First Principle Calculation of NbC Precipitation Competition between TiC Particle and Ferrite Matrix

The electronic structure, cohesive energy and interfacial energy of ferrite (100)/NbC (100) and TiC (100)/NbC (100) interfaces have been investigated by the first-principles calculation. Moreover, the heterogeneous nuclei mechanism of NbC particle was also analyzed. The results showed that the stacking sequences have a great influence on the cohesive energy and equilibrium interfacial separation of the above-mentioned interfaces. Compared with C-terminated interfaces, the cohesive energy of Nb-terminated ones is lower while the equilibrium interface distance is larger. Among the two C-terminated interface structures, the interfacial energy between the NbC and ferrite is 4.54 J/m², which is larger than that of NbC/TiC interface (1.80 J/m²). Therefore, NbC particles prefer heterogeneous nucleation on TiC particles surface rather than the ferrite matrix, which agrees well with the experimental result.     

变形和回火时间对F40微合金钢组织与性能的影响

利用电阻加热结合天锻锻压机对F40微合金钢试样进行不同程度的变形,之后在700℃进行不同的时间回火处理;通过OM、SEM和TEM研究其组织变化,采用电阻仪和显微硬度计测量其电阻率和显微硬度。结果表明:变形量越大,其板条状组织越紊乱,且随着回火时间的延长,板条状组织逐渐呈多边化,回火120 min时局部有小角度亚晶以及位错胞形成;电阻率和硬度随回火时间的变化规律均为先降后升再降,最后趋于稳定;而变形量越大,其电阻率和硬度值越高,达到峰值的时间也越快。     

探讨建筑设计的合理性

在建筑的前期策划、建筑方案设计和建筑技术设计的深化等阶段都应该贯穿着合理性这一原则。自工业社会起,建筑发展构成了社会经济进步的一条重要干线,在发展中消耗的社会资源使其成为了当代能源危机的重要根源之一。     

CuO-CO2-NH3-H2O体系孔雀石浸出的热力学分析

针对氨浸出孔雀石的问题,对CuO-CO2-NH3-H2O体系进行了热力学分析,获得了一系列平衡关系图.结果表明,随着pH值升高,OH^-取代CO3^2-参与形成沉淀,使稳定存在的固体按蓝铜矿、孔雀石、氢氧化铜的顺序转变.pH值对铜的溶解起决定性作用.pH值较低时,H^＋和Cu^2＋竞争与NH3的结合,溶液中铜氨配合物浓度低;pH值较高时,OH-和NH3竞争与Cu^2＋的结合,使铜转化为氢氧化铜沉淀;pH值8-11时,H^＋和OH^-的竞争作用较弱,大部分NH3与Cu^2＋形成配合物,其中Cu（NH3）2＋4为优势物种.氨浸出孔雀石的理论最佳pH值在9.3-9.4之间,该条件时总铜和总氮平衡浓度大体呈直线关系.     

CuO-CO_2-NH_3-H_2O体系孔雀石浸出的热力学分析

针对氨浸出孔雀石的问题,对CuO-CO2-NH3-H2O体系进行了热力学分析,获得了一系列平衡关系图.结果表明,随着pH值升高,OH-取代CO32-参与形成沉淀,使稳定存在的固体按蓝铜矿、孔雀石、氢氧化铜的顺序转变.pH值对铜的溶解起决定性作用.pH值较低时,H+和Cu2+竞争与NH3的结合,溶液中铜氨配合物浓度低;pH值较高时,OH-和NH3竞争与Cu2+的结合,使铜转化为氢氧化铜沉淀;pH值8~11时,H+和OH-的竞争作用较弱,大部分NH3与Cu2+形成配合物,其中Cu(NH3)2+4为优势物种.氨浸出孔雀石的理论最佳pH值在9.3~9.4之间,该条件时总铜和总氮平衡浓度大体呈直线关系.     

