Bioactive Ca-P scaffolds used for bone reconstruction

1　INTRODUCTIONSkeletalreconstructionorregenerationisre quiredincasesinvolvinglargedefectscreatedbytu morresection ,trauma ,andskeletalabnormalities .Graftsandflapsofautogenoustissuearetwoofthemostsuccessfulmeansofreconstructionbecausetheyallowthetransplantationofbonecontainingbioactivemolecules,livecells ,andfrequently ,avascularsup plythatallowthetransplanttosurviveandremodeleveninhostileradiatedenvironments .However ,onlyaminimalamountoftissuecanbeharvestedforauto grafts,anditisverydiff…     

特高含水期油田化学驱提高采收率方法研究

我国陆上油田大多处于油田开发后期,含水超90％,剩余油挖潜难度加大.为大幅度提高油田采收程度,探索了特高含水油田化学驱油方法.首先,对研究区进行分区对比地层厚度、砂岩厚度,精细描述储层分布规律;其次,基于不同区域储层孔喉结构、渗透率统计结果,分析储层非均质特征;最后,设计出与主力油藏相似的三维非均质物理模型,结合岩心分析实验资料,对化学驱不同质量分数、压力对驱油效果的影响进行了研究,总结出了化学驱油效率的变化特征.研究发现,化学驱可提高驱油效率8％左右.     

Evaluation of PLGA/chitosan/HA conduits for nerve tissue reconstruction

A micro-envioment for nerve cells and tissue growth were designed and constructed via surface modification of poly(L-lactide-co-glycolide)(PLGA) with chitosan and hydroxyapatite(HA). The poly(L-lactide-co-glycolide)/chitosan/hydroxyapatite (PLGA/chitosan/HA) conduits were manufactured by a combined solvent casting and particulate leaching technique. The conduits were highly porous with an interconnected pore structure and 76.5% porosity. Micropores with 50–100 micrometer diameter were formed in the conduits. In vivo application of PLGA/chitosan/HA conduits for reconstruction of 10 mm sciatic nerve defect was assessed by the walking track analysis, the quantifying of the wet weight of tibialis anterior muscle and the histological assessment. The conduits in host rats in vivo can not only be an effective in promoting regenerating of nerves but can also lead to favorable nerve functional recovery. Funded by the National Natural Science Foundation of China(No.50774096)     

纳米二氧化硅粉末的制备

采用微乳液法制备了高比表面积纳米SiO2粉末，考察了微乳液体系的配制、反应物浓度、反应温度、焙烧温度、共沸蒸馏脱水工艺制备的纳米SiO2性能的影响，并通过比表面积（BET）、透射电镜（TEM）、红外光谱分析（IR）、X射线衍射（XRD）对样品进行了表征。结果表明，粉末制备的工艺参数对样品性能影响较大，在较佳工艺条件下制备的纳米SiO2粉末近似呈球形，粒径为15～30nm，比表面积高达580-630m^2／g。共沸蒸馏工艺能充分地脱去凝胶中残余的水分，防止因含水胶体干燥过程引起的粉末硬团聚，从而显著地提高了粉末的性能。     

混有CACC车辆和ACC车辆的混合交通流驾驶舒适性

为了探索协同自适应巡航控制(cooperative adaptive cruise control,CACC)车辆对交通系统的潜在影响,分析了CACC车辆市场普及过程中存在的CACC车辆、自适应巡航控制(adaptive cruise control,ACC)车辆与人工驾驶车辆混合交通流驾驶舒适性.应用加州伯克利PATH实车验证的ACC模型和CACC模型进行数值仿真实验,采用国际ISO-2631-1标准评价混合交通流舒适性,并对ACC和CACC期望车间时距进行参数敏感性分析.最后,从交通流稳定性的角度,对舒适性仿真结果进行了讨论.结果表明:随着CACC市场率的增加,舒适性呈现先恶化、再逐渐提升的趋势.较大的ACC车间时距有利于抑制舒适性的恶化程度,CACC车辆对舒适性的提升作用不受其车间时距取值的影响.混合交通流稳定性定性地决定了舒适性的变化趋势,人工车辆安装车车通信设备,有助于舒适性的逐渐提升.     

