Structural and Electrical Properties of Ag/<Emphasis Type="Italic">n</Emphasis>-TiO<Subscript>2</Subscript>/<Emphasis Type="Italic">p</Emphasis>-Si/Al Heterostructure Fabricated by Pulsed Laser Deposition Technique

We have investigated the structural and electrical characteristics of the Ag/n-TiO₂/p-Si/Al heterostructure. Thin films of pure TiO₂ were deposited on p-type silicon (100) by optimized pulsed laser ablation with a KrF-excimer laser in an oxygen-controlled environment. X-ray diffraction analysis showed the formation of crystalline TiO₂ film having a tetragonal texture with a strong (210) plane as the preferred direction. High purity aluminium and silver metals were deposited to obtain ohmic contacts on p-Si and n-TiO₂, respectively. The current–voltage (I–V) characteristics of the fabricated heterostructure were studied by using thermionic emission diffusion mechanism over the temperature range of 80–300 K. Parameters such as barrier height and ideality factor were derived from the measured I–V data of the heterostructure. The detailed analysis of I–V measurements revealed good rectifying behavior in the inhomogeneous Ag/n-TiO₂/p-Si(100)/Al heterostructure. The variations of barrier height and ideality factor with temperature and the non-linearity of the activation energy plot confirmed that barrier heights at the interface follow Gaussian distributions. The value of Richardson’s constant was found to be 6.73 × 10⁵ Am^?2 K^?2, which is of the order of the theoretical value 3.2 × 10⁵ Am^?2 K^?2. The capacitance–voltage (C–V) measurements of the heterostructure were investigated as a function of temperature. The frequency dependence (Mott–Schottky plot) of the C–V characteristics was also studied. These measurements indicate the occurrence of a built-in barrier and impurity concentration in TiO₂ film. The optical studies were also performed using a UV–Vis spectrophotometer. The optical band gap energy of TiO₂ films was found to be 3.60 eV.     

Synthesis and structure-activity relationship of the isoindolinyl benzisoxazolpiperidines as potent,selective, and orally active human dopamine D4 receptor antagonists

A new class of potent dopamine D(4) antagonists was discovered with selectivity over dopamine D(2) and the alpha-1 adrenoceptor. The lead compound was discovered by screening our compound collection. The structure-activity relationships of substituted isoindoline rings and the chirality about the hydroxymethyl side chain were explored. The isoindoline analogues showed modest differences in potency and selectivity. The S enantiomer proved to be the more potent enantiomer at the D(4) receptor. Several analogues with greater than 100-fold selectivity for D(4) over D(2) and the alpha-1 adrenoreceptor were discovered. Several selective analogues were active in vivo upon oral or intraperitoneal administration. A chiral synthesis starting from either D- or L-O-benzylserine is also described.     

The physical character of coal char formed during rapid pyrolysis at high pressure

Rapid pyrolysis was conducted in a drop tube reactor using seven coals under various operating conditions. In addition to dense char, porous chars (network char and cenospheric char) were formed by the rapid pyrolysis under certain conditions. Porous char was mainly composed of film-like carbon and skeleton carbon. The pyrolyzed coal char particles were characterized in detail. Morphology and bulk density of porous char were quite different from the dense char formed under the same conditions, but elemental composition and BET surface area were similar to each other. CO₂ gasification reactivity of porous char was lower than dense char in the later gasification stage, and this was ascribed to the low reactivity of skeleton carbon.     

Synthesis of highly pure and dense 0.9(KNbO3)-0.1(BaNi1/2Nb1/2O3-δ) ceramic with superior magnetic properties

Residual NiO phase is generally detected in 0.9(KNbO₃)–0.1(BaNi_1/2Nb_1/2O_3-δ) (KBNNO) synthesized using NiO as a nickel precursor by solid-state reaction. In this work, NiO phase is found to exist in the form of the residual NiO particles with a size of 100-200 nm using energy dispersive X-ray elemental mapping. These NiO residual particles are eliminated by using nickel acetate as a nickel precursor and a 100% perovskite phase KBNNO is successfully synthesized at as low as 600°C temperature. Furthermore, using the two-step sintering technique, 100% relative density is achieved in this material. The nickel acetate–based KBNNO shows a robust ferromagnetism with the saturation magnetization of 11.42 memu/g and the remanent magnetization of 3.89 memu/g which is 38 times higher than that of previously reported value in NiO-based KBNNO. Thus, a highly pure and fully dense KBNNO ceramic with superior magnetic properties is obtained using nickel acetate and by the two-step sintering method. This is a key step forward in the processing of KBNNO and is likely to have a significant impact on other physical properties of this newly invented and promising photovoltaic perovskite material.     

Novel anhydrous composite membranes based on sulfonated poly (ether ketone) and aprotic ionic liquids for high temperature polymer electrolyte membranes for fuel cell applications

Novel composite membranes were prepared using imidazolium type aprotic ionic liquids and sulfonated poly (ether ketone) (SPEK) as polymer matrix by solution casting process. All the prepared membranes were characterized for their thermal stability, mechanical properties, ion exchange capacity, proton conductivity and leaching out of ionic liquids in presence of water. Ionic liquid based membranes were more flexible than neat SPEK membrane due to the plasticization effect of ionic liquids. The interactions and compatibility occurring among components were investigated by vibration spectroscopy (FTIR ATR) and scanning electron microscopy respectively. The thermal stability of composite membranes was higher than unmodified membranes. The ion conductivity of composite membranes under anhydrous conditions was found to be dependent on temperature, type and concentration of ionic liquid in SPEK matrix. Ion conductivities of composite membranes under anhydrous condition were found to be up to two orders (∼100 times) higher than neat SPEK membrane and it was found to be ∼5 mS/cm at 140 °C for SPEK/OTf-70. These composite membranes can be successfully operated at temperatures ranging from 40 °C to 140 °C under anhydrous conditions.     

Preparation of Au nanoparticles by Q switched laser ablation and their application in 4-nitrophenol reduction

Clean Technologies and Environmental Policy - This work reports the fabrication of Au nanoparticles (NPs) by laser ablation of a gold metal plate immersed in water in the absence of stabilizing...     

Laser-assisted preparation of C3N4/Fe2O3/Au nanocomposite: a magnetic reusable catalyst for pollutant degradation

Clean Technologies and Environmental Policy - Assorted common contaminants namely organic dyes and nitro compounds are generated by various industries and have caused alarming problems for the...     

Experimental Investigation and optimization of Process Parameters for Shear Strength of Compound Cast Bimetallic Joints

Joining of A356 alloy and magnesium was carried out by vacuum assisted sand mold compound casting process. Microstructure at the joint interface was studied by using optical microscope, scanning electron microscope, energy dispersive X-ray spectroscopy and X-ray diffractometer. Characterization indicated that a relatively uniform joint interface was obtained. The joint interface was composed of three distinct layers containing Mg₂Al₃ on aluminum side, Mg₁₇Al₁₂?+?δ eutectic structure on magnesium side and Mg₁₇Al₁₂ as middle layer. As a result of interaction between silicon, present in A356 with magnesium, Mg₂Si compound was formed. Push out test was conducted on electronics universal testing machine to measure the shear strength across the joint interface. The important process parameters (grit size of sand paper, insert temperature, pouring temperature and vacuum pressure) were optimized to maximize the shear strength. Optimization was carried out by using response surface methodology, desirability analysis and genetic algorithm (GA) techniques. It was observed that the shear strength increased by 14.21, 8.60 and 4.80% with genetic algorithm, desirability analysis and regression model respectively. GA reported the optimal value of shear strength.