织构化涂层表面的黏附接触力学行为研究

目的 建立刚性微球与织构化涂层表面黏附接触数值分析模型,探究织构化涂层属性对微观接触副黏附力学性能的影响。方法 基于Hamaker求和法以及Lennard–Jones势能定律,考虑织构高度对接触体间距离分布的影响以及涂层、织构材料属性对接触体间黏附力的影响,建立织构化涂层表面黏附接触力学模型并验证所提模型。基于所提模型,研究不同Tabor数下织构形貌、密度、高度以及涂层厚度对接触系统黏附力学性能的影响。结果 在相同参数下,圆柱型织构黏附力最大,半椭球型织构次之,四棱锥型织构最小。织构密度从200μm^-2增加到4 000μm^-2时,最大黏附力随着织构密度的增加而增加,圆柱型织构增加约5～6倍,四棱锥型织构增加约1.5倍。随着织构高度从1ε_bs增加至30εbs,最大黏附力减小,四棱锥型织构减小最多,约为原来的1%,圆柱形织构减小最少,约为原来的90%。涂层厚度能够影响黏附力的大小,但影响规律与织构化涂层的Tabor数及织构高度相关。随着涂层厚度从1ε_bs增加至16ε_bs,大Tabo...     

Au-20Sn贵金属钎料箔材的制备及性能研究

采用多层复合及扩散合金化工艺制备Au-20Sn贵金属钎料箔材,研究箔材的化学成分、熔化特性、力学性能、物相组成、组织形貌和微区成分,并采用真空钎焊工艺对所制备钎料箔材的钎焊性能进行研究。结果表明,采用多层复合及扩散合金化工艺制备的Au-20Sn钎料箔材脆性明显改善,能够在室温下冷冲裁加工成特定尺寸的预成型焊片;钎料箔材的化学成分和杂质含量符合设计要求,显微组织由连续且均匀分布的(Au Sn)和(Au₅Sn)两相组成;钎料熔程仅为3.1℃,在铜基材上润湿性和铺展性良好,钎焊铜接头力学性能较好。     

超硬多层薄膜的研究现状及展望

由于超硬多层薄膜的性能随调制周期的变化而发生变化,在某一范围出现超硬等异常效应.其潜在的实际应用价值及理论意义,使其成为近年来人们研究的热点.本文综述了近年来国内外超硬多层薄膜的研究结果,介绍了其分类、主要性能特点以及制备工艺,并对超硬多层薄膜以后的发展趋势进行了展望.     

整体多层夹紧式高压容器应力测试与爆破试验研究

介绍了整体多层夹紧式高压容器的应力测试与爆破试验过程及结果,并通过理论分析说明应力测试与爆破试验结果是合理可靠的。     

粉末喷涂型材斑马纹的控制

研究分析静电粉末喷涂中斑马纹产生的原因以及影响因素,并有针对性地采取相应的解决措施,提高产品的外观质量。     

55 dtex/144 f阻燃涤纶DTY的生产工艺

采用磷含量为5 500μg/g的75 dtex/144 f阻燃涤纶POY为原料,在ATF-12型加弹机上生产55 dtex/144 f阻燃涤纶DTY,探讨了其假捻变形工艺。结果表明:选择加工速度400～600 m/min,拉伸掊数1.60～1.72,D/Y值1.70～1.75,热箱温度135～175℃,第二、三超喂率分别为2.5%,3.0%,生产正常,产品满卷率达86%以上,织物极限氧指数达32%,其他物理指标接近同规格的普通涤纶DTY。     

Chromaticity-tunable remote LuYAG: Ce phosphor-in-glass film on regular textured glass substrate for white light emitting diodes

All inorganic remote phosphor-in-glass film exhibits excellent properties in high power white light-emitting-diodes (WLEDs) thanks to their easy fabrication and thermal stability. Herein, fabrication of (Lu, Y)₃Al₅O₁₂: Ce³⁺ (LuYAG: Ce)phosphors embedded in borosilicate glass film by the conventional solid state reaction and spin coating technology has been reported. The introduction of Y³⁺ ions reduces the difference of relative growth rate along some directions in growth of LuYAG microparticles, yielding a finer grain with smooth edges. By adjusting the molar concentration of Y³⁺ ions in LuAG phosphor, a series of tunable broadband emission from green to yellow region is observed and maintains excellent thermal stability. Meanwhile, the decay curves of samples with different Y³⁺ are almost same. SEM images show that phosphor particles are homogenously distributed within the glass matrix and keep their original morphology, suggesting the phosphor-in-glass films were synthesized as expected. Finally, a simple WLEDs based on the films was constructed using the commercial blue chip. The correlated color temperature ranging from 4853K to 4627K and high color rendering index from 81.4–79.7 were obtained. Upon the different driving current, the chromaticity coordinates of as-fabricated film exhibit good light color stability. These results bring an inspiring insight to tune the luminescent performance for remote WLEDs.     

多晶硅太阳电池绒面和二次扩散吸杂工艺研究

对100mm×100mm p型多晶硅片,采用单晶的绒面腐蚀工艺以及二次扩散吸杂工艺后,电池的电性能普遍有所提高.光电转换效率在批量工业生产中达11%左右,最高达到12%.比常规工艺转换效率增加10%左右.电池片的扩散长度L_D有明显提高.     

基于多维社交关系嵌入的深层图神经网络推荐方法

社会化推荐系统通过用户的社会属性信息能缓解推荐系统中数据稀疏性和冷启动问题，从而提高推荐系统的精度。然而大多数社会化推荐方法主要针对单一的社交网络，或对多个社交网络进行线性叠加，使得用户社会属性难以充分参与计算，因而推荐的精度有限。针对该问题，提出一种多重网络嵌入的图形神经网络模型来实现复杂多维社交网络下的推荐，该模型构建了统一的方法来融合用户-物品、用户-用户等各种关系构成的多维复杂网络，通过注意力机制聚合不同类型的多邻居对节点生成作出贡献，并将多个图神经网络进行组合，从而构建了多维社交关系下的图神经网络推荐框架。这种方法通过拓扑结构直接反映推荐系统中实体及其相互间关系，直接在图上对相关信息进行不断更新计算，具有很强的归纳性，有效避免了传统推荐方法中信息利用不完全的问题。通过与相关的社会推荐算法进行比较，实验结果表明，所提方法在均方根误差（RMSE）和平均绝对误差（MAE）等推荐精度指标上有所改善，甚至在数据稀疏情况下也有良好的精度。     

弹丸在多层复合介质中的爆炸破坏效应研究

根据实验得到的运动弹丸在多层复合介质中不同深度爆炸时产生的弹坑形状、体积及破坏面积，对破坏效应进行了理论分析，建立了弹丸在多层复合介质中的爆炸破坏分区；考虑主要影响破坏效果因素条件下应用量纲分析方法，并结合实验数据得到了破坏参数与比炸深的无量纲关系式和关系曲线，由这些曲线能够方便地查找所需最佳破坏效果对应的比炸深，在相同条件下，该结果可推广到类似目标的爆炸破坏效应分析。