Synthesis and characterization of branched yttrium hydroxide fluoride microcrystals with hierarchical tubular structure

Hexagonal yttrium hydroxide fluoride microcrystals were prepared by a two-step hydrothermal route using yttrium nitrate, sodium hydroxide and sodium fluoride as raw materials to react in propanetriol solvent. The samples were characterized by powder X-ray diffraction (XRD), energy dispersive spectrum (EDS), scanning electron microscopy (SEM), transmission electron microscopy (TEM), Fourier trans-form infrared spectroscopy (FT-IR), thermogravimetre and differential-thermogravimetric analysis (TG-DTA), which revealed that Y(OH)2.14F0.86 microcrystals were multi-branched and that the branches of Y(OH)2.14F0.86 microcrystals were composed of hierarchical tubes. This novel multi-branched and intriguing hierarchical tubular structure of yttrium hydroxide fluoride maybe has a potential application in photoelectric crystals. The formation of branched Y(OH)2.14F0.86 microcrystals with hierarchical tubular structure were due to the substitution reaction and Oswald ripening.     

碳糊电极阳极吸附伏安法测定双酚A

报道了用碳糊电极阳极吸附伏安法测定双酚A的方法。在Na2HPO4-NaH2PO4(pH 7.0)缓冲液中,双酚A在碳糊电极(CPE)上有一灵敏的吸附氧化峰,峰电位为0.63 V(vs.SCE)。该氧化峰的二阶导数峰电流与双酚A的浓度在2.0×10-8~8.0×10-6mol/L(富集90 s)范围内呈良好的线性关系,相关系数为0.9963,检出限为1.0×10-8mol/L(S/N=3,富集110 s),探讨了双酚A在碳糊电极上的伏安性质和电极反应机理,并且成功应用于聚碳酸酯塑料中双酚A含量的测定与其加入回收率实验。     

Controlled synthesis and formation mechanism of sodium yttrium fluoride nanotube arrays

Cubic and hexagonal sodium yttrium fluoride were successfully synthesized from yttrium nitrate, sodium fluoride and poly-ethanediol in propanetriol solvent under a facile hydrothermal route. By regulating the molar ratio of yttrium and fluoride, hydrothermal tem-perature and reaction time, the phase and shape of sodium yttrium fluoride were commendably controlled. The as-prepared products were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive X-ray spectrum (EDS) techniques. It was revealed that the hollow-structured Na(Y1.5Na0.5)F6 nanotubes self-assembled and arrayed orientedly to be bamboo raft-shaped. The for-mation of hexagonal Na(Y1.5Na0.5)F6 nanotube arrays was attributed to solid-liquid-solid process and Oswald ripening. This study provided a simple method to prepare hexagonal bamboo raft-shaped Na(Y1.5Na0.5)F6 on a large scale, which broadened their practical applications.     

水热法合成氢氧化钇纳米管

以Y₂O₃为原料,在密闭反应器中采用水热法合成氢氧化钇纳米管. 分别采用X射线粉末衍射(XRD)、扫描电镜（SEM）、能谱（EDS）和热重－差热分析（TG-DTA）方法对所合成的氢氧化钇纳米管进行了物相、形貌、成分表征和热稳定性分析. 对影响氢氧化钇纳米管形成的反应条件如水热温度和水热时间进行了研究,采用透射电镜（TEM）分析了产物各个生长阶段的形貌,推测了氢氧化钇纳米管的形成机理. 研究表明：水热法制备氢氧化钇纳米管材料的最佳合成条件是乙醇和水作为溶剂,pH值为11~12、反应温度为220℃、反应时间为24h;氢氧化钇纳米管的形成过程可以分为两个阶段：第一阶段为钇前驱体的产生,第二阶段为钇前驱体转变为氢氧化钇纳米管.     

