Effects of CaO and Na<Subscript>2</Subscript>CO<Subscript>3</Subscript> on the reduction of high silicon iron ores

The effects of CaO and Na₂CO₃ on the reduction of high silicon iron ores at 1 250 °C were studied. The experimental results showed that the metallization rate was significantly hindered by the addition of CaO and Na₂CO₃, particularly at the early stage of roasting, compared to the rate without additives. In the absence of additives, iron oxides were quickly reduced to metallic iron, and fayalite was difficult to form. When CaO and Na₂CO₃ were added, the low reducible iron-containing silicate compounds formed and melted, subsequently retarding the metallization process. The inhibition of Na₂CO₃ was more noticeable than that of CaO, and higher Na₂CO₃ doses resulted in stronger inhibition of the increased metallization rate. However, when Na₂CO₃ was added prior to CaO, the liquid phase formed, which facilitated the growth of the metallic phase. To reinforce the separation of the metallic phase and slag, an appropriate amount of liquid phase generated during the reduction is necessary. It was shown that when 10% CaO and 10% Na₂CO₃ were added, a high metallization rate and larger metallic iron particles were obtained, thus further decreasing the required Na₂CO₃ dosage.     

齐大山铁尾矿工艺矿物学研究

齐大山铁尾矿的提铁研究是国家高技术研究发展计划（863计划）铁尾矿高效提铁技术研究子项的一部分。为圆满完成深度还原给料铁品位≥30%、铁回收率≥80%,还原铁粉铁品位≥90%的任务目标,对齐大山铁尾矿开展了工艺矿物学研究。结果表明：试样中的铁矿物主要以贫连生体的形式存在,且在-0.038 mm粒级有明显的富集现象,主要铁矿物为赤褐铁矿和硅酸铁,磁铁矿次之,这些铁矿物粒度微细,平均粒度分别为0.022、0.009、0.011 mm,单体解离度分别为61.78%、42.86%、45.64%,铁矿物与脉石矿物共生关系密切;基于上述工艺矿物学特征,推荐了磨矿-弱磁选-强磁选的预富集工艺流程。     

中国钢铁冶金尘泥资源化利用现状及发展方向

 钢铁冶金尘泥的高效综合利用一直是政府、研究机构和企业关注的焦点问题。结合钢铁冶金尘泥来源、物相组成和粒度特性,简述近年来钢铁冶金尘泥资源化综合利用技术的研究现状和应用情况,其发展方向应侧重于多种工艺技术的联合,重点向低成本、精细化、清洁化和整体化利用方向发展。     

白云鄂博铁矿石工艺矿物学研究

为了更好地开发利用白云鄂博铁矿石资源,对白云鄂博铁矿石进行了工艺矿物学研究。结果表明：①矿石中的有用矿物主要为磁铁矿、赤铁矿、稀土矿物,脉石矿物主要有萤石、石英、钠辉石、方解石、长石等。②矿石中的主要铁矿物为磁铁矿,以碎屑状及角砾状为主,占磁铁矿总量的70%以上,与钶铁矿、磷灰石、独居石、重晶石等紧密共生,偶见粗粒块状磁铁矿集合体;矿石中的赤铁矿多紧密镶嵌在碎屑状及角砾状磁铁矿中构成铁矿物集合体。③独居石是矿石中分布最广的稀土矿物,呈粒状,与周边其他矿物紧密共生、镶嵌关系复杂。④矿石中的脉石矿物均呈不规则状或他形粒状,脉石矿物间以及脉石矿物与有用矿物间嵌布关系均非常密切,萤石是分布最广的脉石矿物,是细小稀土矿物颗粒的包裹矿物之一。⑤矿石中铁矿物的嵌布粒度均非常细小,磁铁矿较赤铁矿略粗,嵌布粒度大于10 μm的赤铁矿、磁铁矿分别仅占40%和54%。⑥由于矿石中各矿物的嵌布关系复杂,嵌布粒度微细,单体解离困难,因此,宜采用深度还原工艺使微细粒铁矿物聚集长大后再进行回收。     