Preparation of monomer of degradable biomaterial poly（L-lactide）

1INTRODUCTION Polylactide,oneoftheimportantbiodegrada blematerials,whichhasfavorablebiocompatibility andabsorption[1],hasbeenusedinimplant,chor dasericachirurgicalis,drugcontrolledrelease,boneinternalfixation,tissueengineeringetc[25]. Thepoly(L lactide)(PLLA)withhighrelative molecularmasswasobtainedbyring openingpoly merizationatpresent.Thatis,firsttheintermedi ateproduct(lactide)wasobtainedfromlacticacid, thenthepoly(L lactide)wasobtainedfrominter mediateproductbyring openingpolymer…     

铕三元配合物的合成、表征及其光致发光性能

以苯甲酸、邻苯二甲酸、间苯二甲酸、水杨酸、丙烯酸、甲基丙烯酸、α—噻吩基三氟甲酰丙酮为第一配体,二安替比林甲烷,三正辛基氧化膦、2,2’-联吡啶、邻菲咯啉及邻菲咯啉N-氧化物为第二配体,合成了系列铕三元配合物。经元素分析确定了它们的组成;研究了它们的紫外吸收光谱、红外吸收光谱及荧光光谱。紫外光谱的研究表明,配合物的紫外吸收主要表现为配体的吸收,但是吸收峰的位置发生了移动;红外光谱的研究表明,配合物的红外光谱不同于自由配体的红外光谱,在400~500 cm-1出现了吸收峰,这是Eu-O的伸缩振动峰;荧光光谱的研究表明,第二配体的加入可以显著提高配合物的荧光性能。     

一步还原包裹粉工艺制备WC-Co超粗硬质合金

以费氏粒度为4.1μm的WC粉末和CoCl_2·6H_2O、(NH_4)_2C_2O_4·H_2O为原料,将钴粉制备过程与粉末混合过程相结合,一步还原制备WC-Co包裹粉,并以包裹粉为原料成功制备了WC-8%Co(质量分数)超粗硬质合金。借助扫描电镜、X射线衍射仪、化学元素分析仪、力学试验机等分别对WC-Co复合粉末及硬质合金的微观形貌、物相组成和性能进行表征与分析。结果表明,一步还原法制备的WC-Co包裹粉末中,Co为fcc和hcp双相结构,Co相呈树枝状包裹在WC粉末表面。由该包裹粉制备的硬质合金组织结构均匀,综合性能优异,合金平均晶粒尺寸为8.9μm,密度14.63g·cm~(-3),硬度87.6HRA,抗弯强度2438 MPa,断裂韧性20.92 MPa·m~(1/2)。一步还原包裹粉工艺克服了传统湿磨工艺混料过程中WC粒度显著减小的问题,晶粒度可控性好,且工艺流程简单,有潜在的工业应用价值。     

固溶处理对NbTiZr合金微观组织与力学性能的影响

采用粉末冶金方法制备了50Nb-20Ti-Zr(mass%)合金,并研究了固溶处理对其组织和性能的影响。结果表明:当固溶时间为6 h时,该合金的典型组织是以条幅分解为基础的片层状组织,并且随固溶温度的升高,晶界无析出带现象越明显,合金的弹性模量没有明显的变化,但其断裂强度有所下降;当固溶时间为18 h时,随固溶温度的升高,合金的组织呈现出"片层状-球化-针片状-等轴化"的演化过程,合金的弹性模量与断裂强度均逐渐增加。合金的断口形貌是由塑性韧窝、河流花样和平行分布的准解理小刻面组成,属于韧性断裂和脆性断裂组合的混合型断裂。     

聚合物包覆邻氨基苯甲酸铽配合物的制备与荧光性能

采用直接沉淀工艺,在聚乙烯吡咯酮-乙烯乙酸酯（PVP-VAc）嵌段共聚物在溶剂中形成的微反应器中,制备出表面包覆有嵌段共聚物的邻氨基苯甲酸铽配合物。通过X射线衍射谱（XRD）、透射电子显微镜（TEM）、荧光光谱（LS）、紫外（UV）和红外（IR）光谱对表面包覆的纳米铁粉的结构和形貌进行了分析,并用荧光分光光度计分析了其发光性能。XRD表明所制备的配合物是与配体和氯化铽完全不同的新的晶体,TEM显示样品为形状很规则的长柱状体,长约为150nm,截面为100nm的正方形。LS表明聚合物包覆的邻氨基苯甲酸铽配合物具有很好的荧光性能。紫外光谱说明配合物的紫外吸收主要表现为配体的吸收,红外光谱的分析说明邻氨基苯甲酸铽配合物表面包覆了PVP-VAc嵌段共聚物。