Improving hydrophobicity on polyurethane-based synthetic leather through plasma polymerization for easy care effect

This study reports on the deposition of a hydrophobic coating on polyurethane (PU)-based synthetic leather through a plasma polymerization method and investigates the hydrophobic behavior of the plasma-coated substrate. The silicon compound of hexamethyldisiloxane (HMDSO), inactive gas argon (Ar), and toluene were used to impart surface hydrophobicity to a PU-based substrate. Surface hydrophobicity was analyzed by water contact angle measurements. Surface hydrophobicity was increased by deposition of compositions of 100% HMDSO, 3:1 HMDSO/toluene, and 1:1 HMDSO/toluene. Optimum conditions of 40 W, 30 s plasma treatment resulted in essentially the same initial contact angle results of approximately 100° for all three treatment compositions. The initial water contact angle for untreated material was about 73°. A water droplet took 1800 s to spread out on the plasma-treated sample after it had been placed on the sample surface. An increase in plasma power also led to a decrease in contact angle, which may be attributed to oxidization of HMDSO during plasma deposition. XPS analysis showed that plasma polymerization of HMDSO/toluene compositions led to a significant increase in atomic percentage of Si compound responsible for the hydrophobic surface. The easy clean results for the treated and untreated PU-based synthetic leather samples clearly showed that the remaining stain on the plasma-polymerized sample was less than that of untreated sample. The plasma-formed coating was both hydrophobic and formed a physical barrier against water and stain.     

The analysis of the current–voltage characteristics of the high barrier Au/Anthracene/n-Si MIS devices at low temperatures

The Au/Anthracene/n-Si/Al MIS device was fabricated on the basis of anthracene film covalently bonded to a Si substrate. The MIS device showed Schottky behavior with barrier heights of 0.85 eV and ideality factors of 1.88 at 300 K. The barrier height of the Au/n-Si has increased after deposition of the anthracene layer onto Si. Temperature dependent current–voltage (I–V) measurements were performed on the Au/Anthracene/n-Si/Al MIS diodes in the range 140–300 K. From the temperature dependence of forward bias I–V, the barrier height was observed to increase with temperature. However, the ideality factor decreased with increasing temperature. The values of activation energy (E_a) and Richardson constant (A*) were determined as 0.24 eV and 7.57 × 10⁻⁶ A cm⁻² K⁻² from the slope and the intercept at ordinate of the linear region of Richardson plot, respectively. The increase of the series resistance R_s with the fall of temperature was attributed to lack of free carrier concentration at low temperatures.     

Influence of Laser Peening With and Without Coating on the Surface Properties and Stress Corrosion Cracking Behavior of Laser-Welded 304 Stainless Steel

Metallurgical and Materials Transactions A - This study aims to investigate the effect of laser peening with (LP) and without coating (LPwC) process on subsurface microstructural evolution,...     

Development of a Stabilized Pan/Tilt Platform and the State of the Art

In the context of this paper, a small scale, medium precision, stabilized pan/tilt platform is developed as a prototype, which is used to compare various stabilization algorithms experimentally. The overall performance of the system depends on rigid body dynamics, structural dynamics, servo control loops, stabilization control algorithm, sensor fusion algorithm and sensory feedback such as from the IMU （inertial measurement unit）. In the case that the response bandwidth of the overall system is high enough, the same hardware can also achieve active vibration isolation. All of these design aspects are investigated in the paper via numerical models and with their experimental verification.     

Human Islet Microtissues as an In Vitro and an In Vivo Model System for Diabetes

Loss of pancreatic β-cell function is a critical event in the pathophysiology of type 2 diabetes. However, studies of its underlying mechanisms as well as the discovery of novel targets and therapies have been hindered due to limitations in available experimental models. In this study we exploited the stable viability and function of standardized human islet microtissues to develop a disease-relevant, scalable, and reproducible model of β-cell dysfunction by exposing them to long-term glucotoxicity and glucolipotoxicity. Moreover, by establishing a method for highly-efficient and homogeneous viral transduction, we were able to monitor the loss of functional β-cell mass in vivo by transplanting reporter human islet microtissues into the anterior chamber of the eye of immune-deficient mice exposed to a diabetogenic diet for 12 weeks. This newly developed in vitro model as well as the described in vivo methodology represent a new set of tools that will facilitate the study of β-cell failure in type 2 diabetes and would accelerate the discovery of novel therapeutic agents.     

