Fabrication of barium titanate ceramics via digital light processing 3D printing by using high refractive index monomer

A digital light processing (DLP) technology has been developed for 3D printing lead-free barium titanate (BTO) piezoelectric ceramics. By comparing the curing and rheological properties of slurries with different photosensitive monomer, a high refractive index monomer acryloyl morpholine (ACMO) was chosen, and a design and preparation method of BTO slurry with high solid content, low viscosity and high curing ability was proposed. By further selecting the printing parameters, the single-layer exposure time was reduced and the forming efficiency has been greatly improved. Sintered specimens were obtained after a nitrogen-air double-step debinding and furnace sintering process, and the BTO ceramics fabricated with 80 wt% slurry shows the highest relative density (95.32 %) and piezoelectric constant (168.1 pC/N). Furthermore, complex-structured BTO ceramics were prepared, impregnated by epoxy resin and finally assembly made into hydrophones, which has significance for the future design and manufacture of piezoelectric ceramic-based composites that used in functional devices.     

High-temperature oxidation behavior of monolithic Zr3[Al(Si)]4C6 and its composite incorporating 30vol% ZrB2-SiC: Providing a basis for broadening the service temperature

To provide a basis for the high-temperature oxidation of ultra-high temperature ceramics (UHTCs), the oxidation behavior of Zr₃[Al(Si)]₄C₆ and a novel Zr₃[Al(Si)]₄C₆-ZrB₂-SiC composite at 1500 °C were investigated for the first time. From the calculation results, the oxidation kinetics of the two specimens follow the oxidation dynamic parabolic law. Zr₃[Al(Si)]₄C₆ exhibited a thinner oxide scale and lower oxidation rate than those of the composite under the same conditions. The oxide scale of Zr₃[Al(Si)]₄C₆ exhibited a two-layer structure, while that of the composite exhibited a three-layer structure. Owing to the volatilization of B₂O₃ and the active oxidation of SiC, a porous oxide layer formed in the oxide scale of the composite, resulting in the degradation of its oxidation performance. Furthermore, the cracks and defects in the oxide scale of the composite indicate that the reliability of the oxide scale was poor. The results support the service temperature of the obtained ceramics.     

A cheating immune (k, n) visual cryptography scheme by using the rotation of shares

Multimedia Tools and Applications - Since Noar and Shamir introduced visual cryptography scheme (VCS), the cheating problem of VCS has absorbed much attention of scholars. The current researches on...     

锁紧机构防脱落保持架设计与分析

针对锁紧机构保持架在恶略环境下,反复振动过程中保持架上钢球脱落问题,提出了一种新型防脱落保持架设计方案,重点介绍了锁紧机构中保持架的工作形式,通过ANSYS进行有限元仿真分析,得出新型保持架结构满足刚强度要求以及热变形要求,且在随机振动6.06 g条件位移小,能有效免锁紧机构直线运动时钢球从外部脱落的可能,提高了锁紧机构工作过程中的可靠性与安全性.     

Facile synthesis of MgO–Mg2SiO4 composite ceramics with high strength and low thermal conductivity

The recycling of solid waste is a win-win solution for humans and nature. For this purpose, magnesite tailings and silicon kerf waste were employed to prepare MgO–Mg₂SiO₄ composite ceramics by solid-state reaction synthesis in the present work. Then, effects of sintering temperature and raw material ratio on as-prepared ceramics were systematically studied. As-prepared ceramics showed improvement in their relative density (from 47.55%–68.12% to 90.96%–95.25%) and cold compressive strength (from 7.34–118.66 MPa to 303.39–546.65 MPa) with the increase in sintering temperature from 1300 to 1600 °C. In addition, it was found that Si promoted synthesis process of Mg₂SiO₄ phase through transient liquid phase sintering and Fe₂O₃ accelerated sintering process through activation sintering. Consequently, the presence of Mg₂SiO₄ phase effectively improved the density and strength of MgO–Mg₂SiO₄ composite ceramic, while reducing its thermal conductivity. This work provides a potential reutilization strategy for magnesite tailings, and as-prepared products are expected to be applied in fields of construction, metallurgy, and chemical industry.     

