The microstructure and mechanical properties of AZ61 magnesium alloy with Ca, Sm addition were investigated. The results showed that the addition of 0.5 wt.% Ca reduced the quantity of Mg17Al12 phase, and formed a new Al4 Ca phase which is reticular in AZ61 alloy. With the addition of Ca and Sm, the microstructure was further refined and new Al-Sm rich phases were formed in AZ61 alloy with 0.6 wt.%–1.5 wt.% Sm addition, the TEM analysis confirmed that they were Al2 Sm and Al4 Sm. Tensile tests showed that 1.0 wt.% Sm addition contributed to the formation of the Al2 Sm and Al4 Sm and the improvement in the ambient strength, i.e., an ultimate tensile strength of 327 MPa and an elongation of 10.1%. However, excessive Sm addition led to the coarsening of Al2 Sm and Al4 Sm phases, thus resulted in the decline of strength and plasticity. 相似文献
2.
3.
钢管混凝土支架在高应力巷道加固中的应用 总被引:2,自引:0,他引:2
利用钢管混凝土支架技术,对八采轨道下山进行加固修复,有效地控制了围岩变形,保证了巷道稳定,取得了良好的技术经济效果。 相似文献
4.
5.
6.
为了研究GH1016合金的高温热变形行为,利用Gleeble-3500热模拟试验机进行变形温度在1000~1150℃范围内,应变速率为0. 1~10 s-1,总压缩变形量为60%的热压缩试验,通过获得的真应力-真应变曲线研究了其变形行为。研究结果表明:真应力随变形温度的降低和应变速率的升高而增加。在一定的变形温度下,随着应变速率的增加,峰值应力和峰值应变均增加;在一定的应变速率下,随变形温度的升高,峰值应力和峰值应变减小。根据真应力-真应变曲线中的峰值应变和峰值应力数据,利用数据拟合的方法分别求得了GH1016合金的热变形本构方程和临界变形条件方程。在本实验条件下,GH1016合金发生动态再结晶的热激活能为456. 55 k J·mol-1。 相似文献
7.
介绍了近年来国内外Zn-Al-Mg合金镀层钢板的商业化生产进展,其合金元素的作用机理,性能特点,以及应用现状。展望了Zn-Al-Mg合金镀层钢板未来的发展。 相似文献
8.
9.
通过改变母合金铸锭的重熔次数和熔体冷却速率获得3种具有不同原子有序度的Zr55Al10Ni5Cu30块体非晶合金,并采用差示扫描量热仪研究了原子有序度对该合金等温晶化过程的影响。结果表明,在等温晶化条件下,原子有序度的增加使Zr55Al10Ni5Cu30块体非晶合金孕育期明显减小;对晶化相的形核和长大机制几乎没有影响,均为形核速率随时间增加的扩散控制的三维长大;使Avrami指数出现一定程度的减小。 相似文献