This research emphasizes on the development of highly filled graphene‐polybenzoxazine composites and investigates thermal, electrical, and mechanical properties of the obtained composites for bipolar plate applications. The composition of graphene loading was achieved to be in the range of 10–60 wt%. The experimental results revealed that at the maximum graphene content of 60 wt% (44.8 vol%) in the polybenzoxazine, storage moduli at room temperature of the composites were considerably enhanced with the amount of the graphene, that is, from 5.9 GPa of the neat polybenzoxazine to about 25.1 GPa at 60 wt% of graphene. Glass transition temperatures (Tg) of the obtained composites were observed to be 174–188°C and the values substantially increased with increasing the filler contents. At 60 wt% of graphene content, thermal conductivity, as high as 8.0 W/mK, is achieved for the graphene‐filled polybenzoxazine. Furthermore, the flexural modulus and flexural strength of the composites were found to be as high as 18 GPa and 42 MPa, respectively. Water absorption of graphene filled‐composite is relatively low with the value of only about 0.06% at 24 h of water immersion. Additionally, electrical conductivity was measured to be 357 S/cm at maximum loading of the graphene. Therefore, the graphene‐filled composites based on polybenzoxazine are highly attractive as bipolar plates for polymer electrolyte membrane fuel cells applications. POLYM. COMPOS., 37:1715–1727, 2016. © 2014 Society of Plastics Engineers 相似文献
3.
Arissara Ratcha Chanatip Samart Boonyawan Yoosuk Hideo Sawada Prasert Reubroycharoen Suwadee Kongparakul 《应用聚合物科学杂志》2015,132(42)
Biorenewable polyisoprene latex obtained from natural rubber, Hevea brasiliensis, was used to prepare the reusable polyisoprene–poly(alkyl acrylate) foam for petroleum‐based liquid absorption. The foam was produced via latex vulcanization and cured by steaming. The effect of various types of poly(alkyl acrylate) such as poly(methyl methacrylate) (PMMA), poly(butyl methacrylate) (PBMA), and poly(butyl acrylate) (PBA) on oil sorption capacity of the foam were studied. Scanning electron microscope (SEM) images showed interconnected open‐cell macrostructure with the foam porosity greater than 75% and good compression set. The oil sorption capacity of the foam was in the range of 2.0–16.6 g g?1. The addition of poly(alkyl acrylate) enhanced hydrophobicity and oil sorption capacity of the foam. The absorbed oil was easily recovered by squeezing and the foam can be reused up to 30 sorption–desorption cycles and still preserve high quality sorption. © 2015 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2015 , 132, 42688. 相似文献
1