CaF_2/ZnO的制备及光催化性能研究

ZnO因其费用低、活性高、无毒等特点,在光催化领域有着广泛的应用前景。通过向ZnO中掺入其它物质制备复合材料,可以达到调控ZnO的光催化性能的目的,扩大ZnO的具体应用范畴。以ZnO为主体研究材料,向ZnO中加入不同质量比的CaF_2,通过沉淀法制备CaF_2/ZnO复合材料。利用x-射线衍射分析(XRD)、扫描电镜(SEM)等手段对此复合材料的晶相、组份及微观结构进行表征。通过紫外-可见吸收光谱研究该复合材料在可见光、紫外光下降解亚甲基蓝的效率,发现与纯ZnO相比,可见光下CaF_2/ZnO复合材料对亚甲基蓝的降解效率随着掺入CaF_2的质量比的提高,呈现先下降后升高的趋势;而紫外光下CaF_2/ZnO复合材料对亚甲基蓝的降解效率都要比纯ZnO要高。     

ZnO不同微结构/Cu_4Bi_4S_9异质结光生电荷分离机制与光电性质

采用不同方法分别制备出ZnO纳米颗粒、纳米线、纳米棒、纳米管等4种微结构薄膜,以Cu_4Bi_4S_9(CBS)纳米带为电子给体制备出ZnO不同微结构/CBS异质结。稳态光电压谱结果表明各异质结构都具有优于单一组分的光伏响应,而且光伏性质呈现出,ZnO纳米管/CBS>ZnO纳米棒/CBS>ZnO纳米线/CBS>ZnO纳米颗粒/CBS的特点。较弱正外电场诱导下各异质结构仍然保持稳态下的光伏响应特性。随着外电场逐步提高,ZnO纳米颗粒/CBS光伏性质增加显著,+2 V电压诱导下,ZnO纳米颗粒/CBS已接近ZnO纳米管/CBS光伏响应强度,并明显高于另外2类异质结构光伏性质。从电子受体微结构、异质结厚度、内建电场、能级匹配等方面,分析了关键因素的综合作用对光生电荷分离和收集效率的影响。     

碳微球对中空ZnO结构和药物缓释性能的影响

以碳微球为模板制备中空ZnO微球,接着采用浸渍法将防霉剂填充在中空ZnO微球中,同时对其在水中的缓释效果进行了研究.采用扫描电镜(SEM)和透射电镜(TEM)研究了反应时间和葡萄糖浓度对碳微球形貌的影响,以及不同碳微球模板对中空ZnO微球形貌和结构的影响.SEM和TEM测试结果表明:采用水热法成功地制备了尺寸为50~200nm的碳微球和40nm左右的中空ZnO微球.缓释实验结果表明:载药中空ZnO微球从1h到9h释放的防霉剂浓度从0.008 3mg/mL增加到0.021 4mg/mL,缓释效果明显.     

高压高温制备Sb掺杂的P型ZnO及电致发光

以ZnO和Sb_2O_3为前驱物,在5GPa、1100~1450℃条件下,制备出电学性能稳定的掺Sb的p型ZnO(记作ZnO:Sb)。其中1450℃掺杂4.6%Sb时合成了性能最好的P型ZnO:Sb,电阻率为1.6×10~(-2)Ωcm,载流子浓度为3.3×10~(20)cm~(-3),迁移率为12.1cm/V s。p型导电是由位于Zn位的Sb和两个Zn空位组成的复合受主引起的。测定了受主能级为113meV,讨论了压力对p型ZnO的形成和电性能的影响。此外,以高质量ZnO纳米线作为LED的发射层,通过将p型ZnO:Sb中的空穴注入ZnO纳米线中实现了激光发射。当注入电流达到20mA时,电致发光(EL)的功率可达到10mW。     

Au修饰ZnO纳米带制备及光催化特性研究

通过水热法制备ZnO纳米带,通过溅射的方法在ZnO纳米带进行表面Au修饰.通过扫描电镜、X射线衍射、光致发光等测试手段对样品的形貌、结构和光学性质进行表征.研究ZnO纳米带Au修饰前后的光催化活性的变化.结果表明,Au修饰ZnO纳米带样品对甲基橙降解效果有明显的提高.     

Surface passivation of nanocrystalline silicon powder derived from cryomilling

The surface passivation mechanism of nanocrystalline silicon powder was studied. The liquid nitrogen/argon was used as the medium to prepare the nanocrystalline silicon powder, using a cryomilling technology. The X-ray diffraction, transmission electron microscopy, plasma emission spectroscopy and infrared spectrum were used to analyze the prepared samples, and density functional theory was used to investigate the cryomilling process. For nanocrystalline silicon powder cryomilled with liquid N2, the amorphous outer layer with N element is formed On the surface, and chemisorption caused by the formation of Si-N-Si bond leads to the surface passivation; although physisorpfion also he confirmed, the Si-N bond is steady after exploded in air for 30 days and no new bond is observed. For nanocrystalline silicon powder cryomilled with liquid At, no new chemical bond is Observed, Ar element absorbs on the surface of the prepared powder only through physisorption, and after exploded in air for 30 days, a Si-O bond can be observed obviously.     

Structural,optical and electrical properties of Li-doped ZnO thin films influenced by annealing temperature

Li-doped Zn O thin films had been grown by radio frequency magnetron sputtering and then annealed under various annealing temperatures. The characteristics of Zn O films were examined by XRD, FESEM, Hall measurement and optical transmission spectra. Results showed that p type conduction was observed in Lidoped Zn O films annealed at 500-600 ℃ and the p type Zn O films possessed a good crystalline with c-axis orientation, dense surface, and average transmission of about 85% in visible spectral region.     

Stber法制备单分散,粒径可控碳球及其应用

采用Stber法,以间苯二酚和福尔马林为原料,制备了单分散,粒径可控的碳球.讨论了醇/水比、不同种类的醇、水浴温度、反应物和氨水添加量等对碳球粒径和形貌的影响,并通过SEM、FT-IR、XRD和DLS对最终产物的粒径、形貌和组成进行了表征.结果表明:随着醇/水比、醇的烷链、反应物和氨水的添加量增加时,碳球的粒径变大,且粒径分布在370~1 050nm之间;最佳水浴温度为30℃;碳球具有强的吸附作用,以碳球为牺牲模板,制备出了粒径分布均匀的空心ZnO/ZnFe2O4纳米球.     

IHI推出PEFC系统制氢用高活性催化剂

日本石川岛播磨重工业公司（IHI公司）开发出聚合物电解质电池（PEFC）系统制氢用高活性Pd／ZnO塍化剂。这一基本技术的开发对燃料电池的工业化做出了贡献。用这种新催化剂代替现有Cu／ZnO催化剂，能为汽车热转换（ATR）用新甲醇转换装置开创发展前景。     

纳米ZnO晶体的制备与表征

采用一种简单的直接物理蒸发法制备了纳米ZnO晶体,该生长过程在无催化剂的条件下于900~1 200℃下进行的。所得产物用X射线衍射仪(XRD)和扫描电子显微镜(SEM)进行了表征。结果表明所得的产物属于纤锌矿结构的高纯度六方相ZnO,在实验中发现在900 ~1 000℃的条件下容易生成纳米棒,在1 000 ~1 100℃的条件下容易生成纳米线,在1 100 ~1 200℃的条件下容易生成纳米梳。并简单讨论了其生长机理,提出所得纳米结构是通过简单的VS(Vapor-Solid)机制生长的。