Preparation of Ni/PZT core-shell nanoparticles and their electromagnetic properties

The Ni nanoparticles coated with Pb(Zr,Ti)O_3(PZT) were synthesized by a sol-gel method and in situ reaction. And their structure, oxidation resistance, and electromagnetic properties were investigated. The X-ray diffraction patterns(XRD) exhibited that a small amount of impure phase characterized to Ni(OH)_2 was detected from the ammonia-treated Ni nanoparticles and the ammonia-treated Ni nanoparticles coated with PZT. After being pre-treated with aqueous ammonia, the PZT coating layer was more uniform and about 10 nm in thickness. The oxidation resistance of the ammonia-treated Ni nanoparticles coated with PZT, compared with that of the non-treated ones, was improved by about 66 ℃. The PZT shell layer prepared by in-situ reaction can greatly reduce the dielectric constant and improve the natural resonance loss at high frequency, so as to obtain the optimal impedance matching performance of the electromagnetic wave transmission.     

Ba2+取代对PSN-PZT瓷结构和压电性能的影响

研究了Ba2+A位取代对铌锑锆钛酸铅陶瓷结构及压电性能的影响,XRD分析结果表明:所有样品具有钙钛矿结构,同时Ba2+取代Pb2+使得晶胞体积增大,c/a轴比减小。当Ba2+取代量增大时,样品中三方相和四方相共存。随着Ba2+取代量的增大,陶瓷样品的密度降低,εr(2863)和d33(507pC·N–1)显著提高,居里点向室温移动。     

无铅压电陶瓷(Bi1/2Na1/2)TiO3-KNbO3制备工艺研究

采用传统陶瓷工艺制备了(1-x)(Bi1/2Na1/2)TiO3-xKNbO3(x=0.01,0.02,0.04,0.6,0.08,0.12)无铅压电陶瓷。利用热重-差热(TG-DSC)、X-射线衍射(XRD)和扫描电镜(SEM)等分析技术,研究了(1-x)(Bi1/2Na1/2)TiO3-xKNbO3无铅压电陶瓷的制备工艺条件对陶瓷晶体结构、压电性能的影响。TG-DSC、XRD的结果表明,该体系的的最佳预合成温度在800~850℃;SEM及性能测试的结果表明,该体系随KNbO3含量的增加,烧结温度提高,烧结的温度范围变窄,当x>0.1时,烧结的温度范围只有5~10℃。     

(K0.5Na0.5)1-2xSrx(Nb0.94 Sb0.06)O3无铅压电陶瓷结构及性能研究

以传统电子陶瓷工艺制备了(K_0.5Na_0.5)_1-2xSr_x(Nb_0.94 Sb_0.06)O₃ 无铅压电陶瓷,研究了适量锶、锑取代对陶瓷结构及电性能的影响. 结果表明,少量的锶、锑取代没有改变(K_0.5Na_0.5) NbO₃陶瓷的相结构,仍为单相正交结构的钙钛矿型铁电体;适量的锶取代使得晶粒大小均匀一致,提高了陶瓷的致密度;锶、锑取代降低了陶瓷的居里温度,但对正交四方相变温度的影响不大,且在0~200℃的温度范围,介电常数几乎不依赖频率的变化而变化;在x=0.008处,得到较好综合性能的陶瓷材料：d₃₃=155pC/N,k_p=0.361,Q_m=120,N_p=2862,P_r=23μC/cm²,E_c=1.4kV/mm,ρ=4.411g/cm³.     

(1-x)ZnWO4-xTiO2陶瓷的微波介电性能研究

用固相反应法在1150℃烧结2h得到了致密的(1-x)ZnWO4-xTiO2 (0.1≤x≤0.8)系列微波介质陶瓷,对陶瓷的相组成、显微结构及微波介电性能进行了研究.结果表明:在(1-x)ZnWO4-xTiO2 (0.3≤x≤0.5)陶瓷样品中存在ZnWO4、TiO2及Zn2TiO4三相,当Zn2TiO4相的量较多时,样品的微波介电性能较好.随着TiO2的含量增加,(1-x) ZnWO4-xTiO2陶瓷的εr及τf值单调递增,而Q·f值则先上升后下降.当x=0.4时,(1-x)ZnWO4-xTiO2陶瓷样品的微波介电性能为:εr=26.56、Q·f=42 278 GHz及τf =61.37× 10-6/℃.它是一种具有中等介电常数,中低烧结温度且性能优良的微波介质陶瓷新体系.     

预烧温度对PZN-PZT压电陶瓷电性能的影响

采用传统固相法制备了化学计量比为0.3Pb(Zn1/3Nb2/3)O3-0.35PbTiO3-0.35PbZrO3的压电陶瓷,研究了所制陶瓷的预合成温度对其微观结构和压电介电性能的影响。结果显示,当预合成温度大于800℃时可以获得纯钙钛矿相,低于800℃钙钛矿主晶相不明显且有很多杂相产生。当预烧温度为775℃时,经1 125℃保温3 h烧结的陶瓷具有最佳综合性能:d33=431 pC/N、k31=0.36、Ec=9.98×103 V/mm、Pr=22.52×10–6 C/cm2、εr=1 874、tanδ=0.024、ρ=7.88 g/cm3。     

低温烧结CoFe2O4-(PZN-PZT)多铁复合材料磁电性能研究

采用传统陶瓷工艺和低温烧结制备了CoFe₂O₄-(PZN-PZT)多铁复合陶瓷, 研究了混合方式、PZT包覆和成分变化对其结构、磁性能、磁电耦合性能的影响。XRD图谱和TEM照片显示, 采用溶胶-凝胶和包覆搅拌混合的方法获得了CoFe₂O₄/PZT核壳结构粉末, 在CoFe₂O₄表面形成了10~20 nm的钙钛矿PZT壳层。EDS结果显示, 低温烧结和阻挡层可以有效抑制两相间的元素扩散。SEM照片和磁电性能结果显示, 相对未包覆研磨混合工艺, 包覆搅拌混合可以提高磁性颗粒复合含量, 获得较好烧结匹配性, 有效提高材料的磁电耦合性能。研究结果表明, 包覆搅拌混合制备体积比为4:6的CoFe₂O₄-(PZN-PZT)样品, 经1000℃烧结, 在10 kHz下获得最大磁电耦合系数(18.3 mV/(cm·Oe))。     

复合型直线超声波马达

国内外对直线型超声波马达的理论探索和研制进行了大量的研究。根据近十几年来国内外的有关文献资料,从振动模态的角度分类总结了国内外纵弯型、纵扭型、纵振型、弯振型四类典型直线型超声波马达的发展及其研究现状,并概述了其工作原理和特点。