1.
Physico-chemical properties and microstructure of hydroxyapatite-316L stainless steel biomaterials 总被引:2,自引:0,他引:2
Sintering shrinkage, compressive strength, bending strength, metallurgical morphology, microstructure and chemical composition diffusion of hydroxyapatite-316L stainless steel(HA-316L SS) composites were investiga-ted. The results show that the sintering shrinkage of HA-316L SS composites decreases from 27.38O/6o to 8.87% for cylinder sample or from 27.18% to 8.62% for cuboid sample with decreasing the volume ratio of HA to 316L SS,which leads to higher sintering activity of HA compared with that of 316L SS. The compressive strength of HA-316L SS composites changes just like parabolic curve (245.3→126.3→202.8 MPa) with reducing the volume ratio of HA to 316L SS. Bending strength increases from 86.3MPa to 124. 2 MPa with increasing the content of 316L SS. Furthermore, comprehensive mechanical properties of 1.0:3.0 (volume ratio of HA to 316L SS) composite are optimal with compressive strength and bending strength equal to 202. 8 MPa and 124. 2 MPa, respectively. The microstructure and metallurgical structure vary regularly with the volume ratio of HA to 316L SS. Some chemical reaction takes place at the interface of the composites during sintering. 相似文献
2.
TiO2/活性炭复合体超临界沉淀法制备及其光催化性能 总被引:1,自引:0,他引:1
以活性炭为载体、超临界二氧化碳为流体、钛酸丁酯为前驱体,用超临界流体沉积法制备TiO2/活性炭(TiO2/AC)复合体。用X射线衍射(XRD)、扫描电镜(SEM)、比表面积分析(BET)、热重-差热(TG-DTA)对TiO2/AC进行表征。以紫外灯为光源,偶氮类染料亚甲基蓝为标准降解物,考察TiO2/AC复合体的光催化... 相似文献
3.
采用沉淀法合成一系列Li(Ni1/3Co1/3Mn1/3)O2-xFx正极材料(0≤x≤0.5);用X射线衍射仪和扫描电镜仪分析了合成产物的晶体结构及表面形貌;利用充放电仪测定产物的电化学性能,结果表明Li(Ni1/3Co1/3Mn1/3)O1.7F0.3的电化学性能最佳,首次充放电比容量分别达181.9、174.0 mA.h/g,材料的结构在循环过程中保持稳定,倍率性能变好,电化学阻抗明显降低。 相似文献
4.
以低品位的钼镍矿石为原料与CaO混合高温焙烧,所得焙烧矿采用常压氨-碳铵浸出,对同时浸出镍和钼的工艺条件进行了研究。探讨了温度、液固比、浸出时间、碳酸铵的用量等因素对钼和镍浸出率的影响。结果表明,在浸出温度45℃,液固比4∶1(mL/g),浸出时间24h,碳酸铵用量w((NH4)2CO3)∶w(焙烧矿)=0.3的最佳浸出条件下,钼和镍的浸出率分别为94.0%和90.1%。 相似文献
5.
6.
以碳酸盐为沉淀剂,采用共沉淀法合成晶型良好的亚微米级Li(Ni1/3Co1/3Mn1/3)O2粉末,并将其与AgNO3复合,采用无电流分解沉积法制备出了Ag表面修饰的Li(Ni1/3Co1/3Mn1/3)O2/Ag电极材料.利用X-射线衍射、扫描电镜及电化学测试等方法表征材料的结构、形貌和电化学性能.结果表明:Ag单质的存在可明显改善Li(Ni1/3Co1/3Mn1/3)O2的电化学性能,尤其是倍率特性,以0.2C、0.5C、1C倍率放电进行测试,经过40次循环后比容量分别为156.2、144.3、137.7mAh·g-1,其容量保持率分别为96.2%、95.3%、93.9%.Ag的表面修饰能使Li(Ni1/3Co1/3Mn1/3)O2电荷转移阻抗大幅度减小,阻抗从65Ω减小到50Ω. 相似文献
7.
1 INTRODUCTIONSincetheendoflastcentury ,studiesonthe preparationand propertiesofnanometerparticleshaveattractedalotofattention .Nanometerzincoxidewithsomespecialprop ertiescouldbewidelyusedinmanyaspects,suchasautomobileindustry ,sun proofcosmet ics,photosen… 相似文献
8.
9.
几种野菜部分营养元素的测定及营养价值 总被引:7,自引:0,他引:7
测定了吉首地区蕨, 笋,香椿等8种野菜部分营养元素的含量,并对其营养价值进行了讨论。 相似文献
10.
化学共沉淀法制备四方相ZrO2-CaO纳米粉 总被引:2,自引:0,他引:2
以氯氧化锆、硝酸钙和氨水为原料,并掺杂摩尔数分数为5%的硝酸钙与共沸蒸馏分散相结合,采用化学共沉淀法制备ZrO2-CaO纳米粉末.DTA分析表明化学共沉淀前驱体在温度为593.81℃和1234.56℃时发生相转变.经在400,600,1100和1300℃煅烧1h后所得粉末,用TEM及BET测定其粒子尺寸,用XRD和Raman光谱分析其相结构,讨论了氧化钙的存在及粒径等因素对氧化锆四方相稳定的影响.结果显示:前驱体经600℃和1100℃煅烧后,可在室温下分别得到平均粒径为9.8nm和43.7nm的四方氧化锆纳米粉末.在掺杂摩尔数分数为5%的硝酸钙的ZrO2-CaO纳米粉末中,四方相的稳定区在600~1100℃,1234.5℃为四方相向单斜相转变的临界温度. 相似文献