Preparation of Mesoporous Ce0.5Zr0.5O2 Mixed Oxide by Hydrothermal Templating Method

Mesoporous Ce0.5Zr0.5O2 mixed oxide with high specific surface area was synthesized under basic condition in the presence of non-ionic surfactant PEG-4000. The effect of synthesis conditions, such as synthesis temperature and the molar ratio of PEG-4000/（[ Ce] ＋ [ Zr] ）, on specific surface area were investigated. The products were characterized by transmission electron microscopy, powder X-ray diffraction, and nitrogen adsorption-desorption measurements, respectively. The results showed that synthesis temperature and the molar ratio of PEG-4000/（[ Ce] ＋ [ Zr] ） had great influence on specific surface area. Under the optimum synthesis conditions, the prepared Ce0.5Zr0.5O2 mixed oxide presented cubic fluorite-type structure and possessed high surface area of 148.6 m2·g^-1 with wormlike pores.     

立式叶滤机在母液浮游物回收工段中的应用及问题分析

介绍了立式叶滤机的工作原理,分析了叶滤机在浮游物回收工段中的主要问题,并结合实际运行提出了改进措施。实践证明,采取的改进措施保证了设备的稳定运行。     

铝酸钠溶液蒸发有效温差的计算和分配原则

阐述了氧化铝生产中铝酸钠溶液在蒸发时产生温差损失的原因,并提供了有效温差的计算方法和分配原则,对于铝酸钠溶液蒸发的设计计算具有参考价值。     

溶剂热-煅烧法合成纳米ITO粉体

本文采用溶剂热-煅烧法制备纳米铟锡复合氧化物(ITO).以In(4N)、SnCl4·5H2O为起始原料,通过XRD、SEM及微波吸收性能的分析,考察了溶剂热反应中溶剂对ITO粉体结构及性能的影响.研究表明以1,4-丁二醇为溶剂,KBr为矿化剂(浓度0.5mol/L)在260℃下醇热6h,得到结晶性良好的羟基氧化铟和锡掺杂氧化铟的混合物.溶剂热产物在550℃下煅烧2h得到纳米ITO粉体,醇热-煅烧产物的吸波性能良好.     

粉煤灰提取氧化铝的研究现状

粉煤灰中氧化铝质量分数可达15%～40%,是制备氧化铝的有效资源。综述了近年来从粉煤灰中制备氧化铝的工艺和进展,主要分为酸浸取法,碱焙烧法,(NH4)2SO4焙烧法。分别从各制备工艺的特点和存在的问题等方面进行了简要的评述,并对其发展趋势进行了阐述。     

铈锆复合氧化物的制备及表征

分别采用水热法和共沉淀法制备了铈锆复合氧化物,并对所得的样品进行了XRD,SEM,BET等检测。结果表明,两种方法得到的均是由立方相的Ce0.75Zr0.25O2和四方相的Ce0.5Zr0.5O2组成的复合氧化物。所制备的铈锆复合氧化物均存在中孔结构,水热法制备的样品的比表面积和平均孔径分别为126 m2.g-1和7.3 nm,共沉淀法所得样品的比表面积和平均孔径分别为95 m2.g-1和4.0 nm。     

浅谈几内亚铝土矿高温和低温溶出的经济性对比

对几内亚铝土矿的物相和成分进行了分析，并对该铝土矿进行了高温溶出和低温溶出实验，结合高温溶出和低温溶出的实际生产数据初步计算了两种不同溶出工艺的直接生产成本，对几内亚铝土矿的溶出工艺选择具有一定的参考价值。