高磷鲕状赤铁矿还原物料与刚玉/莫来石砖的反应研究

在还原温度为1200 ℃条件下,实验研究了高磷鲕状赤铁矿还原物料与刚玉/莫来石砖的反应及反应对砖侵蚀的影响.还原物料由高磷(鲕)状赤铁矿、烟煤、CaO和Na2CO3组成,其质量比为1∶0.15∶0.15∶0.03.结果表明,还原物料与刚玉砖反应生成大量钙黄长石及少量钙长石,物料中Fe、Na、Mg离子向反应界面迁移,使钙黄长石产物层熔点降低、抗侵蚀性能下降.还原物料与莫来石砖反应形成密实的钙长石产物层,阻碍Fe、Na、Mg离子向反应界面迁移.对于在高温状态下还原高磷鲕状赤铁矿还原物料,莫来石砖具有比刚玉砖更好的抗侵蚀性能.     

不同地区水泥及河砂对瓷砖胶强度的影响

研究了水泥及河砂对瓷砖胶拉伸粘结强度的影响，用不同地区的水泥、河砂配制相同配方的瓷砖胶。结果表明：不同地区的材料配制的瓷砖胶拉伸粘结强度差异较大；这种差异主要是由水泥引起的；河砂的改变对瓷砖胶的影响不明显。     

抑尘剂对水泥基瓷砖胶粉尘散发性及力学性能的影响研究

分析对比了抑尘剂种类、黏度、掺量对水泥基瓷砖胶粉尘散发性及力学性能的影响规律。结果表明:抑尘剂在较低黏度下能够更好抑制瓷砖胶粉尘的散发,能够更好地保持瓷砖胶的力学性能;随着抑尘剂掺量增加,抑制粉尘散发越强,但超过一定量后,瓷砖胶的力学性能将受到较大影响,抑尘剂最佳掺量为0.4%~0.6%。     

矿物掺合料对瓷砖胶浸水性能的影响

为提高瓷砖胶的浸水性能，本文研究了矿渣粉、偏高岭土两种矿物掺合料单掺与复掺对瓷砖胶浸水后拉伸粘接强度、吸水量及粘接层浸湿面积的影响规律，揭示了矿物掺合料在瓷砖胶中的作用机制。研究结果表明：当矿渣粉或偏高岭土单掺时，随着矿物掺合料掺量的增加，瓷砖胶浸水后的拉伸粘接强度逐渐增大，且偏高岭土对瓷砖胶浸水后的拉伸粘接强度的提升作用要优于矿渣粉。矿渣粉、偏高岭土单掺与复掺均显著提高了瓷砖胶浸水后的拉伸粘接强度，其中矿渣粉与偏高岭土以质量比1∶1（质量分数为6%）复掺时，瓷砖胶浸水后粘接强度达到最大值，为1.65 MPa。矿物掺合料单掺或复掺均可降低瓷砖胶的吸水量与粘接层浸湿面积，减缓水向瓷砖胶内部的渗透，其中复掺比单掺更有利于降低瓷砖胶的吸水量，而对粘接层浸湿面积的影响则取决于复掺时偏高岭土的掺量。物相及显微结构分析发现，掺入矿渣粉与偏高岭土后，阻碍了片状、板状羟钙石在骨料颗粒表面以及瓷砖-瓷砖胶界面的生成与结晶，形成更多C—S—H水化产物与聚合物膜复合结构层，使过渡界面的粘接结构更加密实，从而导致瓷砖胶浸水性能提高。     

S95与S105矿渣粉对低碳柔性水泥基瓷砖胶性能的影响

以S95、S105矿渣粉分别取代部分水泥，研究其对低碳柔性水泥基瓷砖胶施工性能、力学性能及收缩性能的影响。结果表明：S105矿渣粉可提高柔性瓷砖胶的抗滑移性能与湿密度；S95矿渣粉在取代率≥20%时使得柔性瓷砖胶的抗滑移性能下降、终凝时间延长。S105矿渣粉可显著提高柔性瓷砖胶的7 d与28 d抗压、抗折强度；S95矿渣粉对28 d抗压、抗折强度有一定程度的提高。S95、S105矿渣粉均可显著提高柔性瓷砖胶的浸水后、冻融循环后拉伸粘结强度，其中S105矿渣粉的作用效果要优于S95矿渣粉。S105矿渣粉在取代率≤30%时可降低柔性瓷砖胶的28 d收缩率；S95矿渣粉在取代率≤20%时对柔性瓷砖胶的28 d收缩率的影响不显著。