A Silicon–Silica Nanocomposite Material

The synthesis and characterization of a novel silicon–silica nanocomposite material are reported. A self‐assembly method allows the encapsulation of silicon nanoclusters within the channels of a periodic mesoporous silica thin film. The result is the formation of a silicon–silica nanocomposite film with bright, room‐temperature photoluminescence in the visible range, and a nanosecond luminescence lifetime. The properties of the nanocomposite material have been studied by several analytical techniques, which collectively show the existence within the channels of non‐diamondoid‐structure‐type silicon nanoclusters with various hydrogenated silicon sites. It is estimated that the silicon nanoclusters in the silica mesoporous films occupy up to 39 % of the accessible pore volume. The nanocomposite film shows improved resistance to air oxidation compared to crystalline silicon. The high loading and chemical stability to oxidation under ambient conditions are important advantages in terms of the development of silicon‐based light‐emitting diodes from this class of materials.     

Fabrication of Arsenic Sulfide Optical Fiber with Low Hydrogen Impurities

Arsenic sulfide glass optical fibers typically possess extrinsic absorption bands in the infrared wavelength region associated with residual hydrogen and oxygen related impurities, despite using purified precursors. We report a purification process based on the addition of tellurium tetrachloride (TeCl₄) to the glass. During melting, the chlorine from TeCl₄ reacts with the hydrogen impurities to produce volatile products (e.g., HCl) that can be removed by subsequent dynamic distillation. The processing conditions have been modified accordingly to produce optical fibers with significantly reduced loss due to hydrogen sulfide impurity content (1.5 dB/m).     

Surface characteristics of fluorine-modified PAN-based carbon fibers

Different fluorination methods were applied to modify the surface properties of carbon fibers. The relationship between the degree of fluorination and the physicochemical properties of carbon fibers was studied using a combination of mechanical tests, elemental analysis (EA), X-ray photoelectron spectrometry (XPS), and X-ray diffraction (XRD). EA and XPS analyses of fluorinated carbon fibers showed that treatment with mixtures of F₂/O₂ introduced a much higher fluorine concentration than that with F₂ only. However, XRD analysis showed that there was no increase in the interlayer distance, due to the mild fluorination condition applied. Consequently, the oxyfluorination was one of the more effective methods to increase surface polarity of carbon fibers, which probably played an important role in improving the tensile properties of the fibers in the epoxy resin system.     

Effect of fiber types on relevant properties of porous asphalt

The research was conducted to evaluate the effects of cellulose and polyester fibers on the properties of porous asphalt mixes, using the tests of draindown, abrasion, volumetric properties, rutting, and moisture damage. Images of scanning electron microscopy and X-ray computerized tomography were adopted to identify the microstructure of the fiber and inner stone skeleton of porous asphalt. The influence of rutting parameter （G＊/sin δ） of asphalt modified by different fibers on the rutting resistance of the mixes was investigated. Based upon MOHR-COULOMB theory, the cohesion and the angle of internal friction of the mixes were derived from both indirect tension and unconfined compression strength. The experimental results indicate that fibers mainly stabilize asphalt binder and thicken asphalt film around aggregates. Furthermore, they result in the improved mechanical strength of porous asphalt mixes at high temperature slightly. From comparison analysis, cellulose fibers appear to perform better than polyester fibers in porous asphalt mixes.     

Inside Front Cover: Three‐Dimensionally Ordered Gold Nanocrystal/Silica Superlattice Thin Films Synthesized via Sol–Gel Self‐Assembly (Adv. Funct. Mater. 7/2006)

The synthesis of three‐dimensionally ordered, transparent gold‐nanocrystal (NC)/silica superlattice thin films using the self‐assembly (by spin‐coating) of water‐soluble gold nanocrystal micelles and soluble silica is reported by Fan and co‐workers on p. 891. The robust, 3D NC/silica superlattice films are of interest for the development of collective optical and electronic phenomena, and, importantly, for the integration of NC arrays into device architectures. Nanocrystals and their ordered arrays hold many important applications in fields such as catalysis, surface‐enhanced Raman spectroscopy based sensors, memory storage, and electronic and optical nanodevices. Herein, a simple and general method to synthesize ordered, three‐dimensional, transparent gold nanocrystal/silica superlattice thin films by self‐assembly of gold nanocrystal micelles with silica or organosilsesquioxane by spin‐coating is reported. The self‐assembly process is conducted under acidic sol–gel conditions (ca. pH 2), ensuring spin‐solution homogeneity and stability and facilitating the formation of ordered and transparent gold nanocrystal/silica films. The monodisperse nanocrystals are organized within inorganic host matrices as a face‐centered cubic mesostructure, and characterized by transmission electron spectroscopy and X‐ray diffraction.     

Influence of the amount of ferromagnetic addition on the rheological properties of spinning solutions,the structure,the strength,and thermal properties of polyacrylonitrile fibres

The rheological properties of spinning solutions of polyacrylonitrile in dimethyl formamide (DMF) containing various amounts of a ferromagnetic nanoaddition were investigated. The porous structure, the strength and thermal properties of fibers obtained from these solutions were assessed, as well as the uniformity of the nanoaddition distribution on the fiber surface was estimated. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

A comparative study of short nylon fiber—Natural rubber composites prepared from dry rubber and latex masterbatch

A novel method for the preparation of short nylon fiber–natural rubber composites was developed in which short fibers chopped to approximately 6 mm were incorporated in the latex stage and processed into sheet form. By this method, mixing cycle time was reduced without compromising the fiber dispersion. Fiber breakage during mixing was reduced. The new composites when compounded with a dry bonding system based on hexamethylenetetramine, resorcinol and hydrated silica (HRH) showed improved modulus, tensile strength and abrasion resistance compared to conventional composites. Tear strength, resilience, and compression set were similar to the conventional composites. SEM analysis indicated better interaction between matrix and fibers in the case of latex master batch. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Evaluation of improvement of physical and mechanical properties of bamboo fibers due to alkali treatment

Bamboo strips treated with caustic solutions of different concentrations, e.g., 5%, 10%, 15%, 20%, 25%, and 50%, were subjected to mechanical testing giving stresses on tensile strength, percent elongation at break, flexural strength, flexural modulus, and toughness. The change in average density was ?15%, and the weight loss value shows a maximum of 21.94% at 50% alkali treatment. The mechanical properties of bamboo strips increase steadily with increasing concentration of caustic soda, showing a comparable increased value at 15 and 20%, and then exhibiting a gradual fall. The percent elongation at break corroborates these observations showing a continuous decreasing trend. The properties under investigation exhibit a clear transition in between 15 and 20% alkali concentration. The morphology of strips was studied by scanning electron microscope and polarizing light microscope. The crystal structure of both untreated and treated strips was compared by XRD analysis. In both cases, the breakdown of the crystal structures of the cellulose fibers and the recrystallization or reorientation of the degraded chains that are devoid of hemicellulose are quite apparent. However, at a very high concentration (to the extent of 25%) the breakdown of structure predominates much more over the reorientation or recrystallization. © 2007 Wiley Periodicals, Inc. J Appl Polym Sci, 2008     

Several ways to produce porous carbon monoliths by template assisted routes

Several ways to produce microporous and mesoporous carbon monoliths by template assisted synthesis routes are described. Pressed zeolite (HY) and silica powder tablets have been used as templates. Sucrose acts as a carbon precursor and as a binder between the carbon particles as well. In the case of zeolite template, the carbon porosity could be increased by additional loading of the template with ethene. Due to the balance between mechanic stability and porosity of the carbon monolith, an optimal amount of sucrose is required. The final products were characterized by low temperature nitrogen adsorption.