Transparency and toughness characterization of epoxy resins modified with liquid chloroprene rubber

Transparent epoxy resins modified with liquid chloroprene rubber (LCR), containing in a category of rubber-toughened resin were found. Transparency and toughness characterization of the modified epoxy resins were investigated as a function of LCR content. Epoxy resins modified with 0–10 vol % LCR showed complete phase-separation microstructure. However, these modified resins were transparent, because the refractive index of LCR was compatible with that of the epoxy resin matrix at room temperature. On the other hand, it was observed that above 10 vol % LCR, a certain amount of LCR dissolved into the epoxy matrix. In this case, the glass transition temperature decreased with increasing LCR content. It was also found that the critical stress intensity factor, K _c, of the modified epoxy resins exhibited a maximum between 10 and 15 vol % LCR.     

Studies on chitin. IX. Crosslinking of water-soluble chitin and evaluation of the products as adsorbents for cupric ion

Water-soluble chitin was successfully crosslinked to varying extents with glutaraldehyde in homogeneous aqueous solutions to improve the properties as an adsorbent for metal cations, and the effects of crosslinking were discussed. Complete insolubilization was achieved with the fivefold excess aldehyde, but, in terms of adsorptivity of Cu²⁺, the chitin crosslinked at an aldehyde/amino group ratio of 1.0 was found to exhibit remarkable capacity and was much superior to others. The desorption of Cu²⁺ from the adsorption complex was also attained effectively at pH 2.0. These results indicated that the loose crosslinking was quite simple and efficient to produce high capacity adsorbents for practical use. Thermal behavior of the crosslinked chitin was examined by TMA and TGA; a softening phenomenon was observed at 145°C.     

Structure of microporous polypropylene sheets containing CaCO3 filler

The microporous polypropylene sheets were prepared by biaxially stretching polypropylene sheets containing CaCO₃ filler (particle size, 0.08–3.0 μm), when the CaCO₃ filler content was 59% by weight and the stretching ratio was 2.8 × 1.8. The microstructure of the sheets were investigated in relation to the CaCO₃ particle size by a N₂ gas permeation method. (1) Effective porosity increases with decreasing mean particle size of filler. (2) The tortuosity factor of the pore is in the range of 25–40 and becomes relatively smaller with decreasing mean particle size of filler. (3) The equivalent pore size becomes relatively smaller with decreasing mean particle size of filler.     

Mechanical alloying in the Al-Bi alloy system

Mechanical alloying (MA) was carried out to investigate the MA behaviour of the immiscible Al-10, 30 at % Bi alloys. After the MA processing, the Al and Bi were finely and homogeneously alloyed. The Bi crystallite size decreased to 25 nm and 30 nm in the Al-10 at % Bi and Al-30 at % Bi alloys, respectively. By increasing the MA time, the hardness increased up to a value of 80 H _v, which is larger than that obtained from the rule of mixtures. The lattice parameter of Bi decreased by about 0.27%, which shows the formation of a non-equilibrium hcp Bi super-saturated solid solution. The extended solubility of Al in Bi was 1.9% in the Al-30 at % Bi alloy. Due to the extended solubility, depression of the melting temperature of hcp Bi was confirmed in the mechanically alloyed Al-Bi alloys. The maximum depression in the temperature was about 10 K. The measured values corresponded well with those estimated from the extrapolation of the solidus line.     

Recovery retardation in equal channel angular pressed Al–Zr alloy during friction stir welding

The effect of Zr on reduction of hardness and microstructure in an FS weld of equal channel angular-pressed Al alloy was investigated. Zr addition to Al suppressed dynamic recovery in the thermomechanically affected zone and enabled retention of the high hardness of the ECA-pressed material throughout the weld.     

Functions and applications of monostable-bistable transition logicelements (MOBILE's) having multiple-input terminals

The MOBILE is a logic gate exploiting the monostable-bistable transition of a circuit that consists of two resonant tunneling transistors connected in series. It has several advantages including multiple inputs and multiple functions. This paper describes the output characteristics of multiple-input MOBILE's and discusses their applications. For a two-input MOBILE, it is demonstrated that both NAND and NOR operations are possible with the appropriate control voltage. This implies the possibility of a variable function logic gate. Furthermore, the threshold logic operations for a weighted sum of input signals are demonstrated for a three-input MOBILE with a weight ratio of 4:2:1. The applications of MOBILE's in parallel processing architectures such as cellular automata and cellular neural networks are discussed based on the above results. Circuit simulations using a simple model of resonant tunneling transistors successfully reproduce the basic characteristics of MOBILE's, and demonstrate the usefulness of MOBILE's in such applications     

Twin-Related Tetragonal Variants in Yttria Partially Stabilized Zirconia

Crystals of yttria partially stabilized zirconia were grown by the arc-image floating-zone technique and studied by transmission electron microscopy. Crystals annealed at 1700°C consist of tetragonal precipitates and a cubic matrix. The platelike domains in a precipitate are twin-related tetragonal variants stacked alternately parallel to the (011) twin plane. The axial relations between the tetragonal precipitate and the cubic matrix are [100]_tetragonal|[100]_cubic, [011]_tetragonal|[011]_cubic.     

Electrical resistivity and Seebeck coefficient of La1−x M x MnO3 (M = Ca,Sr) single crystals

The temperature dependence of the electrical resistivity and Seebeck coefficient was measured on single crystals of La_1–x Ca _x MnO₃(0 <x 0.3) and La_1–x Sr _x MnO 3 (0 <x 0.4) grown by the arc-image floating zone method. The electrical conduction for La_1–x crystals withx 0.2 was of the activation type aboveT _c and of the degenerate type belowT _c, while that for the crystal withx = 0.1 was of the activation type over the whole measured temperature range between –170 and 400°C. The conduction behaviour of La_{1– x} Sr _x MnO₃ was essentially the same as that of La_1–x Ca _x MnO₃ except that the conduction of the crystals withx = 0.3 and 0.4 was of the degenerate type aboveT _c. A distinct difference in Seebeck data was observed between the calcium and the strontium compounds.     

Preparation of spherical fine ZnO particles by the spray pyrolysis method using ultrasonic atomization techniques

An ultrasonic atomizer was used in the spray pyrolysis method to prepare fine, spherical and uniform ZnO particles. Almost spherical particles were obtained successfully which had a mean particle size of 0.15 m and had a very narrow particle size distribution. By using alcohol as the solvent, it was found that the particles do not have hollow shell layers which could usually be observed in the spray pyrolysis process by using water as the solvent. The morphology of the ZnO particles was strongly affected by the concentration of the starting solution.     

Formation of monodispersed Ta2O5 powders

The Ta₂O₅ powders synthesized by the hydrolysis of tantalum pentaethoxide, Ta(OC₂H₅)₅ in alcoholic solution were monodispersed fine oxide particles, which were a uniform, spherical shape, non-agglomerate, and had a narrow size distribution. They grew to 1.2m after ageing for 1 h after hydrolysis. Powder X-ray diffraction and differential thermal analysisthermogravimetric analysis showed the particles were amorphous and hydrated. These particles lost the water at 290° C and gave well-crystalline Ta₂O at 740° C. Throughout these thermal processes, the particle morphology was kept almost the same.