Filiform corrosion is mainly considered as a cosmetic attack and is undesirable in most applications. The initiation and propagation of the filaments are related to different parameters such as the presence of defects, the permeability of the coating to water and oxygen, the adherence of the paint system and the presence of salts.
The aim of this work is to study the behaviour of painted aluminium samples towards filiform corrosion or delamination. The 6082 Aluminium alloy was selected and the samples were covered with a cataphoretic epoxy primer without lead (PPG Industries France). Prior to the application of the electrocoat, the samples were pre-treated by a commercial Zr/Ti or chromate conversion treatment or simply etched with a commercial acid etching product.
Filiform corrosion was studied by the normalized test (ISO/DIS 4623): painted and scratched samples were inoculated in HCl and exposed in a constant humidity chamber at 40 °C and 82% RH for 3 weeks. After exposure the samples were subjected to a visual and optical microscopic examination.
Electrochemical impedance spectroscopy was used to study the sensitivity to filiform corrosion. The operating mode of this test is similar to the normalized one. The samples were scratched before inoculation for 1 h in HCl and then exposed to the humidity chamber for a maximum of 4 days. The samples were tested by EIS in an acidified 0.1 M Na2SO4 electrolyte solution. The resulting impedance spectra were analyzed with an appropriate equivalent electrical circuit which allows the evaluation of the exposed metallic surface area, directly related to the extent of filiform corrosion or delamination. Different parameters were varied: the exposure time in the humidity chamber; the immersion time in the electrolyte sulphate solution as well as its pH and the coating thickness. 相似文献
A long thin conducting stripline embedded in a dielectric and centered between two large conducting plates, i.e., the stripline environment, is considered. The stripline is modeled as infinitely long, infinitely thin, and perfectly conducting by first considering a stripline of finite length, thickness, and conductivity in a dielectric layer. Starting from Maxwell's equations and assuming that the current on the stripline is a propagating wave in length direction, asymptotic expressions for the fields inside and in the neighbourhood of the stripline are deduced. These expressions are used to model the stripline in the stripline environment, which leads to a boundary-value problem for the electric potential. This problem is solved by two different approaches, leading to integral equations for the current and for an auxiliary function describing the electric potential. A relation between the current and the auxiliary function is deduced, which is used to obtain asymptotic expressions for current and impedance. Results are compared with a numerical solution of the integral equation for the current and with results in literature. 相似文献
The breakdown processes of oil films under quasi-static loading have been investigated by using a newly developed steel-oil-mercury system. The relationship between the thickness and breakdown ratio of a hexadecane film is represented by a single master curve independently of the indentation speed, indentation load, and temperature. The master curve shows that the breakdown process of hexadecane includes two stages; one is the decrement of the thickness without breakdown and the other is the decrement of the thickness with a drastic progress of breakdown. By solving a small amount of fatty acid in hexadecane, the thickness increases and the breakdown ratio decreases noticeably; a multilayer residual film supporting normal load is formed between two metal surfaces. Experiments at different temperatures reveal a negative relationship between the temperature and thickness of residual film, which indicates that the residual film is organized by physical interaction rather than chemical interaction. At least under a lower concentration, the residual film appears to consist of not only fatty acid molecules but also hexadecane molecules. 相似文献
Instantaneous corrosion rates of naturally patinated copper of varying age (16 months, 138 and 145 years) have been determined during continuous rain events in the laboratory with electrochemical impedance spectroscopy using a two-electrode cell. The two-electrode cell was found to yield the same information in bulk rainwater as a conventional three-electrode cell.Relatively constant corrosion rates, between 0.2 and 0.6 μm/y, were determined for samples having a two-layer structure with an inner brownish layer of cuprous oxide and an outer greenish layer of basic copper salts (138, 145 years). Samples with cuprous oxide as the dominating phase of the patina (16 months) showed higher and somewhat increasing corrosion rates during a rain event (from 0.6 to 1.2 μm/y). During a continuous rain event, corrosion rates were found to be approximately 10 (brownish patina) and 25 times (greenish patina) lower than corresponding instantaneous runoff rates. The first flush phenomena of the runoff process, with an increased concentration during first flush and a relatively constant concentration during steady state, was indirectly seen as an increase in solution conductivity during the first rain volume followed by relative constant value. The contribution of the concentration in the first flush to the total annual runoff rate was significant for panels having a greenish layer (138, 145 years) whereas it was negligible for panels having a brownish layer (16 months). 相似文献