Phase fluctuations of cross-polarized signals at 4 GHz in fine weather on earth-space paths

On an earthspace propagation path with the low elevation angle of 10 deg, the phase between co- and crosspolar signals occasionally showed rapid and irregular fluctuations during fine weather. These fluctuations were generally significant during the daytime, and were strongly in phase with the occurrence of the copolar amplitude scintillations. This could be attributed to the combined effects of the crosspolar phase pattern of the receiving antenna and small fluctuations of the angle of arrival of the radiowaves.     

High-efficiency finishing process for metal mold by large-area electron beam irradiation

A new finishing process for metal molds by large-area electron beam (EB) irradiation is proposed in this study. In the large-area EB irradiation equipment used here, an EB with high-energy density is irradiated without focusing the beam, and so the EB with a maximum diameter of 60 mm can be used for melting or evaporating metal surface instantly. Experimental results show that the surface roughness decreases from 6 μmRz to less than 1 μmRz in just a few minutes under proper machining conditions. The corrosion resistance of metal mold surface also could be greatly improved by large-area EB irradiation. Furthermore, the surface roughness of tilting surface close to 90° could be well improved. Therefore, large-area EB irradiation method has a possibility to become a high-efficiency finishing process for metal molds.     

Extensions of polyacrylic acid ammonium salts in the adsorption layer to fluidize alumina slurries

An average shell volume occupied in the adsorption layer on alumina by a polyacrylic acid ammonium salts molecule (PAA) defined as the average area occupied by an adsorbed PAA on alumina multiplied by the average thickness of the water layer at the limit of thickening, has been calculated from the adsorbed amount of PAA and from the flow points of alumina in the presence of PAA of different molecular weights. A steric effect of the PAA dispersant on the dispersion of alumina resulted in a flow with no yield stress. This was due to the change of the extension of PAA in the adsorption shell from a sphere to an ellipsoid with a long axis which exceeded the effective distance that the van der Waals attraction force reaches at a molecular weight for the PAA of between 10 000–20 000.     

Hydroliquefaction of low-sulfur coals using iron carbonyl complexes—Sulfur as catalysts

Hydroliquefaction of low-sulfur Australian coals (Wandoan and Yallourn) was studied using iron carbonyl complexes as catalyst. The addition of Fe(CO)₅ (2.8 wt% Fe of coal) increased coal conversion from 48.6 to 85.2% for Wandoan coal, and from 36.7 to 69.7% for Yallourn coal in 1-methylnaphthalene at 425°C under an initial hydrogen pressure of 50 kg cm^?2. When molecular sulfur was added to iron carbonyls (Fe(CO)₅, Fe₂(CO)₉ and Fe₃(CO)₁₂), higher coal converions ( > 92%) and higher oil yields (>46%) were obtained, along with an increase in the amount of hydrogen transferred to coal from the gas phase (0.2 to 2.8%, d.a.f. coal basis). In the liquefaction studies using a hydrogen donor solvent, tetralin, Fe(CO)₅S catalyst increased the amount of hydrogen absorbed from the gaseous phase and decreased the amount of naphthalene dehydrogenated from tetralin. The direct hydrogen transfer reaction from molecular hydrogen to coal fragment radicals seems to be a major reaction pathway. Organic sulfur compounds, dimethyldisulfide and benzothiophene, and inorganic FeS₂ and NiS were found to be good sulfur sources to Fe(CO)₅. From X-ray diffraction analyses of liquefaction residues, it is concluded that Fe(CO)₅ was converted into pyrrhotite (Fe_1?xS) when sulfur was present, but into Fe₃O₄ in the absence of sulfur.     

Radiation damage induced in Si photodiodes by high-temperature neutron irradiation

Results are presented of a detailed study of the effects of high-temperature 4-MeV neutron irradiation on the performance degradation of Si pin photodiodes together with the radiation-induced defects, observed by deep level transient spectroscopy (DLTS). It was found that the dark current increases after irradiation, while the photocurrent decreases. After irradiation, two majority electron capture levels with (E _c–0.22 eV) and (E _c–0.40 eV) were induced in the n-Si substrate, while one minority hole capture level with (E _v+0.37 eV) was found. Additionally, the degradation of the device performance and the introduction rate of the lattice defects decreases with increasing irradiation temperature. For a 250 °C irradiation, the reduction of the reverse current is only 20% of the starting value. This result suggests that the creation and recovery of the radiation damage proceeds simultaneously at high temperatures.     

Effects of partial recrystallization on high-cycle fatigue deformation and crack generation of a nitrogen-strengthened 32Mn-7Cr austenitic steel at liquid-nitrogen temperature

To achieve higher fatigue resistance against subsurface crack generation, both the refinement of grain structure and the introduction of mobile dislocations on various slip systems have been shown to be effective in the 32Mn-7Cr austenitic steel. A novel treatment which consisted of cold grooved rolling and partial recrystallization was introduced to modify the microstructure. High-cycle fatigue properties and fatigue-crack generation were investigated for both the solution-treated (ST) and the partially recrystallized (PR) materials at 77 K. The PR material displayed higher fatigue strength than the ST material, especially in the high-cycle regime. No subsurface crack generation was detected for the PR material; however, it appeared in the lower peak stress and/or in the longer-life range for the ST material. Intergranular facets formed a subsurface crack initiation site in the ST material. Since the dislocation structure that developed in the fatigued PR material assisted homogeneous and multidirectional plastic deformation, the localized deformation and/or the stress concentration at the grain boundaries by coplanar arrays were believed to be relieved. Therefore, intergranular cracking due to incompatibility at a grain boundary may disappear.     

Present status and future prospects of PV activities in Japan

The photovoltaic (PV) power systems in Japan made great strides in the past decade. The PV industry in the 1990s greatly depended on the research projects and dissemination programs carried out by the Ministry of International Trade and Industry. However, the industrial structure for full-scale deployment of the PV system is currently being established by the manufacturers’ continuous efforts to reduce the PV system cost and the government’s consecutive supports to create the initial market. It is expected that the synergetic effect of the cost reduction and incentives for introduction will activate the PV industry and its market more and more toward achieving 5000 MW of the capacity in FY 2010.     

Preparation of spherical fine ZnO particles by the spray pyrolysis method using ultrasonic atomization techniques

An ultrasonic atomizer was used in the spray pyrolysis method to prepare fine, spherical and uniform ZnO particles. Almost spherical particles were obtained successfully which had a mean particle size of 0.15 m and had a very narrow particle size distribution. By using alcohol as the solvent, it was found that the particles do not have hollow shell layers which could usually be observed in the spray pyrolysis process by using water as the solvent. The morphology of the ZnO particles was strongly affected by the concentration of the starting solution.     

Ring hydrogenation of naphthalene and 1-naphthol over supported metal catalysts in supercritical carbon dioxide solvent

Catalytic ring hydrogenations of naphthalene and 1-naphthol were studied over several supported metal catalysts in supercritical carbon dioxide solvent at low temperature. Higher concentration of hydrogen in supercritical carbon dioxide and lower reaction temperature were responsible for higher catalyst activity and selectivities to the desired partial ring hydrogenated products as compared with those observed in organic solvent for the same catalyst.