在不同的挤压温度和挤压比下,将AZ31B镁合金机加屑冷压后热挤压固结而再生镁合金。与铸锭挤压合金对比,从动态再结晶组织与屑间结合情况两个主要方面分析了加工工艺对再生合金力学性能的影响。随着挤压温度升高,再生合金的极限抗拉强度和延伸率先增加而后降低。随挤压温度升高,晶粒长大与屑间结合增强的相反作用共同导致了再生合金力学性能的变化。当挤压比从4:1 增加到 44:1,晶粒细化且屑间结合增强,使再生合金的抗拉强度增加。而当挤压比高于25:1时,由于显著的形变强化作用导致延伸率下降。 相似文献
5.
6.
Microstructure and mechanical properties of dissimilar joint between aluminum and aluminum-coated steel by cold metal transfer process
下载免费PDF全文
![点击此处可从《中国焊接》网站下载免费的PDF全文](/ch/ext_images/free.gif)
Two dissimilar materials, aluminum alloy and aluminum-coated steel, were joined by cold metal transfer process using AlSi5 filler wire. To this end, the steel was coated with Al-Si. The steel did not melt and aluminum was melt to form the joint during the process, it was actually cold metal transfer welding-brazing. The macrostructure, microstructure, alloy element distribution, and inter-metallic compounds were analyzed by optical microscopy, scanning electron microscopy, and energy dispersive spectroscopy. It was found that the Al-Si coating dissolved into the weld metal. The pre-existing thin Fe-Al-Si ternary inter-metallic compounds in the interface between the Al-Si coating layer and base metal steel also partially dissolved into the weld zone, tending to reduce the thickness of inter-metallic compounds. Approximate 3 μm thick undissolved inter-metallic compound was found at the interface after welding which could guarantee sound bonding strength in dissimilar materials joining. The sample was fractured at the fusion zone near the aluminum side in the tensile test. The ultimate tensile strength was about 156 MPa, and the fracture mode is ductile failure in nature according to its morphology. 相似文献
7.
在不同的挤压温度和挤压比下,将AZ31B镁合金机加屑冷压后热挤压固结而再生镁合金。与铸锭挤压合金对比,从动态再结晶组织与屑间结合情况两个主要方面分析了加工工艺对再生合金力学性能的影响。随着挤压温度升高,再生合金的极限抗拉强度和延伸率先增加而后降低。随挤压温度升高,晶粒长大与屑间结合增强的相反作用共同导致了再生合金力学性能的变化。当挤压比从4:1增加到44:1,晶粒细化且屑间结合增强,使再生合金的抗拉强度增加。而当挤压比大于25:1时,由于显著的形变强化作用导致延伸率下降。 相似文献