非均相羰基氧化一步合成碳酸二苯酯的研究(Ⅴ)筛选催化剂及优化合成条件

Pd/LaxPbyMnOz, Pd/C, Pd/molecular sieve and Pd-heteropoly acid catalysts for direct synthesis of diphenyl carbonate (DPC) by heterogeneous catalytic reaction were compared and the results of DPC synthesis indicated that the catalyst Pd/LaxPbyMnOz had higher activity. The Pd/LaxPbyMnOz catalyst and the support was characterized by XRD, SEM and TEM, the main phase was Lao.szPbo.asMnOa and the average diameter could be about 25.4nm. The optimuna conditions for synthesis of DPC with Pd/LasPbyMnOz were determined by orthogonal experiments and the experimental results showed that reaction temperature was the first factor of effect on the selectivity and yield of DPC, and the concentration of O2 in gas phase also had significant effect on selectivity of DPC. The optimum reaction conditions were catalyst/phenol mass ratio l to 50, pressure 4.5MPa, volume concentration of O2 25%, reaction temperature 60℃ and reaction time 4 h. The maximum yield and average selectivity could reach 13% and 97% respectively in the     

非均相催化一步合成碳酸二苯酯的研究(VI)Sn的添加方法及添加量对Pd-Sn催化性能的影响

The compound metal oxide Lax Pby Mnz O used as support was prepared by the sol-gel method, and the catalyst in which Pd was used as active component and Sn as co-active component for direct synthesis of diphenyl carbonate (DPC) with heterogeneous catalytic reaction was obtained by co-calcination and precipitation respectively. The catalyst was characterized by XRD, SEM and TEM respectively. The specific surface area of catalysts was measured by ChemBET3000 instrument, and the activity of the catalysts was tested by the synthesis of DPC in a pressured reactor. The results showed that when the co-active component Sn was added by co-calcination method A, its loading content was equal to 14.43% and active component Pd was loaded by precipitation, the yield and selectivity of DPC could reach 26.78% and 99% respectively.     

非均相催化一步合成碳酸二苯酯的研究（VI）Sn 的添加量对Pd-Sn催化性能的影响

The compound metal oxide LaxPbyMnzO used as support was prepared by the sol-gel method, and the catalyst in which Pd was used as active component and Sn as co-active component for direct synthesis of diphenyl carbonate (DPC) with heterogeneous catalytic reaction was obtained by co-calcination and precipitation respectively.The catalyst was characterized by XRD, SEM and TEM respectively. The specific surface area of catalysts was measured by ChemBET3000 instrument, and the activity of the catalysts was tested by the synthesis of DPC in a pressured reactor. The results showed that when the co-active component Sn was added by co-calcination method A, its loading content was equal to 14.43% and active component Pd was loaded by precipitation, the yield and selectivity of DPC could reach 26.78% and 99% respectively.