Fabrication of lotus-type porous carbon steel by the continuous zone melting method and its mechanical properties

A lotus-type porous carbon steel with cylindrical pores was fabricated by the continuous zone melting method in a pressurized mixture of hydrogen and helium gases. The porosity increases with increasing partial pressure of the hydrogen gas, while the pore diameter remains almost constant, independent of the pressure. The ultimate tensile strength of the specimen with cylindrical pores parallel to the tensile direction is lower than the estimated value, assuming that the strength is decreased in proportion to the decrease of the cross-sectional area of the specimen, while the yield strength is higher than the estimated value. The compressive yield strength is also higher than the estimated value. The increase in yield strength is considered to be due to precipitation strengthening. The tensile strength is increased by quenching and tempering, while the elongation decreases. Such mechanical properties are discussed in terms of the microstructural analysis.     

Effects of surface charge, micro-bubble size and particle size on removal efficiency of electro-flotation.

Flotation is a water treatment alternative to sedimentation, and uses small bubbles to remove low-density particles from potable water and wastewater. The effect of zeta potential, bubble size and particle size on removal efficiency of the electro-flotation process was investigated because previous model-simulations indicated that these attributes are critical for high collision efficiency between micro-bubbles and particles. Solutions containing Al3+ as the metal ion were subjected to various conditions. The zeta potentials of bubbles and particles were similar under identical conditions, and their charges were influenced by metal ion concentration and pH. Maximum removal efficiency was 98 and 12% in the presence and absence of flocculation, respectively. Removal efficiency was higher when particle size was similar to bubble size. These results agree with modelling simulations and indicate that collision efficiency is greater when the zeta potential of one is negative and that of the other is positive and when their sizes are similar.     

Spectral shape tunable band-rejection filter using a long-period fiber grating with divided coil heaters

We have developed a new type of tunable band rejection filter, which provides high spectral-shaping flexibility in a wide tuning range. The filter consists of a long-period fiber grating (LPFG) with divided coil heaters. Each of the divided coil heaters is controlled individually to adjust a temperature distribution along the LPFG and to modify the spectral shape of the LPFG filter. The tunable band rejection filter is demonstrated to function properly when applied as an erbium-doped fiber amplifier gain-flattening filter.     

Comparison of total and faecal coliforms as faecal indicator in eutrophicated surface water.

The aim of this study was to evaluate the use of total coliforms (TC) and faecal coliforms (FC) using a membrane filtration method for precise monitoring of faecal pollution in Korean surface water. The samples were collected in Korea from both main rivers and their tributaries. Presumptive TC * FC were enumerated. The ratios of presumptive FC to TC were not constant, but varied widely, and TC were difficult to enumerate because of overgrowth by background colonies. For FC this was not the case. Seven hundred and three purified strains of presumptive TC * FC and their background colonies were biotyped using API 20E. Among 272 presumptive TC, non-faecal related species, Aeromonas hydrophila dominated (34.6%) and E. coli accounted for only 5.1%. In contrast, E. coli made up 89% of the 209 presumptive FC. Furthermore, of 164 background colonies on Endo Agar LES, 54.9% was A. hydrophila, while background colonies on m-FC Agar were few (58 strains), and despite their atypical colony appearance, most of them were biotyped as enteric bacteria. These results reveal that the detection of FC rather than TC using m-FC Agar is more appropriate for faecal pollution monitoring in eutrophicated surface water located in a temperate region.     

Inhibition effect of carbon dioxide on the oxidation of hydrogen over a platinum foil catalyst

This paper investigates the catalytic ignition of the H₂/O₂/CO₂ mixture on platinum in a stagnation flow at atmospheric pressure experimentally and numerically. We measure the ignition temperatures of the gas mixtures flowing towards resistively heated platinum with various composition ratios and various diluent gases of N₂, Ar and CO₂. Compared with N₂ or Ar, the CO₂ dilution shows higher ignition temperature by about 50 K, even at the same composition ratio. The ignition temperature increase is proportional to the dilution ratio. Through the numerical simulation, it is illustrated that higher ignition temperature is caused by the adsorption of CO₂ and following dissociation on platinum surface, which was to date considered negligible in catalytic combustion.     

Recording of volume hologram using a beam pattern from taperedoptical fiber

A photorefractive volume hologram was recorded and probed using light diffracted from a tapered optical fiber as a reference beam. A single-mode fiber (SMF) was chemically etched and tapered to give a complicated beam pattern, and it is shown that the tapered optical fiber can be utilized to increase the storage density of the volume hologram. Spatial selectivity of the volume hologram with this method was increased by two times compared to the normal SMF referencing, which is due to the fact that the complicated beam pattern has little correlation with its shifted version     

Microprocessor-Based Control of an Ion Beam Deposition System

A microprocessor-based system with 32 A/D, 24 D/A, and 16 ac load controllers, has been designed and built to monitor and control an ion beam thin-film deposition system. The A/D and D/A channels have electrical isolation of 7.5 kV between channels and between input and output. The microprocessor system keeps the ion beam deposition parameters stable for extended periods of operation and it is proposed as a means to greatly simplify switching from one deposition species to another to grow thin multilayer or alloy films.     

A 0.9 V 92 dB Double-Sampled Switched-RC Delta-Sigma Audio ADC

A 0.9 V third-order double-sampled delta-sigma audio ADC is presented. A new method using a combination of a switched-RC technique and a floating switched-capacitor double-sampling configuration enabled low-voltage operation without clock boosting or bootstrapping. A three-level quantizer with simple dynamic element matching was used to improve linearity. The prototype IC implemented in a 0.13 CMOS process achieves 92 dB DR, 91 dB SNR and 89 dB SNDR in a 24 kHz audio signal bandwidth, while consuming 1.5 mW from a 0.9 V supply. The prototype operates from 0.65 V to 1.5 V supply with minimal performance degradation.     

Facile modifications of polyimide via chloromethylation: II. Synthesis and characterization of thermocurable transparent polyimide having methylene acrylate side groups

From chloromethylated polyimide, a useful starting material for modification of aromatic polyimides, a thermocurable transparent polyimide having acrylate side groups was prepared. In the presence of 1,8‐diazabicyclo[5,4,0]undec‐7‐ene, chloromethylated polyimide was esterified with acrylic acid to synthesize poly(imide methylene acrylate). The polymer was soluble in organic solvent, which makes it possible to prepare a planar film by spin coating. The polymer film became insoluble after thermal treatment at 230 °C for 30 min. Optical transparency of the film at 400 nm (for 1 µm thickness) was higher than 98 % and not affected by further heating at 230 °C for 250 min. Adhesion properties measured by the ASTM D3359‐B method ranged from 4B to 5B. Preliminary results of planarization testing showed a high degree of planarization (DOP) value (>0.53). These properties demonstrate that poly(imide methylene acrylate) could be utilized as a thermocurable transparent material in fabricating display devices such as TFT‐LCD. Copyright © 2004 Society of Chemical Industry     

Slow eroding biodegradable multiblock poloxamer copolymers

Biodegradable multiblock poloxamers (BMPs) with gel duration of 8 h to several weeks were prepared by varying their molecular weights from 4000 to 40 000 g mol^?1. The molecular weight of the BMP was controlled by changing the poloxamer to coupling agent ratio. Assuming a micelle packing model of the BMP gel, as in the case of a poloxamer gel, the micelle properties and critical gel concentration of BMPs were investigated on the basis of the scaling concept. The findings suggest that the control of molecular weight by hydrolyzable groups can be a facile approach to optimize the gel properties for biomedical applications. Copyright © 2005 Society of Chemical Industry