Interfacial microstructure and mechanical properties of Ti3SiC2 ceramic and TC11 alloy joint diffusion bonded with a Cu interlayer

Reliable joints of Ti₃SiC₂ ceramic and TC11 alloy were diffusion bonded with a 50 μm thick Cu interlayer. The typical interfacial structure of the diffusion boned joint, which was dependent on the interdiffusion and chemical reactions between Al, Si and Ti atoms from the base materials and Cu interlayer, was TC11/α-Ti + β-Ti + Ti₂Cu + TiCu/Ti₅Si₄ + TiSiCu/Cu(s, s)/Ti₃SiC₂. The influence of bonding temperature and time on the interfacial structure and mechanical properties of Ti₃SiC₂/Cu/TC11 joint was analyzed. With the increase of bonding temperature and time, the joint shear strength was gradually increased due to enhanced atomic diffusion. However, the thickness of Ti₅Si₄ and TiSiCu layers with high microhardness increased for a long holding time, resulting in the reduction of bonding strength. The maximum shear strength of 251 ± 6 MPa was obtained for the joint diffusion bonded at 850 °C for 60 min, and fracture primarily occurred at the diffusion layer adjacent to the Ti₃SiC₂ substrate. This work provided an economical and convenient solution for broadening the engineering application of Ti₃SiC₂ ceramic.     

Achieving Rich and Active Alkaline Hydrogen Evolution Heterostructures via Interface Engineering on 2D 1T‐MoS2 Quantum Sheets

Large‐scale production of hydrogen from water‐alkali electrolyzers is impeded by the sluggish kinetics of hydrogen evolution reaction (HER) electrocatalysts. The hybridization of an acid‐active HER catalyst with a cocatalyst at the nanoscale helps boost HER kinetics in alkaline media. Here, it is demonstrated that 1T–MoS₂ nanosheet edges (instead of basal planes) decorated by metal hydroxides form highly active ${\text{edge}}_{{\text{1T‐MoS}}_{\text{2}}}$/ ${\text{edge}}_{\text{Ni}{(\text{OH})}_{\text{2}}}$ heterostructures, which significantly enhance HER performance in alkaline media. Featured with rich ${\text{edge}}_{{\text{1T‐MoS}}_{\text{2}}}$/ ${\text{edge}}_{\text{Ni}{(\text{OH})}_{\text{2}}}$ sites, the fabricated 1T–MoS₂ QS/Ni(OH)₂ hybrid (quantum sized 1T–MoS₂ sheets decorated with Ni(OH)₂ via interface engineering) only requires overpotentials of 57 and 112 mV to drive HER current densities of 10 and 100 mA cm^?2, respectively, and has a low Tafel slope of 30 mV dec^?1 in 1 m KOH. So far, this is the best performance for MoS₂‐based electrocatalysts and the 1T–MoS₂ QS/Ni(OH)₂ hybrid is among the best‐performing non‐Pt alkaline HER electrocatalysts known. The HER process is durable for 100 h at current densities up to 500 mA cm^?2. This work not only provides an active, cost‐effective, and robust alkaline HER electrocatalyst, but also demonstrates a design strategy for preparing high‐performance catalysts based on edge‐rich 2D quantum sheets for other catalytic reactions.     

A review on ultrasonic spot welding of copper alloys

As a solid state joining process, ultrasonic spot welding has been proven to be a promising technique for joining copper alloys. However, challenges still remain in employing ultrasonic spot welding to join copper alloys. This article comprehensively reviews the current state of ultrasonic spot welding of copper alloys with a number of critical issues including materials flow, plastic deformation, temperature distribution, vibration, relative motion, vertical displacement, interface friction coefficient, online monitoring technique, coupled with the macrostructure and microstructure, the mechanical properties and electrical conductivity. In addition, the future trends in this field are provided.     

Enhance cycling performance of LiMn2O4 cathode by Sr2+ and Cr3+ doping

Spinel LiSr_0·1Cr_0·1Mn_1·8O₄ was synthesised by high temperature solid state method in order to enhance the electrochemical performance. The LiSr_0·1Cr_0·1Mn_1·8O₄ (LSCMO) materials were characterised by X-ray diffraction (XRD), scanning electron microscopy (SEM) and electrochemical tests. The XRD and SEM studies confirm that LSCMO had spinel crystal structure with a space group of Fd3m, and the particle of LSCMO shows irregular shape. The cyclic voltammetry data illustrated that the heavy current charge–discharge performance of LMO was improved by Sr²⁺ and Cr³⁺ doping. The galvanostatic charge–discharge of LSCMO cathode materials was measured at 1, 5, 10 and 20 C. The results indicated that LSCMO improved the capacity retention.     

Effects of Undercooling and Transformation Time on Microstructure and Strength of Fe–C–Mn–Si Superbainitic Steel

Strength of Materials - A metallographic method, dilatometry, and X-ray diffraction were applied to investigate the effects of undercooling and holding time on bainitic transformation,...