Mechanical properties and microstructure of Portland cement concrete prepared with coral reef sand

The feasibility of using coral reef sand (CRS) in Portland cement concrete is investigated by testing the mechanical property and microstructure of concrete. The composition, structure and properties of the CRS are analyzed. Mechanical properties and microstructure of concrete with CRS are studied and compared to concrete with natural river sand. The relationship between the microstructure and performance of CRS concrete is established. The CRS has a porous surface with high water intake capacity, which contributes to the mechanical properties of concrete. The interfacial transition zone between the cement paste and CRS is densified compared to normal concrete with river sand. Hydration products form in the pore space of CRS and interlock with the matrix of cement paste, which increases the strength. The total porosity of concrete prepared with CRS is higher than that with natural sand. The main difference in pore size distribution is the fraction of fine pores in the range of 100 nm.     

混凝土用石灰石粉与聚羧酸减水剂适配性研究

<正>0引言近年来,由于粤东,赣南地区优质粉煤灰价格高,所以选择粉煤灰与石灰石粉搭配的混合料,或使用石灰石粉全额取代粉煤灰,而很多外加剂厂商提供的聚羧酸减水剂还使用粉煤灰时的配方,坍落度损失过大,尤其是泵送混凝土。国内已有很多专家研究石灰石粉对混凝土各性能的影响。石灰石粉比表面积控制在一定范围[1],能发挥填充效应,强度增加,但超出范围会带来不利影响,对粉煤灰的取代亦是要控制在一定范围。本     

超疏水性气凝胶粉体涂层的制备与性能

为提高建筑物表层的抗蚀性,将经三甲基氯硅烷(TMCS)改性过的疏水性SiO2气凝胶粉体溶于丙酮溶剂中,制成表面防护涂层。研究了不同温度对气凝胶疏水性能的影响,以及超疏水性气凝胶粉体涂层制备条件、涂刷于混凝土表层时对水的耐久性能;利用红外光谱和扫描电镜对其化学基团和微观形貌进行分析。实验结果表明,250℃以下时,气凝胶为超疏水性,之后随温度升高大幅度下降直到完全消失;涂刷次数与气凝胶在分散体系中的质量有关;冲刷时,涂层先由超疏水性变为疏水性,之后长时间保持不变,水浸泡不改变涂层的超疏水性。     

偏高岭土对预制混凝土路面材料耐久性能的影响

预制装配式混凝土路面因其养护时间短、维修方便、性能优异而发展迅速,但高温导致的膨胀应力造成混凝土内部裂纹的发生扩展,有害孔含量增加,造成预制混凝土耐久性能降低。本文通过加入偏高岭土作为辅助胶凝材料改善预制混凝土路面材料耐久性能,研究了不同掺量（0%、3%、6%、9%、12%）的偏高岭土对其力学和耐久性能的影响规律。研究表明,偏高岭土可以显著提高混凝土的强度、抗冻性和抗渗性能。     

聚合多元醇胺的制备及其助磨性能研究

本文以1,4-丁二醇双缩水甘油醚和二乙醇胺为原料合成了一种高分散、高早强活化功能的聚合多元醇胺(PA),利用FT-IR、1 H-NMR以及GPC进行了分析与表征,通过比表面积、粒径分布和中值粒径(D50)研究了PA在水泥粉磨中的助磨性能.结果表明PA具有显著的助磨和增强性能,当PA添加量为0.02wt％时,3～ 32 μm颗粒含量从53.88％提高到59.01％,D50从1.14降低到1.02,水泥3d抗压强度提高3.37 MPa,28 d抗压强度提高3.69MPa,且其助磨和增强明显效果优于三乙醇胺,因而具有广阔的应用前景.     

陶瓷砖胶粘剂放射性测量不确定度分析研究

由于制备陶瓷砖胶粘剂的优质天然石英砂资源日益枯竭,采用固废材料等更为廉价的骨料替代,由此可能带来放射性核素限量的增高,需进行放射性核素限量检测评估。为提高检测的准确性,对检测仪器、称量设备等引入的不确定度因素进行研究,得出内、外照射指数的测量不确定度(扩展因子k=1)分别为6.75%和7.25%,均满足GB 6566-2010中≤20%的要求。     

偏高岭土对预制混凝土路面材料耐久性能的影响

预制装配式混凝土路面因其养护时间短、维修方便、性能优异而发展迅速，但高温导致的膨胀应力造成混凝土内部裂纹的发生扩展，有害孔含量增加，造成预制混凝土耐久性能降低。本文通过加入偏高岭土作为辅助胶凝材料改善预制混凝土路面材料耐久性能，研究了不同掺量（0%、3%、6%、9%、12%）的偏高岭土对其力学和耐久性能的影响规律。研究表明，偏高岭土可以显著提高混凝土的强度、抗冻性和抗渗性能。     

偏高岭土对预制混凝土路面材料耐久性能影响的微观分析*

预制装配式混凝土路面因其养护时间短、维修方便、性能优异而发展迅速,但高温导致的膨胀应力造成混凝土内部裂纹的发生扩展,有害孔含量增加,造成预制混凝土耐久性能降低。而以偏高岭土作为辅助胶凝材料可显著改善预制混凝土路面材料的耐久性能。本文通过XRD和扫描电子显微镜研究了不同掺量（0%、9%）偏高岭土的净浆和混凝土的物相组成和微观形貌差异,对其改性机理进行了探讨。研究表明,偏高岭土在水化过程中能发挥火山灰活性和填充作用,提高水化产物的密实度,消除高温导致的微裂纹,改善界面过渡区结构,降低混凝土孔隙率。     

减水剂在粉煤灰水泥浆体中的吸附及其流变性能影响

针对减水剂—粉煤灰体系的相互作用与分散特性开展研究,通过采用不同性质的粉煤灰和减水剂,研究了减水剂在水泥等胶凝颗粒上的吸附量、zeta电位等界面化学性质,并且测定了不同系统的屈服应力和塑性黏度等流变特性,建立了减水剂吸附量、zeta电位和水泥浆体流变参数之间的关系。试验结果表明:高效减水剂在粉煤灰颗粒表面的吸附规律与水泥颗粒完全不同。由于粉煤灰颗粒较为光滑并且表面动电位为负值,因此对高效减水剂的吸附能力较弱,其吸附能力随粉煤灰密度和颗粒大小差异较大。对于粉煤灰水泥浆体,其流变参数变化与减水剂吸附量关系较小,主要受粉煤灰技术性质的影响。由于粉煤灰表面动电位绝对值远高于掺入减水剂的硅酸盐水泥颗粒表面动电位绝对值,因此其自身具有颗粒分散趋势,及粉煤灰颗粒自身具有增加水泥浆体流动能力的能力。硅酸盐水泥和粉煤灰颗粒吸附萘系减水剂的能力大于吸附聚羧酸盐减水剂的能力。