Current advances concerning the most cited metal ions doped bioceramics and silicate-based bioactive glasses for bone tissue engineering

Studies related to biomaterials that stimulate the repair of living tissue have increased considerably, improving the quality of many people's lives that require surgery due to traumatic accidents, bone diseases, bone defects, and reconstructions. Among these biomaterials, bioceramics and bioactive glasses (BGs) have proved to be suitable for coating materials, cement, scaffolds, and nanoparticles, once they present good biocompatibility and degradability, able to generate osteoconduction on the surrounding tissue. However, the role of biomaterials in hard tissue engineering is not restricted to a structural replacement or for guiding tissue regeneration. Nowadays, it is expected that biomaterials develop a multifunctional role when implanted, orchestrating the process of tissue regeneration and providing to the body the capacity to heal itself. In this way, the incorporation of specific metal ions in bioceramics and BGs structure, including magnesium, silver, strontium, lithium, copper, iron, zinc, cobalt, and manganese are currently receiving enhanced interest as biomaterials for biomedical applications. When an ion is incorporated into the bioceramic structure, a new category of material is created, which has several unique properties that overcome the disadvantages of primitive material and favors its use in different biomedical applications. The doping can enhance handling properties, angiogenic and osteogenic performance, and antimicrobial activity. Therefore, this review aims to summarize the effect of selected metal ion dopants into bioceramics and silicate-based BGs in bone tissue engineering. Furthermore, new applications for doped bioceramics and BGs are highlighted, including cancer treatment and drug delivery.     

Development of low-alcohol isotonic beer by interrupted fermentation

Alcohol-free beer with isotonic properties is getting more popular and its production can be carried out by different production strategies; however, interrupted fermentation is still a challenge. Therefore, the objective of this study was to develop a low-alcohol isotonic beer (<0.5% v/v) by interrupted fermentation. Moreover, the major objective is to compare the developed product to commercial beverages (sports drinks, ‘Pilsen' regular beer, alcohol-free beers and low-alcohol isotonic beer). The beverages were evaluated based on pH, alcohol content (% v/v), total titratable acidity (mEq L⁻¹), osmolality (mOsmol kg⁻¹), bitterness International Bitterness Units, colour European Brewery Convention, total phenolic compounds (mg L⁻¹ gallic acid), reducing and total sugars (%) and Na and K contents (mg L⁻¹). The developed low-alcohol isotonic beer presented characteristics similar to sports drinks, with the advantage of being richer in phenolic compounds and suitable osmolality. Despite salts were added in its formulation, the grades attributed to all beers employed in the sensory evaluation, as well as the purchase intention did not present significant differences.     

Recent Biophysical Issues About the Preparation of Solute-Filled Lipid Vesicles

Here we report some recent biophysical issues on the preparation of solute-filled lipid vesicles and their relevance to the construction of “synthetic cells.” First, we introduce the “semi-synthetic minimal cells” as the liposome-based cell-like systems, which contain a minimal number of biomolecules required to display simple and complex biological functions. Next, we focus on recent aspects related to the construction of synthetic cells. Emphasis is given to the interplay between the methods of synthetic cell preparation and the physics of solute encapsulation. We briefly introduce the notion of structural and compositional “diversity” in synthetic cell populations.     

Barium titanate‐based nanodielectrics of two chemically recyclable thermosets

In this work was investigated the effect of the addition of barium titanate (BaTiO₃) on electrical properties of two chemically recyclable thermosets, polyhemiaminal (PHA) and polyhexahydro‐s‐triazine (PHT), both fabricated from 4,4′‐oxydianiline (ODA), an ether derivative of aniline and paraformaldehyde. Thermal and mechanical properties as well as chemical recyclability of the two polymers and their nanocomposites/nanodielectrics were also investigated. In addition, a quantitative analysis was conducted of the nanoparticle dispersion in the PHA‐/PHT‐based BaTiO₃‐containing nanocomposites using transmission electron microscopy imaging and the nearest‐neighbor distance index and this index was used to analyze the investigated properties in connection with the proper mechanisms. Regarding the electrical properties for both neat polymers, conductivity values of the order of 10^?8 S m^?1 at 100 Hz were observed and dielectric constant values close to 2.80 for both polymers at 1 kHz. The addition of 0.5 wt% of BaTiO₃ ferroelectric nanoparticles increased by about 44% the dielectric constant (1 kHz) and conductivity (10² Hz) of the PHA‐based nanocomposite. PHA and PHT exhibited glass transition temperature (T_g) values in the range 125–180 °C. An increase of 7 °C in T_g was observed after the incorporation of 0.5 wt% of BaTiO₃ into PHA. Concerning the mechanical properties, values in the range 4.00–4.45 GPa for reduced modulus and 0.30–0.43 GPa for nanohardness for PHA and PHT polymers were observed. Independently of filler content or polymer matrix, both mechanical properties were enhanced after the addition of BaTiO₃. The chemical recycling of PHA/PHT and all nanocomposites in the initial ODA reagent after sulfuric acid treatment was successfully characterized using the NMR and Fourier transform infrared spectroscopic techniques. © 2018 Society of Chemical Industry     

