文章从社会和科技的发展出发,对模具专业课程体系改革的相关问题进行了研究,拟定的改革方案已付诸实施,并已取得初步成果。 相似文献
2.
3.
4.
利用透射电镜、SEM形貌观察、剩余强度的测定等试验手段,研究了AlCuMgAg铝合金在欠时效状态下的高温持久对合金的微观组织和力学性能的影响。结果表明,165℃×4h欠时效状态的合金在高温高压持久(200℃、220MPa)条件下,强度逐渐增加,持久时间为20h时,强度达到最大值,而后缓慢下降;持久时间为100h的断裂仍为韧性断裂,只是无析出带的宽度增加。 相似文献
5.
The effect of tensile stress on thermal microstructure evolution of Ω phase in an AI-Cu-Mg-Ag alloy with high Cu/Mg ratio and higher Ag content was investigated by transmission electron microcopy (TEM) .The samples were aged at 200 ℃ for 1 h (T6 condition), then thermal exposed at 250 ℃ for 100 h with and without a tensile stress (130 MPa), respectively. The results indicate that Ω precipitates uniformly disperse in the matrix as a major precipitate after artificially aging at 200℃ for 1 h (T6 condition). Exposed at 250℃ for 100 h without stress, Ωprecipitates dissolve dramatically. Whereas, during stress exposure they coarsen unexpectedly rather than dissolve into matrix. It can be deduced that the stress retards the redissolution of Ω phase. 相似文献
6.
介绍了铸钢齿轮的三种工艺:水平浇注对工装要求低,铸件工艺出品率低,而且用于大平面的铸钢齿轮极易产生夹砂等缺陷;倾斜浇注可使铸件工艺出品率提高8~15%,改善了铸件的表面和内在质量;平做立浇对工装要求高,适用于大批量生产的中小型铸钢齿轮,可提高作业面积利用率。 相似文献
7.
Al-Cu-Mg-Ag合金析出相的研究进展 总被引:2,自引:5,他引:2
Al-Cu-Mg-Ag合金是在Al-Cu-Mg系合金基础上开发的新型合金。根据成分的不同,该合金的常见析出相有θ′、S′和Ω相,其中在基体{111}面析出的臼相具有较高的沉淀硬化能力和热稳定性,使得Al-Cu-Mg-Ag成为一种新型中温高强铝合金。在简要介绍该合金研究过程的基础上,回顾该合金强化相的相组成、相的析出序列和热稳定性;同时总结以Ω相为主要强化相的合金体系合金化研究进展;并对该合金的研究方向进行展望。 相似文献
8.
9.
10.
研究Al-Cu-Mg-Ag-Zr合金在165℃时效组织与性能的变化,并采用欠时效态(165℃×2h)的试样进行200℃及外加应力为200MPa的高温持久试验。结果表明,欠时效态的试样在高温持久下,随时间延长,其剩余强度先上升后下降,强度峰值出现在持久20h。延伸率变化与强度变化基本相似。持久100h后,合金力学性能相对欠时效态无明显下降,显示出优良的热稳定性。 相似文献