Improving the properties of polylactic acid by blending with low molecular weight polylactic acid‐g‐natural rubber

The low molecular weight (M_w) polylactic acid‐g‐natural rubber (PLA‐g‐NR) was synthesized by grafting the maleated natural rubber (MNR) with low molecular weight PLA at a weight ratio of 1:1 in toluene at 80°C. Two types of MNR (MNR10 and MNR20) having anhydride moieties of 10 and 20 wt%, respectively, were prepared. The reaction was followed by IR analysis. Next, the obtained PLA‐g‐NR was blended with pristine PLA using a twin‐screw extruder at PLA to PLA‐g‐NR weight ratios of 90:10, 80:20, 70:30, and 60:40 followed by compression to obtain specimens for testing. In case of 10 wt% PLA‐g‐NR having MNR10, it was found that blending of PLA with PLA‐g‐NR resulted in a 200% improvement in impact strength and twofold percent elongation at break (flexibility). Further SEM analysis confirmed that PLA‐g‐NR was compatible with PLA matrix. In contrast, NR was present as disperse particles which exhibited poor adhesion to PLA. From these findings, it was also found that PLA‐g‐NR was capable of improving the properties of PLA more than NR due to the fact that it exhibited higher compatibility. POLYM. ENG. SCI., 54:2770–2776, 2014. © 2013 Society of Plastics Engineers