Valorization of textile waste hydrolysate for hydrogen gas and levulinic acid production

The objective of this research was to explore the potential for utilizing cellulose-based waste fluff that constitute a significant portion of the solid waste of textile industry to obtain high yield hydrogen gas and levulinic acid by using two-step conversion process. In the first step, hydrothermally hydrolysis of cellulose-based waste fluff was achieved and then the hydrolysate solution was further treated by two different catalysts (Pt/AC and BT500S) in different reaction conditions for producing hydrogen gas and levulinic acid. The results showed that in reforming process the highest gasification performance and hydrogen selectivity (increased up to 25.6%) were achieved from waste fluff hydrolysate compared to other lignocellulosic/cellulosic hydrolysates studied in the literature. On the other hand, 655.3 mg/mL hydrolysate of levulinic acid was produced at the reaction temperature of 200 °C with BT500S solid acid catalyst corresponding to a higher concentration than during one-step conversion process.     

Supramolecular assemblies based on dative boron-nitrogen bonds

Dative boron-nitrogen bonds were found to be a useful binding motif in structural supramolecular chemistry. Crystalline cages were formed using a diboronate ester and 2,4,6-tri(4-pyridyl)-1,3,5-triazine. These cages can act as hosts for electron-rich planar aromatic systems such as triphenylene. Further, crystalline two-dimensional polymers were formed via dative B-N bonds between a triboronic ester and a ditopic pyridyl ligand. Use of an extended triboronate ester resulted in formation of a gel in toluene with a minimum gelation concentration of 0.5 wt%.     

Nanocrystalline spherical iron–nickel (Fe–Ni) alloy particles prepared by ultrasonic spray pyrolysis and hydrogen reduction (USP-HR)

FeCl₂ and NiCl₂ were used for synthesis of nanocrystalline spherical Fe–Ni alloy particles by ultrasonic spray pyrolysis and hydrogen reduction (USP-HR). Spherical ultrafine Fe–Ni particles were obtained by USP of aqueous solutions of iron–nickel chloride followed by thermal decomposition of generated aerosols in hydrogen atmosphere. Particle sizes of the produced Fe–Ni particles can be controlled by the change of the concentration of an initial solution. The effect of the precursor solution in the range of 0.05, 0.1, 0.2 and 0.4 M on the morphology and crystallite size of the Fe–Ni alloy particles are investigated under the conditions of 1.5 h running time, 900 °C reduction temperature, and 1.0 L/min H₂ volumetric flow rate. X-ray diffraction (XRD) studies and Scherrer crystallite size calculations show that the crystalline size was nearly 28 nm. Energy dispersive spectroscopy (EDS) was performed to determine the chemical composition of the particles. Transmission electron microscope (TEM) was used to confirm the crystalline size, that was determined using XRD results. Scanning electron microscopy (SEM) observations reveal that the precursor solution strongly influences the particle size of the synthesized Fe–Ni alloy particles. Spherical nanocrystalline Fe–Ni alloy particles in the range of 80 and 878 nm were obtained at 900 °C.     

Synthesis of High‐Temperature‐Stable TiO2 and its Application on Ag+‐Activated Ceramic Tile

The main purpose of study was to provide a common synergy using Ag⁺‐doped calcium phosphate powder and high‐temperature‐stable TiO₂ for antibacterial and photocatalytic tile applications. Thermally stable SiO₂‐modified TiO₂ active layer was deposited on Ag⁺‐activated ceramic tiles by spray coating. The results showed that a nearly 100% cleanability degree was detected for SiO₂‐modified TiO₂ (TS)‐coated antibacterial tiles when compared uncoated and unmodified TiO₂‐coated tiles. Antibacterial tests and colorimetric analyses indicated that ceramic tiles provide both antibacterial and photocatalytic properties simultaneously.