The present article reports the investigation of the effects of surrounding brightness on a visual search for three safety colors: red, orange, and yellow. Images of visual stimuli consisting of an array of colored circles placed on a large visual field (a visual angle of 40°) were displayed on an 80‐in. screen with a DLP projector. Experiment I examined the search efficiency under three levels of background luminance that were equivalent to the three target luminances. The results showed that the search efficiency for the orange target decreased as the number of distractors increased, under each of the background luminance levels, whereas the efficiency scarcely decreased for the red and yellow targets. Although a reduction in background luminance increased the search efficiency for the orange target, it is suggested that the effect of background luminance is smaller than the effect of the target color in search efficiency. Experiment II examined the search efficiency under three conditions of low levels of incident illuminance, which were matched with a linear regression to the luminance of color chips of safety colors measured twilight conditions. The results showed that the search efficiency for the orange target decreased as the number of distractors increased under each of the different illuminance conditions, whereas the efficiency scarcely decreased for red and yellow targets. Furthermore, as illuminance decreased, the search time for the orange target was more greatly impacted than for red or yellow. These results imply that the recognition of orange tends to be influenced by the surrounding brightness. © 2005 Wiley Periodicals, Inc. Col Res Appl, 30, 400–409, 2005; Published online in Wiley InterScience (www.interscience.wiley.com). DOI 10.1002/col.20152     

Simple and modified rule of mixtures of deformation parameters in stage III of single ductile fibre-ductile matrix composites

By employing a single thick molybdenum fibre-copper matrix composite with very weak interfacial bonding, it was confirmed that flow stress, internal stress, effective stress and change in flow stress due to change in strain rate of the composite obey the simple rule of mixtures; strain-hardening exponent, stress exponent of strain rate, effective stress exponent of dislocation velocity and activation volume obey the modified rule of mixtures in the whole range of plastic deformation of the composite. This means that the inherent features of the fibre in the present composite were conserved beyond the failure strain of the fibre tested alone, and the above deformation parameters of the composite were, to a first approximation, determined by the inherent parameters of the fibre and the matrix.     

66/77-kV C-GIS using composite insulation in SF6 gas

A second-generation model of cubicletype gas-insulated switchgear (C-GIS) with composite insulation incorporating SF₆ gas has been developed. The design does not require a gas process in field assembly; it has high reliability and its installation is more rapid; and a further reduction in size is achieved. The design principles are described in detail.     

FDTD analysis of switching characteristics in magnetooptic functional devices using magnetostatic surface waves

Collinear magnetooptic interaction with magnetostatic surface waves (MSSW) can be used for wavelength‐selective switches, wavelength filters, and frequency shifters in wavelength‐division‐multiplexed (WDM) photonic networks and optical processing systems. The switching efficiency can be improved with a multilayer waveguide structure. To investigate the dynamic switching characteristics, the FDTD method was employed. The mode conversion between TE and TM mode was successfully demonstrated with FDTD simulation. The filtering characteristics were also evaluated. The FDTD results were compared with the result from the coupled mode theory, and good agreement was obtained. Switching of an optical pulse was also demonstrated by the FDTD method. © 2007 Wiley Periodicals, Inc. Electr Eng Jpn, 162(1): 40–47, 2008; Published online in Wiley InterScience ( www.interscience.wiley.com ). DOI 10.1002/eej.20501     

The integral experiment on beryllium with D-T neutrons for verification of tritium breeding

A clean benchmark experiment on beryllium was performed with D-T neutrons at the FNS facility of the Japan Atomic Energy Agency. The main objective was to verify the integral data related to the tritium production on lithium isotopes. Tritium production rates, as well as activation reaction rates were measured inside the beryllium assembly that was shaped as a pseudo-cylindrical slab with an area-equivalent diameter of 628 mm and a thickness of 355 mm. Experimental results were analyzed with a three-dimensional Monte Carlo transport code MCNP-4C and FENDL/MC-2.0, JENDL-3.2/3.3 neutron transport libraries. Evaluation of reaction rates was based on the cross section data taken from the JENDL Dosimetry File and ENDF B-VI data libraries. Analysis shows that all calculation combinations (transport and activation cross section libraries) used for evaluation of reaction rates give data that is agreeable with measured values within 10%.     