L360QS钢钙处理的热力学分析与试验研究

针对管线钢L360QS,利用活度相互作用系数和Bjorkvall方法对钙处理过程进行热力学分析,并对管线钢进行了实验室的钙处理试验和工业试验。热力学分析结果表明,当钢中a(Als)=0.045%时,如果要生成12CaO·7Al2O3夹杂且避免CaS夹杂析出,则应控制钢液中a(Ca)在33.21×10-6左右,a(S)0.002 563%。钙处理试验表明,CaS夹杂数量随着钢液中钙含量的增加而增多,且含MgO·Al2O3尖晶石的夹杂物有所减少。为使氧化夹杂和硫化夹杂变性完全,应控制钢液中w(S)≈0.002%,w(Ca)=0.003 5%~0.004 0%,且w(T.Ca)/w(S)1.9。工业试验结果表明夹杂物变性良好,达到预期效果。     

Al2O3对钢渣提铁后二次渣制取的微晶玻璃性能的影响

为了利用大量的钢渣、改质剂A和改质剂B等固体废弃物制备具有高附加值的微晶玻璃,将钢渣与改质剂A和B混合熔融提铁并采用DTA、XRD、SEM等手段研究了Al2O3对钢渣提铁后二次渣制取的微晶玻璃性能的影响.结果表明,当Al2O3质量分数为3％ ～6％时,试样的主晶相为硅灰石,微晶玻璃晶体呈粒状,晶体结构疏松且有少许气孔存在;随着Al2O3含量的增加,微晶玻璃的主相由硅灰石转变为镁黄长石和钙铝黄长石.当Al2O3质量分数为15％时,析晶动力学参数k(Tp)最大,析晶能力强,此时微晶玻璃的晶粒尺寸为1～2 μm左右,且晶相结构致密,其抗弯强度为49.85 MPa,显微硬度为3.60 GPa,抗压强度为181.47 MPa,符合建筑装饰用微晶玻璃的国家标准要求.     

硅酸锌加压硫酸浸出的热力学分析与实验研究

计算绘制了Zn-Si-H2O系ET-pH图,分析了硅酸锌硫酸浸出和原硅酸高温脱硅的热力学可行性. 通过人工合成硅酸锌的加压酸浸实验,考察了始酸浓度、终点pH值、铁含量、硫酸铝添加量、浸出温度对硅酸锌酸浸和硅酸凝聚的影响. 结果表明,升高浸出温度能有效降低硅溶胶的稳定性且有利于原硅酸的高温脱硅过程,进而改善矿浆的过滤性能;硫酸铝能促使硅溶胶凝结析出,可降低硅酸浓度;控制恰当的矿浆终点pH值和Si/Fe及Si/Al质量比均有助于硅析出. 在浸出温度120℃、浸出时间0.5 h、液固比8 mL/g及H2SO4浓度120 g/L的优化条件下,锌、硅浸出率分别约为98%和1%.     

钙处理对无取向硅钢总氧含量的影响

在RH破真空后,往钢液中喂硅钙线,通过比较喂钙前后钢液中T．O、N以及夹杂物尺寸、数量的变化,来研究钙处理对无取向硅钢总氧含量的影响。热力学计算表明无取向硅钢中由于铝含量较高,钢中自由氧含量低,钢中总氧含量基本可以代表钢中氧化夹杂物的含量。钙处理可以明显降低无取向硅钢的总氧含量,这主要是由于钙处理会使钢液中夹杂物变性长大,密度减小,从而有利于夹杂物的上浮去除。     

四流方坯连铸中间包结构优化

在实验室建立了4流中间包流体流动的物理模型,通过测定停留时间分布(RTD)曲线,研究不同的控流装置组成的中间包结构对流体流动特性的影响。研究结果表明:沟槽或者圆孔槽均能明显改善各流流动特性的一致性,与带"V"型挡墙组合的挡坝高度对中间包内钢液的流动特性有影响;适当高度的坝与湍流控制器、沟槽、"V"型挡墙组合的控流装置在控制流体流动方面效果较好,在其基础上将沟槽改成圆孔槽控流效果更佳。根据实验研究提出最佳方案,即带湍流控制器、孔径φ150mm的"V"型挡墙、高300mm的坝和圆孔槽的中间包组合。