Electrospun microporous gelatin–polycaprolactone blend tubular scaffold as a potential vascular biomaterial

The work reported involved the fabrication of an electrospun tubular conduit of a gelatin and polycaprolactone (PCL) blend as an adventitia‐equivalent construct. Gelatin was included as the matrix for increased biocompatibility with the addition of PCL for durability. This is contrary to most of the literature available for biomaterials based on blends of gelatin and PCL where PCL is the major matrix. The work includes the assiduous selection of key electrospinning parameters to obtain smooth bead‐free fibres with a narrow distribution of pore size and fibre diameter. Few reports elucidate the optimization of all electrospinning parameters to fabricate tubular conduits with a focus on obtaining homogeneous pores and fibres. This stepwise investigation would be unique for the fabrication of gelatin–PCL electrospun tubular constructs. The fabricated microfibrous gelatin–PCL constructs had pores of size ca 50–100 μm reportedly conducive for cell infiltration. The measured value of surface roughness of 57.99 ± 17.4 nm is reported to be favourable for protein adhesion and cell adhesion. The elastic modulus was observed to be similar to that of the tunica adventitia of the native artery. Preliminary in vitro and in vivo biocompatibility tests suggest safe applicability as a biomaterial. Minimal cytotoxicity was observed using MTT assay. Subcutaneous implantation of the scaffold demonstrated acute inflammation which decreased by day 15. The findings of this study could enable the fabrication of smooth bead‐free microfibrous gelatin–PCL tubular construct as viable biomaterial which can be included in a bilayer or a trilayer scaffold for vascular tissue engineering. © 2019 Society of Chemical Industry     

Biodegradation of poly(lactic acid)—cassava bagasse composites produced by injection molding

Neat poly (lactic acid) (PLA) and PLA/cassava bagasse (CB) composites were used to produce seedling tubes by extrusion and injection molding. The tubes were buried in simulated soil, and their biodegradation was investigated by weight loss, scanning electron microscopy (SEM), and Fourier transform infrared spectroscopy (FTIR). After 180 days, the composites' biodegradation was higher than neat PLA material, and the higher the CB content, the higher the biodegradation, which caused fissures and voids in the material. The biodegradation of PLA/CB composites increased the phosphorus content in the soil after 180 days. Composites of PLA with CB, an abundant agro-industrial residue in Brazil, are promising because they can reduce the environmental impact due to CB's proper destination, and the composites' costs and biodegradation are faster than pure PLA material. Both the faster biodegradation of the tube and the higher P content are advantageous for seedling tubes.     

Polyetherimide-LaNi5 composite films for hydrogen storage applications

This study investigates the preparation of polyetherimide (PEI) – LaNi₅ composites films for hydrogen storage. Prior to the polymer addition, LaNi₅ was ball-milled at different conditions (250, 350, and 450 RPM) and annealed at 500 °C for 1 h under vacuum. The composites were produced with BM-LaNi₅-350 (PEI/LaNi₅-350) and annealed BM-LaNi₅-350 (PEI/LaNi₅-350-TT). Membranes were successfully produced through solvent casting assisted by an ultrasonic bath. The particles dispersion and the film morphology did not change after hydrogenation cycles. In the H₂ sorption experiments at 43 °C and 20 bar, the films stored H₂ without incubation time; both samples reached a capacity of ~0.6 wt%. The H₂ sorption kinetics of PEI/LaNi₅-350 was comparable to that of BM-LaNi₅-350, whereas PEI/LaNi₅-350-TT presented significantly slower kinetics. LaNi₅ oxidation was hindered by PEI, showing that it can be explored to improve metal hydrides air resistance. The results demonstrated that PEI films filled with LaNi₅ are promising materials for hydrogen storage.