80钢盘条拉拔断裂原因分析

用扫描电镜、金相显微镜观察分析了80钢盘条拉拔断裂的断口，并对盘条进行了理化检验分析。结果表明，盘条组织中较多的网状二次渗碳体是盘条在拉拔过程中脆断的主要原因。     

浅谈日本胶合板热压机

浅谈日本胶合板热压机从日本进口的胶合板生产设备中，热压机、装卸板机具有结构设计合理、动作可靠、故障率低等优点。下面仅就我厂引进日本生产的热压机谈几点看法。１机架部分：该机机架采用焊接式整体结构，用厚１２ｍｍ的普通钢板在上下横梁处呈蜂窝状焊接。安装油缸...     

铈对中铝耐热铸铁抗氧化性能的影响

采用氧化增重法测定了含Ce中铝耐热铸铁在850℃时氧化动力学曲线，用SEM，X－ray对氧化膜表面的形貌，结构及氧化层－基体界面进行了观察分析，结果表明：Ce改变了中铝耐热铸铁氧化膜的结构和组成，提高了中铝耐热铸铁的抗氧化性能。     

几何因素与摩擦耦合对高纯铝箔剪切织构的影响

采用取向分布函数 (ODF)研究了轧制几何因素、轧制摩擦条件对高纯铝箔轧制织构的影响。结果显示 ,如果轧制摩擦因数大 ,当处于均匀变形几何条件 1相似文献   

剪切变形方向特征对高纯铝箔轧制织构的影响

运用取向分布函数(ODF)研究了每个轧制道次的剪切变形特征对高纯铝箔轧制织构的影响.提出用中性角的相对大小来量化轧制剪切变形作用方向改变的位置,运用Taylor晶体塑性变形理论模拟计算了中性角的相对大小对轧制织构演变的影响.实测与模拟的轧制织构特征表明:中性角靠近轧制变形区的中心位置有利于形成{001}<110>剪切织构,从而证实了除剪切变形的程度外,剪切变形方向改变的位置也是影响高纯铝箔轧制织构的重要因素.     

Corrosion resistance of cerium conversion film electrodeposited on Mg-Gd-Y-Zr magnesium alloy

The cerium conversion film was applied to improving the corrosion resistance of Mg-Gd-Y-Zr magnesium alloy. The film was electrodeposited on the surface of the Mg-RE alloy in cerium nitrate solution. The compositions and morphologies were analyzed by X-ray diffraction(XRD), scanning election microscopy (SEM). The corrosion behaviors of the film were investigated electrochemical impedance spectroscopy (EIS), potentiodynamic polarization tests and immersion tests. The results show that the optimum parameters for electrochemical deposition are as follows: pH 10.0, time 30 min, 50 mmol/L Na₂CO₃ and temperature 25 °C by the designed experiments according to the orthogonal table L(9, 3⁴). The corrosion protection efficiency is dependent on the deposition parameters. The cerium conversion film shows better corrosion protection behavior than chromate conversion film on Mg-Gd-Y-Zr magnesium alloy. Foundation item: Project (5133001E) supported by the Major State Basic Research and Development Program of China     

微量Zr对Al-5.8Cu-0.3Mn合金焊接接头组织与性能的影响

采用4047焊丝对Al-5．8Cu-0．3Mn铝合金进行熔化极惰性气体保护焊，利用金相显微镜、透射电镜、显微硬度等检测分析手段研究了Zr对Al-5．8Cu-0．3Mn母材及焊接接头的力学性能和显微组织的影响。结果表明，Al-5．8Cu-0．3Mn合金中添加适量Zr元素可使母材强度提高30MPa，焊接接头强度提高50MPa，同时，细化了母材的再结晶组织和焊缝组织。焊接接头的强度低于母材强度，焊缝区是合金的薄弱处，热影响区强度降低是θ‘相粒子受热粗化所致。     

Effect of Zr content on quench sensitivity of AlZnMgCu alloys

The effect of Zr content on quench sensitivity of AlZnMgCu alloys was investigated by mechanical properties testing and microstructure observations. The results show that with the increase of Zr the quench sensitivity relative to hardness and strength increases, while that relative to elongation decreases. From hardness and strength viewpoints, the low quench sensitivity is observed for the Zr-free and 0.05% Zr-containing alloys, which is quite quench sensitive from the ductility viewpoint. The largest quench sensitivity relative to hardness and strength is observed for 0.1% Zr-containing alloy, this is mainly due to large amount of high angle grain boundaries and incoherent Al3Zr dispersoids caused by recrystallization, which may efficiently promote heterogeneous precipitation during air quenching. More than 0.05% Zr can significantly decrease the quench sensitivity relative to ductility, which can be primarily attributed to recrystallization inhibiting and grain refining effects of Zr.     

Mechanism of strengthening of cube texture for high purity aluminum foils by additional-annealing

1　INTRODUCTIONHighpurityaluminumfoilsareusedastheanodematerialofhighvoltageelectrolyticcapacitorswhichneedstrongcubetexture { 0 0 1}〈10 0〉forlargeeffec tivesurfacefromchanneletching[1] .Becauseofitstechnicalimportance ,alotofeffortshavebeenmadetodevelopstrongcubetextureinhigh purityalu minumfoils[2 8] .Itwasfoundthatthecubetextureinthefoilscanbestrengthenedviaanannealingpro cessfollowedbyalowcoldrolling[7,8] ,andsuchanannealingiscalledadditional annealinginthispaper .Buttherewerefewinv…     

淬火介质对7055铝合金晶界析出行为的影响

采用透射电镜研究了淬火介质对7055铝合金晶界析出相及无沉淀析出带的影响。结果表明，空气淬火时，合金冷却过程在晶界上析出η平衡相。合金经室温水淬及沸水淬火合金时效后，晶界析出相尺寸差别小，呈链状连续分布；晶界无沉淀，析出带较窄，平均宽度分别约为33nm和43nm。空气淬火合金时效后晶界析出相尺寸差别较大，呈不连续分布；晶界无沉淀，析出带很宽，约102nm。对其原因进行了分析和讨论。