以埔酸钇和碳酸氢铵为原料,通过向碳酸氢铵溶液滴加埔酸钇溶液,制备出了前驱物经950℃煅烧后颗粒尺寸大小为40-60nm的Y2O3粉体。该粉体在添加一定量的添加剂后经真空热压和热等静压成功烧结出红外透过率达82%的Y2O3透明陶瓷。 相似文献
2.
3.
进入新世纪以来,我国经济快速增长,各项建设取得巨大成就,但也付出了很大的资源和环境代价,经济发展与资源环境的矛盾日益突出.严峻的形势要求我们一定要从构建社会主义和谐社会的高度,更加注重解决发展不平衡问题,建设资源节约型、环境友好型社会,坚持节约发展、清洁发展、安全发展,推动经济社会协调发展,促进人与自然相和谐.我们必须进一步优化产业结构,大力发展循环经济,推广清洁生产,节约能源资源,坚决淘汰落后工艺技术和生产能力,从源头上控制环境污染. 相似文献
4.
5.
6.
The effect of LiF as a sintering aid to the optical transparency of magnesium aluminate (MgAl2O4) spinel ceramics is studied. The spinel ceramics is prepared in a process proved to be suitable for commercial production. LiF, in different concentrations ranging from 0-2.5 wt%, is doped into MgAl2O4 powders prepared by sol-gel method. Sample MgAl2O4 ceramic discs are fabricated by ball milling, cold pressing, and hot-pressing, or hot-isostatic-pressing of the powder mixtures. Optical transparency measurements show that, hot-pressed samples exhibit higher transparency when more LiF is added. While for hot-isostatic pressed samples, excessive LiF content leads to a decrease in optical transparency. The optimal LiF doping quantity is suggested for the present technique. 相似文献
7.
LiF对镁铝尖晶石透明陶瓷红外透过率的影响 总被引:1,自引:0,他引:1
以溶胶-凝胶法制备镁铝尖晶石(以下简称“尖晶石”)粉末, 掺入0~2.5wt%的LiF, 经球磨后, 测试混合粉末的物相组成. 采用热压(HP; 32 MPa/1550℃)及热压结合热等静压(HP/HIP; 热等静压工艺条件为150 MPa/1700℃)工艺制备出尖晶石透明陶瓷. 分析测试了掺入不同LiF的尖晶石陶瓷的结构和红外透过率, 采用感应耦合等离子体(Inductively Coupled Plasma, 或ICP)方法测定了LiF掺杂后的粉料和透明陶瓷中的Li离子含量. 实验显示, LiF的加入促进了尖晶石晶粒长大和气孔的排除, 并促进了尖晶石陶瓷烧结的致密化进程. 添加1.0wt%~1.5wt% LiF的尖晶石透明陶瓷具有最高的红外透过率. LiF在尖晶石陶瓷中形成残余物质, 添加过量的LiF对尖晶石陶瓷的光学性能会产生不利影响. 相似文献
8.
制备了一系列非化学计量比镁铝尖晶石粉体及透明陶瓷( MgO·nAl2O3,n=1,1.5,2,4),研究了n值对粉体物相的影响以及n值与陶瓷中波红外透过率、抗弯强度的关系.n值为1.5、2、4时,MgO·nAl2O3粉体仍可保持纯尖晶石相.MgO·1.5A12O3透明陶瓷在具备与计量比镁铝尖晶石透明陶瓷(MgAl2O4,即MgO·Al2O3)相当的优良中波红外透过率的同时,抗弯强度从152 MPa提高至215 MPa,提高幅度达41%.力学性能的提升有利于镁铝尖晶石透明陶瓷的应用. 相似文献