The phase transformation of R2O-CaO-SiO2-F system glass-ceramics with various additions of K2O and F was investigated by DTA, XRD, SEM and other techniques. The crystallization and the microstructure of the obtained glass-ceramics were also evaluated. The phase separation occurred in CN1 specimen after being quenched in water, but phase separation did not appear in other quenched specimens with the content of K2O and F increasing obviously, showing K2O and F modified the structure of the glass-forming melts... 相似文献
2.
3.
R2O-CaO-SiO2-F系统微晶玻璃析晶过程较为复杂,能析出多种晶相,导致性能发生改变。为获得预期的性能,必须对母体玻璃结构和析晶过程进行控制。而Al2O3质量分数的改变对母体玻璃结构和析晶会产生深远的影响,因此本文采用XRD、SEM、IR等测试分析方法,研究Al2O3对微晶玻璃结构和析晶过程的影响。结果表明:铝离子以四配位参与到玻璃的硅氧网络结构中,随着Al2O3引入量的增大,母体玻璃的网络结构得到加强。当氧化铝质量分数为2.5%时,微晶玻璃晶化后析出氟化钙和a-硅碱钙石晶相,当氧化铝质量分数增大至3.5%和4%时,微晶玻璃析出的晶相转变为氟化钙和硬硅钙石,氧化铝质量分数继续升高至4.5%时,微晶玻璃析出的晶相转变为氟化钙、硬硅钙石和a-硅碱钙石晶相。 相似文献
4.
R2O-CaO-SiO2-F系统微晶玻璃的析晶过程较为复杂,析出晶体种类繁多。为得到预期的晶相,获得最佳性能,需要对整个析晶过程进行合理控制。因此采用DTA、XRD、SEM等测试分析方法,研究K2O引入量对R2O-CaO-SiO2-F系统微晶玻璃的析晶温度、主晶相、晶体含量以及微观形貌的影响。研究结果表明:随着K2O引入量的增加,玻璃转变点温度降低,而最大析晶峰温度升高。当K2O引入量为质量分数5%左右时,微晶玻璃的主晶相为颗粒状的氟化钙和柱状的硬硅钙石,晶体含量为15%。当氧化钾质量由6%增加到8%时,微晶玻璃主要析出放射状a-硅碱钙石,次晶相为少量的氟化钙,晶体含量增大到40%。 相似文献
1