt of bisulfate. The optimum conditions for the ring‐opening reaction of the epoxidized SBS with an aqueous solution of KHSO₄ were studied. During the ring‐opening reaction, both phase‐transfer catalyst and ring‐opening catalyst were necessary to enhance the conversion of epoxy groups to ionic groups. The products were characterized with Fourier transform infrared spectrophotometry and transmission electron microscopy (TEM). After the potassium ions of the ionomer were substituted with lead ions, the lead sulfated ionomer exhibited dark spots under TEM. Some properties of the sulfated ionomer were studied. With increasing ionic groups or ionic potential of the cations, the water absorbency and emulsifying volume of the ionomer and the intrinsic viscosity of the ionomer solution increased, whereas the oil absorbency decreased. The sulfated ionomer possessed excellent emulsifying properties compared with the sulfonated SBS ionomer. The sodium sulfated ionomers in the presence of 10% zinc stearate showed better mechanical properties than the original SBS. When the ionomer was blended with crystalline polypropylene, a synergistic effect occurred with respect to the tensile strength. The ionomer behaved as a compatibilizer for blending equal amounts of SBS and oil‐resistant chlorohydrin rubber. In the presence of 3% ionomer, the blend exhibited much better mechanical properties and solvent resistance than the blend without the ionomer. SEM photographs indicated improved compatibility between the two components of the blend in the presence of the ionomer. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Synthesis and characterization of bacterial cellulose/alginate blend membranes

Bacterial cellulose and alginate in an aqueous NaOH/urea solution were used as substrate materials for the fabrication of a novel blend membrane. The blend solution was cast onto a Teflon plate, coagulated in a 5 wt % CaCl₂ aqueous solution, and then treated with a 1% HCl solution. Supercritical carbon dioxide drying was then applied for the formation of a nanoporous structure. The physical properties and morphology of the regenerated bacterial cellulose and blend membranes were characterized. The blend membrane with 80% bacterial cellulose/20 wt % alginate displayed a homogeneous structure and exhibited a better water adsorption capacity and water vapor transmission rate. However, the tensile strength and elongation at break of the film with a thickness of 0.09 mm slightly decreased to 3.38 MPa and 31.60%, respectively. The average pore size of the blend membrane was 10.60 Å with a 19.50 m²/g surface area. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Synthesis and magnetic properties of novel fully conjugated polymeric complexes containing 1,10‐phenanthroline

A novel fully conjugated polymer containing 1,10‐phenanthroline (DAPcDOD) was first synthesized by the polycondensation of 2,7‐dimethyl‐2,4,6‐octatriene‐1,8‐dial with 5,6‐diamine‐1,10‐phenanthroline. Three polymeric complexes were first prepared by the reaction of DAPcDOD with NiSO₄, CoCl₂, and FeSO₄, respectively. The structures of the polymer and the complexes were characterized by IR, ¹H‐NMR, and elemental analysis. The magnetic behaviors of these complexes were measured as a function of magnetic field strength (0–50 kOe) at 5 K and as a function of temperature (5–300 K) at a magnetic field strength of 30 kOe. The results show that DAPcDOD–Ni²⁺ and DAPcDOD–Co²⁺ were soft ferromagnets, whereas DAPcDOD–Fe²⁺ exhibited the features of an antiferromagnet. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Maghnite‐H+, a solid catalyst for the cationic polymerization of α‐methylstyrene

The polymerization of α‐methylstyrene (AMS) catalyzed by Maghnite‐H⁺ (Mag‐H) was investigated. Mag‐H is a montmorillonite sheet silicate clay, exchanged with protons. It was found that the cationic polymerization of AMS is initiated by Mag‐H at ambient temperature in bulk and in solution. The effect of the amount of Mag‐H, the temperature, and the solvent was studied. The polymerization rate increased with increase in the temperature and the proportion of catalyst, and it was larger in nonpolar solvents. These results indicated the cationic nature of the polymerization. It may be suggested that the polymerization is initiated by proton addition to monomer from Mag‐H. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

A strategy for the electro-organic synthesis of new hydrocaffeic acid derivatives

Electrochemical treatment processes can significantly contribute to the protection of the environment through the minimization of waste and toxic materials in effluents. From a pharmaceutical point of view and due to the existing resemblance between the electrochemical and biological reactions, it can be assumed that the oxidation mechanisms on the electrode and in the body share similar principles. In this paper, the application of electrochemical studies in the design of an environmentally friendly method was delineated for the new hydrocaffeic acid (HCA, 3,4-dihydroxy hydrocinnamic acid) derivatives synthesis at carbon electrodes in an undivided cell. In this cell, the EC mechanism reaction was involved, comprising two steps alternatively; (1) electrochemical oxidation and (2) chemical reaction. In particular, the electro-organic reactions of HCA, an important biological molecule, were studied in a water–acetonitrile (90:10 v/v) mixture in the presence of benzenesulfinic acid (3) and p-toluenesulfinic acid (4). The research included the use of a variety of experimental techniques, such as cyclic voltammetry, controlled-potential electrolysis and product spectroscopic identification.