TEM Studies of High Temperature Corrosion Behaviour of TiAl Intermetallics with Surface Modifications

The oxidation/sulphidation behaviour of a Ti‐46.7Al‐1.9W‐0.5Si alloy with a TiAl₃ diffusion coating was studied in an environment of H₂/H₂S/H₂O at 850^oC. The kinetic results demonstrate that the TiAl₃ coating significantly increased the high temperature corrosion resistance of Ti‐46.7Al‐1.9W‐0.5Si. The SEM, EDX, XRD and TEM analysis reveals that the formation of an Al₂O₃ scale on the surface of the TiAl₃‐coated sample was responsible for the enhancement of the corroison resistance. The Ti‐46.7Al‐1.9W‐0.5Si alloy was also modified by Nb ion implantation. The Nb ion implanted and as received sampels were subjected to cyclic oxidation in an open air at 800^oC. The Nb ion implantation not only increased the oxidation resistance but also substantially improved the adhesion of scale to the substrate.     

Chemische Zusammensetzung und Mikrostruktur polymerabgeleiteter Gläser und Keramiken im System Si–C–O. Teil 2: Charakterisierung der Gefügeausbildung mittels hochauflösender Durchstrahlungselektronenmikroskopie und Feinbereichsbeugung

Chemical Composition and Microstructure of Polymer‐Derived Glasses and Ceramics in the Si–C–O System. Part 2: Characterization of microstructure formation by means of high‐resolution transmission electron microscopy and selected area diffraction Liquid or solid silicone resins represent the economically most interesting class of organic precursors for the pyrolytic production of glass and ceramics materials on silicon basis. As dense, dimensionally stable components can be cost‐effectively achieved by admixing reactive filler powders, chemical composition and microstructure development of the polymer‐derived residues must be exactly known during thermal decomposition. Thus, in the present work, glasses and ceramics produced by pyrolysis of the model precursor polymethylsiloxane at temperatures from 525 to 1550 °C are investigated. In part 1, by means of analytical electron microscopy, the bonding state of silicon was determined on a nanometre scale and the phase separation of the metastable Si–C–O matrix into SiO₂, C and SiC was proved. The in‐situ crystallization could be considerably accelerated by adding fine‐grained powder of inert fillers, such as Al₂O₃ or SiC, which permits effective process control. In part 2, the microstructure is characterized by high‐resolution transmission electron microscopy and selected area diffraction. Turbostratic carbon and cubic β‐SiC precipitate as crystallization products. Theses phases are embedded in an amorphous matrix. Inert fillers reduce the crystallization temperature by several hundred °C. In this case, the polymer‐derived Si–C–O material acts as a binding agent between the powder particles. Reaction layer formation does not occur. On the investigated pyrolysis conditions, no crystallization of SiO₂ was observed.     

A novel way to treat refractory waste: Sonication followed by wet oxidation (SONIWO)

The effectiveness of the hybrid system sonication followed by wet oxidation (SONIWO) to treat otherwise refractory waste has been demonstrated. In such a hybrid system homogeneous CuSO₄ catalyst was found to be very efficient.     

测定钠中杂质的手动阻塞计的研究

文章介绍了测定钠中杂质浓度的手动阻塞计的原理、装置和实验结果。为了减少测量误差,我们研究了影响准确测定阻塞温度的因素,并且找到了减少测量误差的办法。在同样的杂质饱和温度下,该阻塞计测得的高、低阻塞温度所对应的杂质浓度差是很接近的。对氧其差值为1.03ppm;对氢为0.0763ppm。     

Poly(butylene terephthalate)–clay nanocomposites prepared by melt intercalation: morphology and thermomechanical properties

Nanocomposites based on poly(butylene terephthalate) (PBT) and an organoclay (Cloisite 30B) were prepared by melt blending using a twin‐screw extruder. Two kinds of PBTs, ie PBT‐A and PBT‐B, with different inherent viscosities (η_inh), were used for this study (η_inh of PBT‐A and PBT‐B were 0.74 and 1.48, respectively). Dispersion of the clay layers in the PBT nanocomposites was characterized by using X‐ray diffraction (XRD) and transmission electron microscopy (TEM). Tensile and dynamic mechanical properties and non‐isothermal crystallization temperatures of the nanocomposites were also examined. Nanocomposites based on the higher‐viscosity PBT (PBT‐B) showed a higher degree of exfoliation of the clay and a higher reinforcing effect when compared to the composites based on the lower‐viscosity PBT (PBT‐A). The clay nanolayers dispersed in PBT matrices lead to increases in the non‐isothermal crystallization temperatures of the PBTs, with such increases being more significant for the PBT‐B nanocomposites than for the PBT‐A nanoocomposites. Copyright © 2004 Society of Chemical Industry     

Influence of ethyl methacrylate content on the volume‐phase transition of temperature‐sensitive poly[(N‐isopropylacrylamide)‐co‐(ethyl methacrylate)] microgels