上衣下裳间的闪亮装饰——侗族围腰浅析

通过对侗族服饰中围腰的款式、色彩、纹样等进行梳理归纳,从美学、色彩学的角度阐明围腰在侗族女性服饰中的重要性。     

CO2开关型表面活性剂聚酯烯基磺酸钠的合成及其乳化性能

高分子表面活性剂被广泛应用于科学研究及食品、农业、纺织等工业领域。为了减少在大多数实际应用过程结束后失去活性的高分子因残留引起的副作用,设计并开发新型的开关型高分子表面活性剂具有重要的意义和应用价值。为此,通过自由基聚合法制备了一种CO₂开关型高分子表面活性剂聚(甲基丙烯酸二乙氨基乙酯-乙烯基磺酸钠)(P(DEAEMA-SVS))。采用1H-NMR谱和GPC谱研究聚合物的结构与分子量分布。通过表面张力和界面张力的变化研究P(DEAEMA-SVS)乳液的稳定性。当甲基丙烯酸二乙氨基乙酯(DEAEMA)/乙烯基磺酸钠(SVS)单体投料比为1∶1(摩尔比)时,形成的聚合物粒子粒径约为113 nm,粒径分布窄,可将水的表面张力降低至37.279 mN/m,将水/液体石蜡的界面张力降低至5.492 mN/m,是一种有效的CO₂开关型表面活性剂,可作为唯一乳化剂稳定乳液。P(DEAEMA-SVS)的水/液体石蜡乳液具有很好的CO₂开关性能,在通入CO₂ 30 min后可破乳,在60℃下通入N₂又可再乳化,且可多次循环。P(DEAEMA-SVS)表面活性剂水溶液可与液体石蜡形成水包油型乳液。乳化机制研究表明,P(DEAEMA-SVS)因侧链上的叔胺基团的疏水性,在CO₂的作用下发生质子化作用形成亲水的季铵盐,使乳液油水两相分离而破乳;60℃温度下通入N₂可去除CO₂,使聚合物侧链上的叔胺基团去质子化疏水吸附在油水界面上再次稳定乳液。      

ρ-Al2O3在不同介质中的水化行为研究

通过测定ρ-Al2O3在9种介质中水化时料浆的温度与粘度变化和水化产物相组成分析与显微结构观察研究ρ-Al2O3的水化行为.研究结果表明,酸性介质阻止ρ-Al2O3的水化,碱性介质促进ρ-Al2O3的水化;ρ-Al2O3在水中和碱性介质中的水化产物主要为粒状、结晶良好的拜耳石,酸性介质中为结晶不完整、呈无定形的勃姆石.     

开关表面活性剂的机理及其研究进展

表面活性剂的应用已渗透到乳化、分散等各个方面,然而大多数应用中表面活性剂仅被需要用在某一阶段,过程结束后需要其分离或失活。因此,开关表面活性剂的研究引起了广泛的关注。本文介绍了近年来被发现的开关表面活性剂的开关种类,并概述了温度、酸碱、CO_2等开关表面活性剂的响应基团及其作用机理。同时指出了开关表面活性剂在稠油的乳化降粘领域的应用前景。     

Zn2+/GaOOH纳米线的制备、表征与荧光性能

羟基氧化镓(GaOOH)是一类宽带隙的半导体材料,在光催化降解有机染料、甲醇燃料电池、锂离子电池和生物光学成像方面有着潜在的应用前景。本研究以乙二胺四乙酸二钠(Na₂Y)为模板剂,选取醋酸锌和硝酸镓为反应源,在简便易操作的水热条件下制备了Zn²⁺/GaOOH纳米线。采用XRD、SEM、HRTEM、EDS对材料进行了物相、成分、形貌与微结构表征。所制备的Zn²⁺/GaOOH纳米线长度达数十微米、直径约为100 nm,粗细均匀;Zn²⁺/GaOOH晶体呈现单晶的特性,纳米线沿<110>晶向生长。反应源及其摩尔量强烈地影响着产物的物相和形貌。当控制硝酸镓为1.5 mmol不变,Zn(Ac)₂为1.0 mmol,Na2Y为0.5 mmol时,生成ZnGa₂O₄;Na₂Y为1.0～1.7 mmol时,生成Zn²⁺/GaOOH纳米线。改变Zn(Ac)2为2.0 mmol,当Na2Y为1.5 ...     

“材料化学”湖南省特色专业建设的思考（二）——专业实验教学

湖南科技大学材料化学专业于2009年被批准建设为湖南省特色专业。结合本专业2年来的建设情况,从专业实验教学的角度,分析与总结了专业实验室的建设、实验室师资的建设以及具有特色的专业实验教学体系的构建。