Morphology, structure and formation mechanism of silicide coating by pack cementation process

The MoSi2 coating on C 103 niobium based alloy was prepared by pack cementation method. The formative mechanism, morphology and structure of coating were investigated. The silicide coating was formed by reactive diffusion obeying parabolic rule during pack cementation process. It is found that the composite structural coating is composed of three inferior layers as follows. The main layer is composed of MoSi2, the two phases＇ transitional layer consists of NbSi2 and a few NbsSi3 and the diffuse layer is composed of NbsSi3. The dense amorphous glass layer formed on the surface at high temperature oxidation circumstance can effectively prevent the diffusion of oxygen into coating.     

Microstructure and mechanical properties of 8YSZ ceramics by liquid-phase sintering with CuO-TiO2 addition

The 8% (mass fraction) yttrium-partially-stabilized zirconia (8YSZ) ceramic was fabricated via liquid phase sintering at 1 200–1 400 °C by adding different mass ratios of CuO-16.7%TiO₂ (molar fraction) as sintering aid. Relative density, microstructure, Vickers hardness and bending strength as a function of sintering temperature and additive content were investigated. The experiment results show that liquid phase sintering at low temperature can be realized through adding CuO-16.7% TiO₂ to 8YSZ. The Vickers hardness and bending strength of samples with sintering aid are generally much higher than those of samples without sintering aid for all sintering temperatures, and increase with the increase of sintering temperature. When the addition content of CuO-16.7% TiO₂ is beyond 0.5%, the relative density, Vickers hardness and bending strength decrease with the increase of the mass ratio of sintering aid. Low additions of sintering aid are beneficial to aiding densification; high additions of sintering aid are detrimental to the sintered properties mainly due to greater amounts of pores generated by the volatilization of oxygen with the eutectic reaction between copper oxide and titanium dioxide. It is found that the fine grain size and high relative density are two main reasons of the high bending strength and Vickers hardness of the materials.     

包渗法制备硅化物涂层的结构形貌及形成机理

采用包渗法在C-103铌合金基体上制备MoSi2涂层,通过X射线衍射、扫描电镜和能谱分析等手段研究涂层表面、截面形貌以及氧化后涂层结构变化,并分析硅化过程中涂层的形成机理。研究结果表明：包渗法制备硅化物涂层是通过反应扩散形成的,硅化过程服从抛物线规律;该涂层为复合结构：MoSi2相为主体层;以NbSi2相为主、并含少量Nb5Si3相的两相为过渡区;Nb5Si3相为扩散层。在高温氧化环境下,涂层表面生成致密的非晶氧化层,有效地阻止了氧向涂层内扩散。     

增材制造GH3536合金的高温拉伸及疲劳裂纹扩展性能研究

采用选区激光熔化技术制备GH3536合金试样,经热等静压和固溶处理后对合金试样的显微组织、高温拉伸性能和不同应力比下的裂纹扩展性能进行了分析。结果表明,经热等静压和固溶处理后合金试样内部存在2种不同大小的等轴晶粒,在晶间存在连续片状分布的M₂₃C₆和M₆C碳化物。合金试样的拉伸性能随着温度的升高而不断下降,断裂方式由室温下的韧性断裂转变为900℃下的脆性断裂。在不同应力比下,合金试样的裂纹扩展方式主要为穿晶扩展,裂纹扩展速率随着应力比的不断上升而提高,在高应力比下合金内部的疲劳裂纹更倾向于在取向差较小的晶粒内部扩展。     

无铅锑黄铜轧制工艺的研究EI北大核心

在研究锑黄铜板材熔铸工艺的基础上,通过控制开坯温度、压下制度、轧制温度和退火制度,轧制出抗拉强度达到461.7MPa,延伸率可达15.67%,力学性能与铅黄铜HPb59-1相当的锑黄铜,为进一步提高无铅易切削锑黄铜的热轧提供了参考。     

Si3N4(p)/SiC(w)协同复合MoSi2材料的强韧化及机理研究

采用X射线衍射(XRD)、扫描电子显微镜(SEM)、维氏硬度计、电子万能材料试验机研究MoSi_2-Si_3N_(4(p))/SiC_(w)复合材料的结构、形貌、硬度、断裂韧性,并对SiC晶须和Si_3N_4颗粒复合强韧化MoSi_2的机理进行了探讨.结果表明,SiC晶须和Si_3N_4颗粒对MoSi_2具有协同强韧化作用,MoSi_2-20%Si_3N_(4(p))-20%SiC_(w)(体积分数,下同)复合材料的抗弯强度达427 MPa,室温断裂韧性达到10.4 MPa·m~(1/2),均高于单一强韧化剂的强韧化效果.MoSi_2-20%Si_3N_(4(p))-20%SiC_(w)复合材料的强化机理为细晶强化和弥散强化;韧化机制为细晶韧化、裂纹偏转与分支和微桥接韧化.     