A novel series of temperature‐sensitive poly[(N‐isopropylacrylamide)‐co‐(ethyl methacrylate)] (p(NIPAM‐co‐EMA)) microgels was prepared by the surfactant‐free radical polymerization of N‐isopropylacrylamide (NIPAM) with ethyl methacrylate (EMA). The shape, size dispersity and volume‐phase transition behavior of the microgels were investigated by transmission electron microscopy (TEM), ultraviolet–visible (UV–Vis) spectroscopy, dynamic light scattering (DLS) and differential scanning calorimetry (DSC). The transmission electron micrographs and DLS results showed that microgels with narrow distributions were prepared. It was shown from UV–Vis, DLS and DSC measurements that the volume‐phase transition temperature (VPTT) of the p(NIPAM‐co‐EMA) microgels decreased with increasing incorporation of EMA, but the temperature‐sensitivity was impaired when more EMA was incorporated, causing the volume‐phase transition of the microgels to become more continuous. It is noteworthy that incorporation of moderate amounts of EMA could not only lower the VPTT but also enhance the temperature‐sensitivity of the microgels. The reason for this phenomenon could be attributed to changes in the complicated interactions between the various molecules. Copyright © 2004 Society of Chemical Industry     

Facile modifications of polyimide via chloromethylation: II. Synthesis and characterization of thermocurable transparent polyimide having methylene acrylate side groups

From chloromethylated polyimide, a useful starting material for modification of aromatic polyimides, a thermocurable transparent polyimide having acrylate side groups was prepared. In the presence of 1,8‐diazabicyclo[5,4,0]undec‐7‐ene, chloromethylated polyimide was esterified with acrylic acid to synthesize poly(imide methylene acrylate). The polymer was soluble in organic solvent, which makes it possible to prepare a planar film by spin coating. The polymer film became insoluble after thermal treatment at 230 °C for 30 min. Optical transparency of the film at 400 nm (for 1 µm thickness) was higher than 98 % and not affected by further heating at 230 °C for 250 min. Adhesion properties measured by the ASTM D3359‐B method ranged from 4B to 5B. Preliminary results of planarization testing showed a high degree of planarization (DOP) value (>0.53). These properties demonstrate that poly(imide methylene acrylate) could be utilized as a thermocurable transparent material in fabricating display devices such as TFT‐LCD. Copyright © 2004 Society of Chemical Industry     

High char‐yielding poly[acrylonitrile‐co‐(itaconic acid)‐co‐(methyl acrylate)]: synthesis and properties

Polyacrylonitrile terpolymers of various compositions consisting of acrylonitrile (AN), itaconic acid (IA) and methyl acrylate (MA) were synthesized by solution polymerization in dimethylsulfoxide. Increase in concentration of either IA or MA retarded the overall polymerization rate and the polymer molecular weight. The system consisting of AN + MA and varying IA concentration was more prone to retardation in comparison with the system composed of AN + IA with variable MA concentration. The retardation factors were quantified. Minor quantities of MA boost the reactivity of IA in the terpolymer system. The terpolymer was richer in MA vis‐à‐vis the feed. The thermal characteristics of the terpolymer were examined as a function of its composition. In contrast to the copolymer of AN and IA requiring 1–1.5 mol% IA, the terpolymer required an IA content of approximately 2.5 mol% for optimum thermal stability. The polymer with 90 mol% AN, 2.5 mol% IA and 7.5 mol% MA exhibited reasonably good char‐forming characteristics and thermal stability. The overall crystallinity and crystallite size of the polymers were found to decrease on incorporation of the comonomers. The ‘aromatization index’ of the copolymer increased with the temperature of pyrolysis through re‐organization of the tetrahydropyridine ladder structure. Copyright © 2005 Society of Chemical Industry     

Low temperature synthesis of aluminium titanate by an aqueous sol-gel route

Formation of aluminium titanate (AT) has been achieved at low temperature through sol-gel process using boehmite and titanium hydroxide as precursors by controlling the particle size at nanoscale followed by in-situ peptisation. The formations of AT phase, particle size distributions, sintering and thermal expansion characteristics, and microstructural features have been reported. DTA and XRD analysis have been performed to confirm the formation of AT. A 94% relative density was obtained for aluminium titanate sintered at 1550 °C with controlled grain size in the range of 2-3 μm.     

Ozonation of CI Reactive Black 5 using rotating packed bed and stirred tank reactor

This study investigates the ozonation of CI Reactive Black 5 (RB5) by using the rotating packed bed (RPB) and completely stirred tank reactor (CSTR) as ozone contactors. The RPB, which provides high gravitational force by adjusting the rotational speed, was employed as a novel ozone contactor. The same ozone dosage was separately introduced into either the RPB or the CSTR for the investigation, while the experimental solution was continuously circulated within the apparatus consisting of the RPB and CSTR. The decolorization and mineralization efficiencies of RB5 in the course of ozonation are compared for these two methods. Moreover, the dissolved and off‐gas ozone concentrations were simultaneously monitored for the further analysis. As a result, the ozone mass transfer rate per unit volume of the RPB was significantly higher because of its higher mass transfer coefficient and gas–liquid concentration driving force. Furthermore, ozonation kinetics was found to be independent of the gravitational magnitude of an ozone gas–liquid contactor. Therefore, the results suggest employing RPBs as ozone‐contacting devices with the advantage of volume reduction. The experimental results, which can be used for further modeling of the ozonation process in the RPB, also show the requirement of correct design for the RPB. Consequently, the present study is useful for the understanding of practical application of RPBs. Copyright © 2004 Society of Chemical Industry