The distributions of the axial stress and shear stress in Al2O3-TiC/Q235 diffusion bonded joints were studied using finite element method (FEM). The effect of interlayer thickness on the axial stress and shear stress was also investigated. The results indicate that the gradients of the axial stress and shear stress are great near the joint edge. The maximal shear stress produces at the interface of the Al2O3-TIC and Ti interlayer. With the increase of Cu interlayer thickness, the magnitudes of the axial stress and shear stress first decrease and then increase. The distribution of the axial stress changes greatly with a little change in the shear stress. The shear fracture initiates at the interface of the Al2O3-TiC/ Ti interlayer with high shear stress and then propagates to the Al2O3-TIC side, which is consistent with the stress FEM calculating results. 相似文献
3.
用有限元方法计算了Al2O3-TiC/1Cr18Ni9Ti扩散焊接头的应力分布,研究了加热温度、压力和中间层对应力分布的影响.结果表明,残余轴向应力和剪切应力在试样边缘处梯度都较大,靠近中心轴,应力分布比较均匀,最大剪切应力出现在A12O3-TiC/中间层界面处.在扩散焊冷却过程中,Al2O3-TiC/1Cr18Ni9Ti扩散焊接头最大轴向拉应力先是出现在边缘陶瓷侧,随着温度的降低,逐渐向试样中心靠近,应力值也逐渐增大.加热温度越低,轴向压应力越大.压力越大,最大轴向拉应力越小,压应力越大,但压力对剪切应力的影响较小.使用Ti-Cu-Ti复合中间层比使用Ti中间层可降低最大轴向压应力和最大剪切应力. 相似文献
4.
5.
6.
CCD视觉传感器及图像处理技术在焊缝自动跟踪中的应用 总被引:3,自引:1,他引:3
应用程序设计语言VISUAL BISIC研究开发了一种在电弧焊过程中进行轨迹跟踪的实时图像处理方法,由CCD面阵摄像机在焊接点之前摄取坡口图像,通过图像采集系统和计算机软件处理,得到坡口中心位置,以肖妆坡口中心相对初始坡口中心的偏差量为检测量,据此指引焊抢运动进行实时跟踪,轨迹跟踪精度可达0.5mm,如果用多台摄像机同时摄像,则可以检测出三维信息,大大提高跟踪精度。 相似文献
7.
8.
9.
10.
用有限元方法计算了Al2O3-TiC/1Cr18Ni9Ti扩散焊接头的应力分布,研究了加热温度、压力和中间层对应力分布的影响。结果表明,残余轴向应力和剪切应力在试样边缘处梯度都较大,靠近中心轴,应力分布比较均匀,最大剪切应力出现在Al2O3-TiC/中间层界面处。在扩散焊冷却过程中,Al2O3-TiC/1Cr18Ni9Ti扩散焊接头最大轴向拉应力先是出现在边缘陶瓷侧,随着温度的降低,逐渐向试样中心靠近,应力值也逐渐增大。加热温度越低,轴向压应力越大。压力越大,最大轴向拉应力越小,压应力越大,但压力对剪切应力的影响较小。使用Ti-Cu-Ti复合中间层比使用Ti中间层可降低最大轴向压府力和最大前切府力。 相似文献