排序方式: 共有47条查询结果,搜索用时 16 毫秒
1.
2.
A new kind of doped rare earth free phosphor Y2O2S∶xTi(0<x≤0.10) with doped Ti as activative center was synthesized by solid state reaction and sintered at 1200 ℃ for 2.5 h under reducing atmosphere. XRD patterns, photoluminescence spectra, time-resolved phosphorescence spectra and decay curves of the phosphor were investigated. XRD results reveal that a single Y2O2S phase exists with Ti content up to 6%(mol fraction). Yellow long lasting phosphorescence for present materials was observed in the dark with naked eye after the removal of the excitation light. From the time-resolved phosphorescence spectra the broad emission band centered at 565 nm was confirmed to be responsible for the long lasting phosphorescence which could maintain above 1 h. The possible mechanism responsible for the long lasting phosphorescence of the Y2O2S∶Ti phosphor was proposed. 相似文献
3.
采用高温还原法合成了Eu,Ti共激活橙红色Y2O2S长余辉发光材料,并测量了Y2O2S:0.03Eu,0.03Ti磷光体的荧光光谱,余辉分辨和余辉衰减曲线谱.实验结果表明,Y2O2S:0.03Eu,0.03Ti磷光体的发射谱由一系列Eu^3+离子内部能级跃迁的尖峰组成;余辉分辨谱则不同,由一个主峰位于565nm的宽发射带和一系列波长范围位于500nm以上的窄发射带两种峰形组成,可分别归为Ti离子的宽带余辉发射和三价Eu^3+的线状余辉发射,分析认为,样品中存在Ti余辉发射向Eu^3+内部能级间产生选择性的余辉传能机制,从而导致Y2O2S:0.03Ti,0.03Eu磷光体中同时出现两种发光中心离子的余辉分辨谱现象. 相似文献
4.
水热法制备纳米TiO2的可见光波段光催化活性的溶剂效应 总被引:3,自引:0,他引:3
采用单乙醇、丙酮、吡啶、二元以及三元混合有机溶剂的有机溶剂水热法合成高分散纳米TiO2粉体,通过XRD,TEM和DTA-TG等手段研究合成的粉体物相与表面吸附特性,以及可见光光催化降解效率.结果表明在颗粒尺寸与晶型差别不大的各种溶剂制备粉体中,含丙酮单元、二元及三元溶剂制备TiO2粉体光催化效率在76%-89%;而单乙醇、乙醇-吡啶二元溶剂制备的光催化效率很低,均在15%以下.分析表明,可见光波段光催化效率与表面吸附物结构、基团与其极性等密切相关碳链结构溶剂中,含中极性羰基的丙酮溶剂吸附的粉体光催化效率,远高于含强极性羟基的单乙醇、乙醇-吡啶溶剂吸附粉体的光催化效率.) 相似文献
5.
用固态配料和硝酸盐共沉淀配料制备了各组份为(Bi_(1.85)Pb_(0.40))Sr_(1.95)Ca_(2.05)Cu_(8.10)的超导材料,研究了两种不同制备工艺对Bi系超导相形成过程、超导电磁性能和显微结构的影响.实验发现,由共沉淀制备的样品T_(c(zero))稳定性好,T_(c(zero))均在107.5K以上.SEM观察表明:共沉淀法制备的样品中超导相颗粒比固态配料制备的要细小、均匀,颗粒间连结紧密,与T_(c(zero))结果相符.但XRD相分析结果显示:固态配料样品中高温相含量高于共沉淀配料,共沉淀配料制备作品中高、低温相同时存在,但其交流磁化率—温度曲线上仅在120K附近出现相应于高温相的抗磁信号.研究认为,这是由于共沉淀配料烧成时,高温相容易在部分液相参与下,在低温相表面通过反应成核生长,导致在形成的高温相内部包裹有残余低温相的“内芯”.依此包裹模型可自洽地解释X射线相分析与电、磁性能测定结果间的矛盾,讨论了Bi系高温相的形成机理,为选择合理的制备工艺提供了依据. 相似文献
6.
7.
8.
用高温固相还原法合成了无稀土激活离子Y2O2S∶0.09Ti长余辉发光材料,研究了 Li2CO3,Na2CO3,K2CO3,K3PO4和K2HPO4等 5种助熔剂对Y2O2S∶Ti磷光体发光性能的影响。结果表明:除了 K2HPO4外,加入 Li2CO3,Na2CO3, K2CO3与 K3PO4助熔剂均可得到单相Y2O2S∶Ti晶体。发射光谱结果显示:不同助熔剂的加入并没有改变样品发射谱主峰位置(565 nm),但对其峰强度产生明显影响。助熔剂也显著改善了Y2O2S∶Ti的余辉亮度,特别是Li2CO3。10 min衰减时,Y2O2S∶Ti样品的余辉亮度从加 K2CO3助熔剂的0.15 mcd/m2增加到加Li2CO3助熔剂的10.1 mcd/m2。用紫外光激发样品,移去光源后,加Li2CO3助熔剂合成的样品在暗室中的余辉时间可持续达 5 h(0.32 mcd/m2) 。 相似文献
9.
10.
Al离子掺杂增强SrTiO3:Pr3 荧光体发光性能的研究 总被引:1,自引:0,他引:1
采用Sol-gel方法合成了Al和Pr离子共掺的红色纳米晶SrTiO30.002Pr,xAl(x=0~0.35)荧光体.XRD分析表明,经1200℃高温烧成后所得的荧光体为单一组成的SrTiO3立方相,空间群为Pm-3m,晶胞参数计算得α为3.9043 nm.光谱测试表明,该荧光体的主发射峰位于617nm,对应于Pr3 离子的1D2→3H4跃迁发射.随着Al3 掺杂浓度的增加,发光强度先增后减,当x=0.26时发光强度达到最大值,此时荧光体的发光强度约是未掺Al样品发光强度的2倍.晶体结构和光谱性能分析暗示,Al3 离子掺入可能提高了SrTiO3Pr基质晶体的完整度,从而增加其发光强度. 相似文献