Preparation and electrochemical characterization of Ti-based amorphous metallic glass with high strength

Ti-based amorphous metallic glasses have excellent mechanical, physical, and chemical properties, which is an important development direction and research hotspot of metal composite reinforcement. As a stable, simple, efficient, and large-scale preparation technology of metallic powders, the gas atomization process provides an effective way of preparing amorphous metallic glasses. In this study, the controllable fabrication of a Ti-based amorphous powder, with high efficiency, has been realized by using gas atomization. The scanning electron microscope, energy-dispersive spectrometer, and X-ray diffraction are used to analyze surface morphology, element distribution, and phase structure, respectively. A microhardness tester is used to measure the mechanical property. An electrochemical workstation is used to characterize corrosion behavior. The results show that as-prepared microparticles are more uniform and exhibit good amorphous characteristics. The mechanical test shows that the hardness of amorphous powder is significantly increased as compared with that before preparation, which has the prospect of being an important part of engineering reinforced materials. Further electrochemical measurement shows that the corrosion resistance of the as-prepared sample is also significantly improved. This study has laid a solid foundation for expanding applications of Ti-based metallic glasses, especially in heavy-duty and corrosive domains.     

Microstructure and electric properties of Pr-doped Pb(Zr0.52Ti0.48)O3 ceramics

Improving the piezoelectric activity of lead zirconate titanate (PZT) ceramics is of great importance for practical applications. In this study, the influence of Pr³⁺ doping on the ferroelectric phase composition, microstructure, and electric properties on the A-site of (Pb_1-1.5xPr_x)(Zr_0.52Ti_0.48)O₃ is extensively investigated. A dense and fine microstructural sample is obtained with the introduction of Pr³⁺. The results show that the morphotropic phase boundary (MPB) moves to the rhombohedral phase region. The rhombohedral and tetragonal phases exhibit an ideal coexistence in the 4 mol.% Pr³⁺ doped (PPZT4) samples. Lead vacancy and the reduction of the potential energy barrier are considered to be the key mechanisms for donor doping, which is upheld by the Pr³⁺ doping. Combining the I-E hysteresis loops with the P-E hysteresis loops, it becomes apparent that both contribution maximums of the domain switching and residual polarisation are in PPZT4. Moreover, the thermal aging resistance of PZT is improved by doping, and the temperature stability is optimised from 83% in PZT to 96% in PPZT4. Hence, an appropriate amount of Pr³⁺ doping can effectively improve the piezoelectric activity of PZT ceramics in the MPB area and optimise the performance stability of the material under application temperatures.     

基于图像分割技术的图像数字水印算法研究

针对数字图像水印技术,通过对闭运算得到的图像再进行开运算,使实验得到的图像区域较为完整,采用4×4的正方形结构元素,使得图像区域有更多的白色像素被置为黑色,对图像进行取反操作,能够对图像区域的非连通区域进行填充.希望能够利用精确的图像分割算法,实现对复杂版面的文档图像的有效切割,在一定程度上对图像数字水印的推广起到促进作用.     

Rheological phase reaction synthesis and electrochemical performance of LiFe2/3Mn1/3PO4/C cathode for lithium-ion batteries

LiFe_2/3Mn_1/3PO₄/C composite was prepared by the rheological phase reaction using LiH₂PO₄, Li₂CO₃, FePO₄, Mn(Ac)₂·4H₂O and ascorbic acid as starting materials. The crystal structure and morphology of as-synthesized sample were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The analysis of XRD results showed that the obtained sample was single-phase with orthorhombic olivine-type structure (Pnma space group). SEM micrographs revealed that the sample was aggregates, with an irregular morphology. The initial discharge capacity was 166.9, 149.1, 139.6, 112.8, 82.93 mAh g^??1 at the rate of 0.1, 0.5, 1, 2, and 10 C, respectively. And when the rate was 0.1, 0.5, 1, 2, and 10 C, the capacity retention was 92.2%, 90%, 92.9%, 97.6%, 91.5% after 50, 100, 200, 200, 500 cycles, respectively.