Twin-Related Tetragonal Variants in Yttria Partially Stabilized Zirconia

Crystals of yttria partially stabilized zirconia were grown by the arc-image floating-zone technique and studied by transmission electron microscopy. Crystals annealed at 1700°C consist of tetragonal precipitates and a cubic matrix. The platelike domains in a precipitate are twin-related tetragonal variants stacked alternately parallel to the (011) twin plane. The axial relations between the tetragonal precipitate and the cubic matrix are [100]_tetragonal|[100]_cubic, [011]_tetragonal|[011]_cubic.     

Effect of Silicon Dioxide on the Thermal Diffusivity of Aluminum Nitride Ceramics

The thermal diffusivity of AlN ceramics was significantly decreased by the addition of SiO₂. The AlN ceramics with 4 wt% SiO₂ could not be densified by pressureless sintering in the temperature range 1400° to 1800°C. The thermal diffusivity of these samples was very low because of their porous structure. The AlN ceramics containing 2, 4, and 8 wt% SiO₂ were densified by hot-pressing and also had low thermal diffusivity. In these samples, the grains of the 27R polytype that resulted from the reaction between AlN and SiO₂ were dispersed, obstructing the conduction of heat. The relation between the amount of 27R polytype and the thermal diffusivity of the AlN ceramics was determined.     

Fibrous support for immobilization of enzymes

A poly(vinyl alcohol) (PVA) fiber support incorporating various aminoacetal functional groups has been developed for immobilizing enzymes. The aminated PVA fiber seems to adsorb enzymes with electrostatic force of attraction; thus the immobilization procedure is simple. By the use of this fiber having immobilized enzymes, the reaction between enzymes and substrates is nearly independent of the size of subtstrates. This newly developed type of fiber, which is formed by a mass superfine fibers (SFF), each measuring 1 μm or less in diameter, permits much more increased surface area than the conventional enzyme immobilization supports. Our studies of the properties of the fiber for immobilization of enzymes show the following results: (1) SFF has a greater ability for the immobilization of invertase than ordinary fibers; (2) dimethyl-aminated SFF has the best performance for the immobilization of invertase. From these results, it is concluded that the dimethyl-aminated SFF is an excellent support for the immobilization of invertase.     

Local disturbances preceding a running crack front in a viscoelastic solid

The local disturbances ahead of a running crack front in a viscoelastic solid were measured through noncontact electro-optical tools. It was observed that the very high local strain rate up to 200/sec exists even in the present quasistatic loading case. It may be concluded that the running crack propagation velocities, not the conventional average strain rates ranging from about 10^?4/sec to 10^?2/sec, govern the local disturbances, as the crack propagation velocities always exceed 200m/sec for both average strain rates, while the local strain rates observed do not show much differences between both average strain rate cases.     

Prooxidant effects of inorganic chromium compounds in the autoxidation of methyl linoleate

The prooxidant property of inorganic chromium compounds was determined in methyl linoleate free from natural antioxidants and metals. Prooxidant properties of inorganic chromium compounds appeared in order of sodium chromate > chromium (VI)-oxide > chromium chloride > potassium chromate > chromium (III)-oxide > potassium dichomate. In comparison with the control, additions of chromium compounds induced different amounts of autoxidation products derived from methyl linoleate, such as small amounts of hydroperoxides and conjugated dienes and large amounts of hydroxy groups,α,β,γ,δ-unsaturated carbonyls, isolatedtrans double bonds, polymers, and free radicals. From these analytical data, the catalysis of chromium compounds in the autoxidation of methyl linoleate seemed to be based on their abilities of abstracting a hydrogen from methyl linoleate and decomposing hydroperoxides derived from the autoxidation of methyl linoleate.