A biocompatible heterogeneous hydrogel of poly[N-(2-hydroxypropyl) methacrylamide] (PHPMA) showing an open porous structure, viscoelastic properties similar to the neural tissue and a large surface area available for cell interaction, was evaluated for its ability to promote tissue repair and axonal regeneration in the transected rat spinal cord. After implantation, the polymer hydrogel could correctly bridge the tissue defect, from a permissive interface with the host tissue to favour cell ingrowth, angiogenesis and axonal growth occurred within the microstructure of the network. Within 3 months the polymer implant was invaded by host derived tissue, glial cells, blood vessels and axons penetrated the hydrogel implant. Such polymer hydrogel matrices which show neuroinductive and neuroconductive properties have the potential to repair tissue defects in the central nervous system by promoting the formation of a tissue matrix and axonal growth by replacing the lost of tissue. 相似文献
Drop deformation and breakup were investigated in the presence of a block copolymer in step-wise simple shear flow using a home-made Couette cell connected to an Anton Paar MCR500 rheometer. Polyisobutylene (PIB) was used as the matrix, while five different molecular weights of polydimethylsiloxane (PDMS) were selected to provide drops with a relatively wide range of viscosity ratio. A block copolymer made of PDMS-PIB was used for interfacial modification of the drop-matrix system. The copolymer concentration was 2 wt% based on the drop phase. The experiments consisted in analyzing the drop shape and measuring the variation of the length to diameter ratio, L/D, both in steady state and in transient regimes till breakup. This allowed revising of the classical Grace curve that reports the variation of the critical capillary number for breakup as a function of viscosity ratio and providing also a new one for blends compatibilized with an interfacial active agent with a given molecular weight. 相似文献
Summary: Poly(butylene succinate‐co‐adipate) (PBSA) and organically modified montmorillonite (OMMT) nanocomposites of three different compositions were prepared by melt‐extrusion in a batch mixer. The structure of the nanocomposites was studied using X‐ray diffraction (XRD) and transmission electron microscopy (TEM) that revealed a coexistence of exfoliated and intercalated silicate layers dispersed in the PBSA matrix, regardless of the silicate loading. The degree of crystallinity of PBSA decreases with the addition of OMMT platelets. Dynamic mechanical analysis revealed remarkable increase in flexural storage modulus when compared with that of neat PBSA. Tensile property measurements exhibit substantial increase in stiffness with simultaneous increase in elongation at break of nanocomposites as compared to that of neat PBSA. The effect of clay loading on the melt‐state linear viscoelastic behavior of mixed intercalated/exfoliated nanocomposites was also investigated.
Elongation at break of compression molded annealed samples of neat PBSA and various PBSACNs. 相似文献
The role of organically modified layered silicate as a compatibilizer for immiscible polystyrene (PS) with polypropylene (PP) or polypropylene grafted with maleic anhydride (PP-g-MA) blends was investigated. Scanning electron micrographs (SEM) revealed efficient mixing of the polymers in the presence of organically modified layered silicate. X-ray diffraction (XRD) patterns and transmission electron microscopic (TEM) observations showed that silicate layers were either intercalated or exfoliated, depending on their interactions with the polymer pair, and were located at the interface between the two polymers. The compatibilizing action of the organically modified layered silicate resulted in a decrease in interfacial tension and particle size and in a remarkable increase in mechanical properties of the modified immiscible blends. 相似文献
The main objective of the present work was to tailor a new thermoplastic vulcanisate (TPV) composed of PA 12 as the thermoplastic phase and PDMS as the rubber phase. The PDMS was crosslinked by dicumyl peroxide (DCP). Interestingly, addition of 2,2,6,6‐tetramethylpiperidinyloxyl (TEMPO) to the TPV provided the compatibilization of the PA12/PDMS blend in the dynamic process and gave a new material with control structure and morphology. The electron microscopy (SEM and TEM) studies revealed that adding silica nanoparticles and Lotader in PA12 and PDMS phases, respectively, led to a drastic reduction in Rv of the PDMS particles from 16.5 µm (virgin blend) to nearly 0.6 µm for the PA12/PDMS reactive blend. Therefore, a stable co‐continuous morphology was obtained for the new TPV based on 60–40 wt.‐% of PDMS‐PA12 blend.