热型连铸铝线的制备及其显微组织和性能

采用自制的热型连铸设备制备铝线材料,研究铸型温度和拉铸速度等工艺参数对材料表面质量、显微组织及力学性能的影响,通过对最佳工艺条件下制备的铸锭断口形貌进行观察和分析,探讨其相关机理。结果表明:当铸型温度为675~685℃、拉铸速度为90~120 mm/min时,可以制备出表面质量较佳的铸锭;同时,工艺参数会对晶体的择优取向产生一定影响,当铸型温度和拉铸速度分别为680℃和90 mm/min时,晶体的取向更倾向于沿?100?方向生长,铸型温度越高,铸锭力学性能越优异。当拉铸速度为90 mm/min时,制备的热型连铸铝线具有最佳的塑性加工能力。相比于普通多晶铝线,热型连铸铝线具有更好的塑性。     

钼合金Si-Cr-Ti-SiC-MnO2涂层的制备与组织性能

目的提高钼合金表面红外辐射性能与高温抗氧化性能。方法将40%Si、20%Cr、5%Ti、5%SiC、30%Mn O_2五种粉末与酒精、粘结剂按比例混合,经高能球磨6 h后制得均匀悬浮的料浆。采用浸涂工艺对预处理的钼合金试样进行料浆涂覆,在1450℃真空烧结0.5 h后制得黑色涂层试样。通过1550℃高温静态氧化试验和高温粒子薄片红外光谱综合实验系统,分别评价涂层抗氧化性能和红外辐射性能,并通过扫描电镜(SEM)、能谱分析(EDS)、X射线衍射仪(XRD)对涂层氧化前后的形貌与组织结构进行分析。结果钼合金Si-Cr-Ti-SiC-Mn O_2涂层在700、900℃的法向发射率分别达0.85、0.88,在1550℃高温有氧环境下的静态抗氧化寿命达7 h。原始涂层呈四层复合梯度结构,由外到内分别为SiO_2+Mn3O_4+M5Si3(M指Mo、Cr、Ti)、M5Si3+Mo Si2+SiC+Mn3O_4、Mo Si2、Mo5Si3。高温氧化后,涂层四层复合结构由外到内转变为SiO_2+(Cr,Ti)5Si3+Mn Cr2O_4+Mn3O_4、M5Si3+SiC+Mn Cr2O_4+Mn3O_4、Mo Si2、M5Si3。高温氧化过程中,MSi2高硅化物层逐渐转变为M5Si3低硅化物层,涂层表面形成含Mn Cr2O_4尖晶石相和复合硅化物的致密SiO_2玻璃膜。结论 Si-Cr-Ti-SiC-Mn O_2涂层可有效提高钼合金基体的红外辐射性能和高温抗氧化性能,复合硅化物与硅锰复杂氧化物具有良好的抗氧化性能、高辐射性能和自愈合性能。     

自然时效对GT35合金组织与性能的影响

采用XRD、SEM、残余应力测试仪、维氏硬度计、测长机等手段对合金物相、微观组织、残余应力、硬度、线膨胀率进行表征,研究自然时效对GT35合金组织与性能的影响。结果表明,GT35合金在自然时效过程中,增强相TiC的形貌与粒径没有明显变化。当自然时效时间小于15天时,GT35合金的硬度、残余应力与线膨胀率逐渐增加,随后逐渐减小并趋于稳定。当自然时效超过90天后,GT35合金的组织与性能趋于稳定,其硬度、残余应力和线膨胀率分别为945.7 HV5、-184 MPa和-2.22×10^-5。     

溶胶-凝胶法制备的ZnO:Al薄膜的微观结构及光学、电学性能

采用溶胶-凝胶法制备了ZnO:Al(AZO)透明导电薄膜．通过X射线衍射(XRD)、紫外-可见分光光度计 (UV-Vis)、扫描电镜(SEM)和电阻测量装置,考察了Al掺杂量、退火温度及镀膜层数等工艺参数对薄膜的微观结构和光电性能的影响．结果表明,退火温度越高,多晶AZO薄膜的(001)晶面择优取向生长的趋势越强,并且随退火温度升高,薄膜的晶粒尺寸增大,透光率增加．薄膜晶体结构为纯ZnO的六角纤锌矿结构．在掺杂浓度1％(摩尔分数)、退火温度500℃及镀膜层数10的条件下,得到了电阻率为3．2×10-3Ω·cm、可见光区的平均透射率超过90％的AZO薄膜．