The green sheets with Ni paste as inner electrodes were sintered at 1 320 ℃ for 1 h under a N2/H2 mixing gas at an oxygen partial pressure p(O2)=10-8-10-12 MPa, and then reoxided at 900-1 000 ℃ to form multilayer positive temperature coefficient of resistance(PTCR). During the experiments, electronic characteristic effects of PTC with different thicknesses were contrasted. A certain extending of Ni diffusion is beneficial to the ohmic contact of multilayer PTCR but excessive diffusion is harmful to PTCR. The diffusion was studied by scanning electron microscopy(SEM) and energy-dispersive X-ray spectrometry(EDS). Inter-diffusion of element takes place along the Ni-BaTiO3 interface, especially Ni diffusion to BaTiO3 dominated the process. Furthermore, the degree of Ni diffusion is very severe as ceramic layers are very thin. 相似文献
3.
以溶胶-凝胶法制备了BaTiO3基PTCR纳米陶瓷粉体,通过适当控制材料的掺杂量和烧成制度达到细化晶粒、降低烧结温度及降低室温率的目的。讨论了溶胶.凝胶过程中水的加入量、乙酸加入量、乙醇加入量、成胶温度对形成细晶粉体的影响,制备出的BaTiO3粉体具有纯度高、粒径小、均匀性好、活性高、热处理温度低等优点。R-T丁曲线表明1260℃较1240℃烧结具有高的升阻比、温度系数,低的电阻率、居里温度:XRD分析表明所得粉体与BaTiO3主峰相吻合;800℃预烧2h所得BaTiO3粉体的TEM图表明粉体分布较均匀、外形为近似球形,其平均晶粒尺寸约30nm左右,与XRD得到的晶粒相当,单个颗粒是单晶;1240℃下烧结所得样品的SEM图片看出样品的平均晶粒约1~2μm、晶粒较为均匀致密。 相似文献
4.
TlBr粉末的水热重结晶提纯和TlBr晶体生长(英文) 总被引:1,自引:0,他引:1
采用水热重结晶法提纯TlBr,用等离子耦合质谱仪检测痕量杂质。结果表明:水热重结晶法是一种有效的TlBr提纯方法,经一次水热重结晶提纯后,杂质Ca,Fe,Mg,K,Zn,Cu,Na和Si的总浓度从139.6×10–6(质量分数,下同)下降为9.3×10–6;随着溶液冷却速率的下降,杂质含量下降幅度明显增大。对比真空蒸馏提纯法,水热重结晶法具有更高的提纯效率。以水热重结晶制备的TlBr粉为原料,采用垂直Bridgman法生长了尺寸为φ8mm×55mm的TlBr晶体。TlBr晶体的禁带能为(2.83±0.005)eV,电阻率为2.26×1011(Ω·cm)。 相似文献
5.
6.
自蔓延高温合成过程中的非平衡问题 总被引:1,自引:1,他引:0
自蔓延高温合成(SHS)技术是一门新兴的学科,因其独特的优越性而备受材料科学家的关注。在简要介绍自蔓延高温合成技术的基础上,系统地阐述了SHS过程中的非平衡现象,重点分析了非平衡现象的影响因素及SHS非平衡理论的研究进展,并对SHS非平衡研究作了简要评价,提出了目前存在的问题和未来SHS的研究方向。 相似文献
7.
8.
9.
采用固相反应法制备了Ba0.96 Ca0.04 Ti0.8 Zr0.2 O3 (BCTZ)陶瓷粉末,然后采用溶液混合,热压的方法制备了BCTZ-环氧树脂(Epoxy)复合材料,研究BCTZ-环氧树脂复合材料介电性能与陶瓷含量、测试频率和温度的关系.结果表明,BCTZ-环氧树脂复合材料具有高的介电常数(48.6)和低的损... 相似文献