磁控溅射制备纳米Ni-Ti薄膜工艺研究

为了得到高质量的纳米薄膜，对直流磁控溅射法制备Ni-Ti薄膜工艺进行了研究。采用单晶硅和玻璃两种基体材料，并在不同的基体温度、晶化温度、溅射功率等条件下制备薄膜。之后对薄膜进行了XRD，SEM分析。分析结果表明：薄膜成分、厚度、表面形貌、致密度与溅射功率、基体温度、晶化温度、基体材料密切相关。并根据实验结果给出优化的纳米Ni-Ti薄膜制备工艺。     

两种钢材COD及J积分值的实验研究

采用18CrNiWA和40Cr钢，用3种不同强度材料的试件，进行了一系列3点弯曲试件深裂纹和浅裂纹的OOD及J积分值试验，再次得出了浅裂纹的ODD和J积分值大于深裂纹值的结果．文中用滑移线场理论进行分析。得出浅裂纹的静水应力值要小于深裂纹值，从而造成浅裂纹的断裂韧度值大于深裂纹值的结论．并以双参数断裂理论分析得出a／W值的减小导致了T应力的减小，并由此导致裂纹尖端塑性区的增大．即浅裂纹塑性约束的减小，造成了浅裂纹的δi及Ji值明显高于深裂纹值的结果．文中还指出了其重要的工程实际意义．     

低拉应力下12Cr1MoV钢中P原子的晶界非平衡偏聚

对低应力作用下12Cr1MoV钢中磷原子的晶界偏聚现象进行了俄歇能谱实验研究和动力学分析．实验获得了在30MPa拉应力作用下，磷原子在晶界处发生的非平衡晶界偏聚，临界时间是1h．分析表明，低拉应力极大地提高了磷-空位复合体在钢中的扩散速率，低拉应力引起的晶界变形对磷-空位复合体具有强烈的吸引作用．通过动力学计算给出了磷-空位复合体偏聚阶段扩散系数Dc和磷原子反偏聚扩散系数Di随时间变化的表达式．     

Nd-Fe-B薄膜的磁控溅射法制备与组织结构

对直流磁控溅射法制备Nd-Fe-B薄膜工艺进行了研究.在不同的溅射功率、溅射气压、溅射时间等条件下制备薄膜,并对薄膜进行了AFM、XRD分析.结果表明,Nd-Fe-B薄膜的沉积速率、表面形貌及相结构与溅射功率、溅射气压、溅射时间密切相关.薄膜的沉积速率随磁控溅射功率的增加而增加,薄膜表面晶粒尺寸和表面粗糙度随溅射功率增加而增大.沉积速率随溅射气压的升高先增大后减小.低功率溅射时,薄膜中出现α-Fe、Nd2Fe14B相相对较少,随溅射功率增加,α-Fe相消失,Nd2Fe14B相增多.综合考虑各种因素,最佳溅射功率为100～130 W.     

变温条件下石墨形态对缸套铸铁磨损性能的影响

为了研究缸套铸铁材料石墨形态对其磨损过程的影响,选取了灰铸铁、蠕墨铸铁和球墨铸铁3种具有不同石墨形态的铸铁材料为研究对象,分别在不同温度下对其进行了干摩擦磨损实验。结果表明:灰铸铁的摩擦系数及磨损量随温度的上升而上升,而蠕墨铸铁及球墨铸铁随温度的上升呈现先上升后下降的变化趋势;常温下灰铸铁的摩擦系数及磨损量最大,耐磨性能最差;高温时灰铸铁的摩擦系数及磨损量仍然最大,蠕墨铸铁的摩擦系数大于球墨铸铁,但磨损量最小,耐磨性能最优。     

Ti6Al4V合金表面热浸镀Ti-Al镀层相组成

采用热浸镀方法在Ti6Al4V合金表面制备Ti-Al镀层,并在1100 ℃高温下进行热扩散处理。结果表明,TC4合金热浸镀铝后在1100 ℃保温,形成了表面氧化层、过渡层及基体,表面氧化层和过渡层厚度随扩散时间延长而增加,表面氧化层主要由Al₂O₃和TiO₂构成,过渡层主要相为TiAl₃、Ti₂Al₅和Ti₁₉Al₆金属间化合物。     

Mechanical and corrosion resistant properties of martensitic stainless steel plasma nitrocarburized with rare earths addition

In order to improve surface hardness and corrosion resistant property of 17-4PH martensitic stainless steel, the steel was plasma nitrocarburized at 560 °C for 2-24 h in a gas mixture of nitrogen, hydrogen and ethanol with rare earths (RE) addition. The experimental results showed that the modified layer was characterized by a compound layer containing two distinct zones (i.e. out ’dark zone’ and inner ’white zone’). The inner ’white zone’ was almost a precipitation free zone and had high hardness as well as good corrosion resistance. Anodic polarization test results showed that the specimens plasma nitrocarburized with RE addition had good corrosion resistance resulted mainly from their higher corrosion potentials, lower corrosion current densities and larger passive regions as compared with those of the untreated one.     

马氏体不锈钢低温等离子体稀土氮碳共渗研究

将17-4PH马氏体不锈钢在430℃进行了有无稀土添加的等离子体氮碳共渗处理,其利用OM、XRD、显微硬度计和摩擦磨损试验机研究了共渗动力学、渗层组织结构、硬度以及摩擦磨损行为.结果表明,添加稀土使共渗层组织更加致密,渗层增厚;添加稀土不改变渗层的表面相结构组成,即主要由含氮碳膨胀马氏体(α 'N)、γ '-Fe4N和CrN相组成;添加稀土可使氮碳共渗层厚度增加46％以上,渗层显微硬度可提高100 HV0.1左右,同时明显提高耐磨性能.     

强烈淬火对20CrMnTi钢组织与性能的影响

对20CrMnTi钢进行了强烈淬火试验,研究了强烈淬火工艺对20CrMnTi钢试样的组织和力学性能的影响.试验结果表明,分别用CaCl2水溶液、液氮淬火和CaCl2水溶液+液氮分级淬火后,试样的组织与力学性能不尽相同,在CaCl2水溶液×1 s+液氮×4 s分级淬火后效果较好,其抗拉强度达1 521 MPa,冲击韧度达1 392.66 kJ/m2,较传统的渗碳淬火处理后有较大的提高.